Vacuum process for avoiding devitrification damage to transparent slip-cast silica crucibles
Assignee: Sherwood Refractories Inc
•
Filing: 1976-05-10
•
Granted: 1978-02-07
•
Expires: 1996-05-10
Abstract
Abstract A process is disclosed for making vitreous silica crucibles of exceptional high quality for use in the growing of a silicon crystal from molten silicon. The crucibles are formed from fine particles of high purity fused silica by slip casting or other suitable process, are dried and fired to provide a rigid porous body, and are thereafter sintered to a high density, preferably to the transparent state. The invention solves the problem of spalling, blistering and cracking during crystal growing and the resulting contamination of the molten silicon, which has long plagued the industry, by eliminating water from the fused silica particles before the porous body is sintered to the transparent state. Said body is thoroughly dried in a vacuum furnace at a high temperature and at a sub-atmospheric pressure low enough to remove the chemically bound water which cannot be removed by heat alone. The crucibles of this invention retain their transparency and high quality without spalling or introducing microscopic particles of silica into the silicon, thereby making it possible to grow a silicon crystal of highest quality without dislocations and imperfections due to contamination by said particles.
Inventors
- 👤 Ted A. Loxley
- 👤 Walter G. Barber
- 👤 Walter W. Combs
- 👤 John M. Webb
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 03:19
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/14; C03; C03B; C03B19/00; C03B19/06; C03B19/066; C03B20/00; Y; Y10; Y10S; Y10S65/00; Y10S65/04; Y10S65/08; Y10S65/13
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
230 words
In a process for manufacture of thin-wall crucibles for holding molten silicon during crystal growing comprising the steps of forming, from a slurry of finely divided silica particles of high purity, a porous vitreous silica crucible containing chemically combined water in the form of hydroxyl groups, drying the crucible and firing it to eliminate the combustibles and the free water, continuing the heating of the porous crucible at a temperature up to 2200° F. to strengthen the crucible, placing the crucible on a support shaped to support the inner surface of the crucible, heating the crucible on said support in a furnace to a sintering temperature to coalesce the particles and to provide a high-density transparent vitreous silica, and cooling the sintered crucible, the improvement wherein the silica particles of said slurry have an average particle size not in excess of 10 microns and wherein the chemically combined water is removed by heating the crucible, after said firing and before sintering to high density, to a temperature of from about 2000° to about 2200° F. and under a subatmospheric pressure not in excess of 10 torrs for a time period of at least one hour such that, after sintering, the transparent vitreous silica of the finished crucible has excellent optical transmittance in the near infrared and is not subject to damage by rapid devitrification during growing of the silicon crystal.
Claim 2
Dependent Claim
230 words
In a process for manufacture of thin-wall crucibles for holding molten silicon during crystal growing comprising the steps of forming, from a slurry of finely divided silica particles of high purity, a porous vitreous silica crucible containing chemically combined water in the form of hydroxyl groups, drying the crucible and firing it to eliminate the combustibles and the free water, continuing the heating of the porous crucible at a temperature up to 2200° F. to strengthen the crucible, placing the crucible on a support shaped to support the inner surface of the crucible, heating the crucible on said support in a furnace to a sintering temperature to coalesce the particles and to provide a high-density transparent vitreous silica, and cooling the sintered crucible, the improvement wherein the silica particles of said slurry have an average particle size not in excess of 10 microns and wherein the chemically combined water is removed by heating the crucible, after said firing and before sintering to high density, to a temperature of from about 2000° to about 2200° F. and under a subatmospheric pressure not in excess of 10 torrs for a time period of at least one hour such that, after sintering, the transparent vitreous silica of the finished crucible has excellent optical transmittance in the near infrared and is not subject to damage by rapid devitrification during growing of the silicon crystal.
Claim 3
Dependent Claim
38 words
The process of claim 1 wherein the fired crucible is heated for about one to about two hours under a high vacuum such that the chemically combined water is eliminated before the silica is sintered to high density.
Claim 4
Dependent Claim
53 words
The process of claim 1 wherein the crucible is sintered to high density in a helium atmosphere at a temperature not in excess of 3150° F. for up to ten minutes so that cristobalite is retained in the finished crucible in a small percentage insufficient to damage the crucible when it is cooled.
Claim 5
Dependent Claim
56 words
The process of claim 3 wherein the formation of cristobalite is promoted by providing the silica particles of said slurry with an average particle size not in excess of 4 microns and wherein most of the chemically combined water is removed by heating the fired crucible under vacuum to a temperature up to about 2100° F.
Claim 6
Dependent Claim
68 words
A process according to claim 1 for producing highpurity cristobalite-containing crucibles wherein the fired crucible is heated for a period of time at a temperature above 2200° F. to form cristobalite before sintering of the crucible is completed in said furnace and said sintering is carried out at a temperature not in excess of 3150° F. and below the melting point of cristobalite whereby the cristobalite is retained.
Claim 7
Dependent Claim
40 words
A process according to claim 1 wherein most of the chemically combined water in the fired crucible is eliminated by heating the fired crucible under vacuum to a temperature of at least 2000° F. in no more than two hours.
Claim 8
Dependent Claim
229 words
A process for manufacturing thin-wall water-free crucibles for use in the growing of silicon crystal rods comprising the steps of slip casting a porous vitreous silica crucible of a predetermined shape from a slurry of finely divided silica particles of high purity having an average particle size not in excess of 10 microns, the silica of said crucible containing chemically bound water in the form of hydroxyl groups, drying the crucible to remove the free water and firing it to burn out the combustibles and to strengthen the crucible while providing a rigid body of high purity, placing the crucible on a refractory support, heating the crucible on said support in a furnace from a temperature below 2200° F. to a sintering temperature up to about 3150° F. in a vacuum or helium atmosphere for a period of at least several minutes to coalesce the particles and to provide a high-density transparent vitreous silica, and cooling the resulting transparent silica crucible, the chemically combined water being removed from the fired crucible before it is sintered to high density by firing it at a temperature up to 2200° F. for a substantial time period and under a high vacuum such that the transparent vitreous silica of the finished sintered crucible has a hydroxyl content so low that it is not subject to devitrification damage during growing of the silicon crystal.
Claim 9
Dependent Claim
229 words
A process for manufacturing thin-wall water-free crucibles for use in the growing of silicon crystal rods comprising the steps of slip casting a porous vitreous silica crucible of a predetermined shape from a slurry of finely divided silica particles of high purity having an average particle size not in excess of 10 microns, the silica of said crucible containing chemically bound water in the form of hydroxyl groups, drying the crucible to remove the free water and firing it to burn out the combustibles and to strengthen the crucible while providing a rigid body of high purity, placing the crucible on a refractory support, heating the crucible on said support in a furnace from a temperature below 2200° F. to a sintering temperature up to about 3150° F. in a vacuum or helium atmosphere for a period of at least several minutes to coalesce the particles and to provide a high-density transparent vitreous silica, and cooling the resulting transparent silica crucible, the chemically combined water being removed from the fired crucible before it is sintered to high density by firing it at a temperature up to 2200° F. for a substantial time period and under a high vacuum such that the transparent vitreous silica of the finished sintered crucible has a hydroxyl content so low that it is not subject to devitrification damage during growing of the silicon crystal.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-02-06 | 1981-08-08 | 1982-02-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-02-06 | 1985-08-08 | 1986-02-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-02-06 | 1989-08-08 | 1990-02-07 | $7700.00 | Window Closed / Lapsed |