US4072533A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Lightweight, non-cementitious building material
Assignee: Armstrong World Industries Inc
•
Filing: 1976-10-14
•
Granted: 1978-02-07
•
Expires: 1996-10-14
Abstract
Abstract An improved lightweight building material capable of being formed in a continuous sheet operation. The material comprises sodium silicate as a binder and an expanded inorganic aggregate. In addition, an efflorescence inhibitor is included in such composition comprising boric acid, a metal borate selected from the group consisting of zinc borate, calcium borate, magnesium borate and mixtures thereof, a calcium salt selected from the group consisting of calcium sulfate, calcium nitrate, calcium phosphate, calcium orthophosphate and mixtures thereof, an alkali metal fluorosilicate, or mixtures of the above.
Inventors
- 👤 Jeffery L. Barrall
- 👤 William R. Reed
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 16:58
CPC Classifications
C; C04; C04B; C04B28/00; C04B28/24; C04B28/26; Y; Y10; Y10S; Y10S106/00; Y10S106/02
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
62 words
An improved non-cementitious building material comprising sodium silicate and an expanded siliceous inorganic aggregate, the improvement comprising said building material further including an efflorescence inhibitor comprising a boron compound selected from the group consisting of the borates of zinc, calcium, magnesium, and mixtures thereof; a calcium salt selected from the group consisting of calcium nitrate, calcium phosphate, calcium orthophosphate, and mixtures thereof.
Claim 2
Dependent Claim
62 words
An improved non-cementitious building material comprising sodium silicate and an expanded siliceous inorganic aggregate, the improvement comprising said building material further including an efflorescence inhibitor comprising a boron compound selected from the group consisting of the borates of zinc, calcium, magnesium, and mixtures thereof; a calcium salt selected from the group consisting of calcium nitrate, calcium phosphate, calcium orthophosphate, and mixtures thereof.
Claim 3
Dependent Claim
31 words
The improved building material in accordance with claim 1 wherein said expanded siliceous inorganic aggregate is perlite and said sodium silicate is Na 2 O:SiO 2 of 1:4 to about 1:2.
Claim 4
Dependent Claim
29 words
The improved building material in accordance with claim 1 wherein said efflorescence inhibitor is selected from the group consisting of zinc borate, magnesium borate, calcium borate and mixtures thereof.
Claim 5
Dependent Claim
29 words
The improved building material in accordance with claim 1 wherein said efflorescence inhibitor is selected from the group consisting of calcium phosphate, calcium orthophosphate, calcium nitrate and mixtures thereof.
Claim 6
Dependent Claim
35 words
The improved building material in accordance with claim 2 wherein said perlite has a loose bulk density of between 2 to 10 pounds per cubic foot and between 5 and 100 Tyler Sieve Mesh number.
Claim 7
Dependent Claim
23 words
The improved building material in accordance with claim 2 wherein said perlite content is about 39% to about 80% of the total formula.
Claim 8
Dependent Claim
28 words
The improved building material in accordance with claim 3 wherein said efflorescence inhibitor is in the range of 6% to 45% by weight based on said sodium silicate.
Claim 9
Dependent Claim
28 words
The improved building material in accordance with claim 5 wherein said efflorescence inhibitor is in the range of 6% to 45% by weight based on said sodium silicate.
Claim 10
Dependent Claim
26 words
The improved building material of claim 6 additionally containing an organic fiber, said organic fiber replacing the perlite in 5% to 30% of said perlite content.
Claim 11
Dependent Claim
55 words
An improved non-cementitious building material comprising sodium silicate and 39%-80% by weight of an expanded perlite, the improvement comprising said building material further including 10 to 37 weight percent of a boron compound selected from the group consisting of zinc borate, calcium metaborate, magnesium borate, and mixtures thereof, based on weight of said sodium silicate.
Claim 12
Dependent Claim
55 words
An improved non-cementitious building material comprising sodium silicate and 39%-80% by weight of an expanded perlite, the improvement comprising said building material further including 10 to 37 weight percent of a boron compound selected from the group consisting of zinc borate, calcium metaborate, magnesium borate, and mixtures thereof, based on weight of said sodium silicate.
Claim 13
Independent Claim
85 words
A method for forming an improved non-cementitious building material comprising 1. admixing sodium silicate with an expanded siliceous inorganic aggregate; 2. adding to said admixture a boron compound selected from the group consisting of the borates of zinc, calcium, magnesium, and mixtures thereof; a calcium salt selected from the group consisting of calcium nitrate, calcium phosphate, calcium orthophosphate, and mixtures thereof; and 3. pressing and drying the mixture of step 2; whereby the efflorescence of the pressed and dried material of step 3 is inhibited.
Claim 14
Independent Claim
85 words
A method for forming an improved non-cementitious building material comprising 1. admixing sodium silicate with an expanded siliceous inorganic aggregate; 2. adding to said admixture a boron compound selected from the group consisting of the borates of zinc, calcium, magnesium, and mixtures thereof; a calcium salt selected from the group consisting of calcium nitrate, calcium phosphate, calcium orthophosphate, and mixtures thereof; and 3. pressing and drying the mixture of step 2; whereby the efflorescence of the pressed and dried material of step 3 is inhibited.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-02-06 | 1981-08-08 | 1982-02-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-02-06 | 1985-08-08 | 1986-02-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-02-06 | 1989-08-08 | 1990-02-07 | $7700.00 | Window Closed / Lapsed |