Polysiloxane-polyoxyalkylene block copolymers as stabilizers in the production of urethane foam

Claim 2

A process for preparing flexible polyether polyurethane foam, said process comprising reacting and foaming a mixture comprising (a) a polyether containing at least two hydroxyl groups per molecule, (b) an organic polyisocyanate, (c) a catalyst for the reaction of (a) and (b) to produce the polyurethane, (d) a blowing agent and (e) as the foam stabilizer a polysiloxane-poly(oxyethylene-oxypropylene) block copolymer consisting essentially of from about 15 to about 35 percent by weight of polysiloxane blocks and from about 85 to about 65 percent by weight of polyoxyalkylene blocks, and further consisting essentially of siloxy units of the formula R 2 SiO, siloxy units selected from the group consisting of those of the formulas (R)(Q)SiO and RSiO3/2 and terminal siloxy units selected from the class consisting of those of the formulas R 3 SiO1/2 and (R 2 ) (Q)SiO1/2, wherein the average number of total siloxy units per molecule of the polysiloxane-polyoxyalkylene block copolymer ranges from about 20 to about 200, wherein from about 6 to about 15 percent of said total siloxy units are selected from the group consisting of (R)(Q)SiO and (R 2 ) (Q)SiO1/2 and wherein there are no more than about four RSiO3/2 siloxy units per average polysiloxane molecule, wherein each R individually represents a monovalent hydrocarbon radical or a substituted monovalent hydrocarbon radical, said radicals being free from aliphatic multiple carbon to carbon bonds, and wherein each Q individually represents a polyoxyalkylene polyether block having the formula --MX wherein each M is a bridging group individually selected from the class consisting of --O-- and --C n H 2n O-- wherein n has a value of 2 or 3, and X is a polyoxyalkylene radical consisting essentially of an admixture of Units A and B of the formula (C 2 H 4 O) x (C 3 H 6 O) y Z wherein Z is a terminal group selected from the class consisting of alkyl, aryl and aralkyl radicals, with the proviso that when M is --C n H 2n O-- as defined above, Z can also be a terminal acyl radical, the values of x and y being determined by the following conditions prevailing for Units A and B;

Claim 3

Unit A representing from about 20 to about 80 percent by weight of low molecular weight polyoxyalkylene polyether based on the total weight of Units A and B in said admixture; said polyether being selected from the class consisting of (i) a polyoxyalkylene copolymer having an average molecular weight in the range of from about 800 to about 2300 wherein about 20 to about 60 weight percent of the oxyalkylene groups of said copolymer are oxyethylene, the remainder of the oxyalkylene groups being oxypropylene, and (ii) a blend of at least two polyoxyalkylene copolymers having different average molecular weights in the range of from about 500 to about 2900 and wherein about 20 to about 60 weight percent of the oxyalkylene groups of the copolymers in said blend are oxyethylene, the remainder of the oxyalkylene groups being oxypropylene, with the proviso that said blend has an average molecular weight in the range of from about 800 to about 2300; and Unit B representing from about 80 to about 20 percent by weight of high molecular weight polyoxyalkylene polyether based on the total weight of Units A and B in said admixture said polyether being selected from the class consisting of (i) a polyoxyalkylene copolymer having an average molecular weight in the range of from about 3400 to about 5500 wherein about 20 to about 60 weight percent of the oxyalkylene groups of said copolymer are oxyethylene, the remainder of the oxyalkylene groups being oxypropylene, and (ii) a blend of at least two polyoxyalkylene copolymers having different average molecular weights in the range of from about 3000 to about 5500 and wherein about 20 to about 60 weight percent of the oxyalkylene groups of the copolymers in said blend are oxyethylene, the remainder of the oxyalkylene groups being oxypropylene, with the proviso that said blend has an average molecular weight in the range of from about 3400 to about 5500; and with the added proviso that said admixture of Units A and B has an average molecular weight in the range of from about 1600 to about 2900.

Claim 4

Unit A representing from about 20 to about 80 percent by weight of low molecular weight polyoxyalkylene polyether based on the total weight of Units A and B in said admixture; said polyether being selected from the class consisting of (i) a polyoxyalkylene copolymer having an average molecular weight in the range of from about 800 to about 2300 wherein about 20 to about 60 weight percent of the oxyalkylene groups of said copolymer are oxyethylene, the remainder of the oxyalkylene groups being oxypropylene, and (ii) a blend of at least two polyoxyalkylene copolymers having different average molecular weights in the range of from about 500 to about 2900 and wherein about 20 to about 60 weight percent of the oxyalkylene groups of the copolymers in said blend are oxyethylene, the remainder of the oxyalkylene groups being oxypropylene, with the proviso that said blend has an average molecular weight in the range of from about 800 to about 2300; and Unit B representing from about 80 to about 20 percent by weight of high molecular weight polyoxyalkylene polyether based on the total weight of Units A and B in said admixture said polyether being selected from the class consisting of (i) a polyoxyalkylene copolymer having an average molecular weight in the range of from about 3400 to about 5500 wherein about 20 to about 60 weight percent of the oxyalkylene groups of said copolymer are oxyethylene, the remainder of the oxyalkylene groups being oxypropylene, and (ii) a blend of at least two polyoxyalkylene copolymers having different average molecular weights in the range of from about 3000 to about 5500 and wherein about 20 to about 60 weight percent of the oxyalkylene groups of the copolymers in said blend are oxyethylene, the remainder of the oxyalkylene groups being oxypropylene, with the proviso that said blend has an average molecular weight in the range of from about 3400 to about 5500; and with the added proviso that said admixture of Units A and B has an average molecular weight in the range of from about 1600 to about 2900.

Claim 5

A process as defined in claim 1, wherein said block copolymer consists essentially of from about 18 to about 27 percent by weight of polysiloxane blocks and from about 73 to about 82 percent by weight of polyoxyalkylene blocks, wherein R is a methyl radical and wherein the oxyalkylene groups in said copolymers of Units A and B are present in a random distribution.

Claim 6

A process as defined in claim 2 wherein M is --O-- and Z is an alkyl radical.

Claim 7

A process as defined in claim 2, wherein M is --C 3 H 6 O-- and Z is an alkyl radical.

Claim 8

A process as defined in claim 2, wherein said block copolymer simultaneously contains both polyoxyalkylene blocks of the formulas --OX and --C 3 H 6 OX and wherein Z is an alkyl radical.

Claim 9

A process as defined in claim 2, wherein Unit A represents a low molecular weight polyoxyalkylene copolymer having an average molecular weight in the range of from about 800 to about 2300; and wherein Unit B represents a high molecular weight polyoxyalkylene copolymer having an average molecular weight in the range of from about 3400 to about 5500.

Claim 10

A process as defined in claim 6, wherein said admixture consists essentially of about 25 to about 50 percent by weight of Unit A and about 75 to about 50 percent by weight of Unit B, wherein said low molecular weight polyoxyalkylene copolymer has an average molecular weight in the range of from about 900 to about 1300 wherein about 30 to about 55 weight percent of the oxyalkylene groups of said copolymer are oxyethylene, the remainder of the oxyalkylene groups being oxypropylene; wherein said high molecular weight polyoxyalkylene copolymer has an average molecular weight in the range of from about 3800 to about 5000, wherein about 30 to about 55 weight percent of the oxyalkylene groups of said copolymer are oxyethylene, the remainder of the oxyalkylene groups being oxypropylene; wherein said admixture of Units A and B has an average molecular weight in the range of about 2000 to about 2400, wherein M is an --C 3 H 6 O-- bridging group and wherein Z is an alkyl radical.

Claim 11

A process as defined in claim 2, wherein Unit A represents a blend of at least two low molecular weight polyoxyalkylene copolymers having different average molecular weights in the range of about 500 to about 2900, with the proviso that said blend has an average molecular weight in the range of from about 800 to about 2300; and wherein Unit B represents a high molecular weight polyoxyalkylene copolymer having an average molecular weight in the range of from about 3400 to about 5500.

Claim 12

A process as defined in claim 8, wherein said admixture consists essentially of about 30 to about 60 percent by weight of Unit A, and about 70 to about 40 percent by weight of Unit B, wherein at least one of said low molecular weight polyoxyalkylene copolymers has an average molecular weight in the range of from about 900 to about 1300 and at least one of said low molecular weight polyoxyalkylene copolymers has an average molecular weight in the range of from about 1700 to about 2900 and wherein about 30 to about 55 weight percent of the oxyalkylene groups of the copolymers in said blend of Unit A are oxyethylene, the remainder of the oxyalkylene groups being oxypropylene, with the proviso that said blend of Unit A has an average molecular weight in the range of from about 1100 to about 1900; wherein said high molecular weight polyoxyalkylene copolymer has an average molecular weight in the range of from about 3800 to about 5000 wherein about 30 to about 55 weight percent of the oxyalkylene groups of said copolymer are oxyethylene, the remainder of the oxyalkylene groups being oxypropylene, wherein M is a bridging group selected from the class consisting of --O-- and --C 3 H 6 O--; and wherein Z is an alkyl radical.

Claim 13

A process as defined in claim 2, wherein Unit A represents a low molecular weight polyoxyalkylene copolymer having an average molecular weight in the range of from about 800 to about 2300; and wherein Unit B represents a blend of at least two high molecular weight polyoxyalkylene copolymers having different average molecular weights in the range of about 3000 to about 5500, with the proviso that said blend has an average molecular weight in the range of from about 3400 to about 5500.

Claim 14

A process as defined in claim 10, wherein said admixture consists essentially of about 30 to about 60 percent by weight of Unit A and about 70 to about 40 percent by weight of Unit B, wherein said low molecular weight polyoxyalkylene copolymer has an average molecular weight in the range of about 900 to about 1300 and wherein about 30 to about 55 weight percent of the oxyalkylene groups of said copolymer are oxyethylene, the remainder of the oxyalkylene groups being oxypropylene; wherein at least one of said high molecular weight polyoxyalkylene copolymers has an average molecular weight in the range of from about 3000 to about 3400 and at least one of said high molecular weight polyoxyalkylene copolymers has an average molecular weight in the range of from about 3800 to about 5000 wherein about 30 to about 55 weight percent of the oxyalkylene groups of the copolymers in said blend of Unit B are oxyethylene, the remainder of the oxyalkylene groups being oxypropylene, with the proviso that said blend of Unit B has an average molecular weight in the range of from about 3400 to about 5000; and with the added proviso that said admixture of Units A and B has an average molecular weight in the range of from about 1600 to about 2600; wherein M is a bridging group selected from the class consisting of --O-- and --C 3 H 6 O-- and wherein Z is an alkyl radical.

Claim 15

A process as defined in claim 2, wherein Unit A represents a blend of at least two low molecular weight polyoxyalkylene copolymers having different average molecular weights in the range of about 500 to about 2900, with the proviso that said blend has an average molecular weight in the range of from about 800 to about 2300; and wherein Unit B represents a blend of at least two high molecular weight polyoxyalkylene copolymers having different average molecular weights in the range of about 3000 to about 5500, with the proviso that said blend has an average molecular weight in the range of from about 3400 to about 5500.

Claim 16

A process as defined in claim 1, wherein said block copolymer consists essentially of R 2 SiO, (R) (Q)SiO and R 3 SiO1/2 siloxy units.

Claim 17

A process as defined in claim 1, wherein said block copolymer consists essentially of R 2 SiO, (R) (Q)SiO and (R 2 ) (Q)SiO1/2 siloxy units.

Claim 18

A process as defined in claim 1, wherein said block copolymer consists essentially of R 2 SiO, (R) (Q)SiO, RSiO3/2 and R 3 SiO1/2 siloxy units.

Claim 19

A process as defined in claim 1, wherein said block copolymer consists essentially of R 2 SiO;, (R) (Q)SiO, RSiO3/2 and (R 2 ) (Q)SiO1/2 siloxy units.

Claim 20

A process as defined in claim 1, wherein said block copolymer consists essentially of R 2 SiO, RSiO3/2 and (R 2 ) (Q)SiO1/2 siloxy units.

Claim 21

A process as defined in claim 1, said block copolymer consisting essentially of from about 19 to about 26 percent by weight of polysiloxane blocks and from about 81 to about 74 percent by weight of polyoxyalkylene blocks, and further consisting essentially of from about 65 to about 140 slurry units of the formula (CH 3 ) 2 SiO, from about 6 to about 17 siloxy units of the formula CH 3 (Q)SiO and about two siloxy units of the formula (CH 3 ) 3 SiO1/2, wherein about 7 to about 14 percent of the total siloxy units are CH 3 (Q)SiO units, wherein M is a --C 3 H 6 O-- bridging group, wherein said admixture consists essentially of about 25 to about 50 percent by weight of Unit A and about 75 to about 50 percent by weight of Unit B, wherein Unit A represents a low molecular weight polyoxyalkylene copolymer having an average molecular weight in the range of from about 900 to about 1300 wherein from about 20 to about 60 weight percent of the oxyalkylene groups of said copolymer are oxyethylene, the remainder of the oxyalkylene groups being oxypropylene, said oxyalkylene groups being present in the copolymer in a random distribution, wherein Unit B represents a high molecular weight polyoxyalkylene copolymer having an average molecular weight in the range of from about 3800 to about 5000, wherein from about 20 to about 60 weight percent of the oxyalkylene groups of said copolymer are oxyethylene, the remainder of the oxyalkylene groups being oxypropylene, said oxyalkylene groups being present in the copolymer in a random distribution, and wherein said admixture of Units A and B has an average molecular weight in the range of from about 1800 to about 2600.

Claim 22

A process as defined in claim 18, wherein said block copolymer consists essentially of from about 20 to about 24 percent by weight of polysiloxane blocks and from about 80 to about 76 percent by weight of polyoxyalkylene blocks and further consists essentially of from about 100 to about 135 siloxy units of the formula (CH 3 ) 2 SiO, from about 10 to 15 siloxy units of the formula CH 3 (Q)SiO, and about two siloxy units of the formula (CH 3 ) 3 SiO1/2, wherein about 8 to about 12 percent of the total siloxy units are CH 3 (Q)SiO, wherein Z represents a methyl or n-butyl radical, wherein said admixture consists essentially of about 35 to about 45 percent by weight of the low molecular weight polyoxyalkylene polyether copolymer and about 65 to about 55 percent by weight of the high molecular weight polyoxyalkylene polyether copolymer wherein said high molecular weight copolymer has an average molecular weight of from about 4000 to about 5000, wherein from about 30 to about 55 weight percent of the oxyalkylene groups of the copolymers of Units A and B are oxyethylene, the remainder of the oxyalkylene groups being oxypropylene, and wherein said admixture of Units A and B has an average molecular weight of from about 2000 to about 2400.

Claim 23

A process as defined in claim 1, said block copolymer consisting essentially of from about 19 to about 26 percent by weight of polysiloxane blocks and from about 81 to about 74 percent by weight of polyoxyalkylene blocks and further consisting essentially of from about 25 to about 65 siloxy units of the formula (CH 3 ) 2 SiO, from about 3.5 to about 7.5 siloxy units of the formula CH 3 (Q)SiO and about two siloxy units of the formula (CH 3 ) 3 SiO1/2, wherein about 10 to about 12 percent of the total siloxy units are CH 3 (Q)SiO units, wherein M is a --C 3 H 6 O-- bridging group, wherein said admixture consists essentially of about 35 to 45 percent by weight of Unit A and about 65 to 55 percent by weight of Unit B, wherein Unit A represents a low molecular weight polyoxyalkylene polyether copolymer having an average molecular weight in the range of from about 800 to about 1300 wherein from about 20 to about 60 weight percent of the oxyalkylene groups of said polyether copolymer are oxyethylene, the remainder of the oxyalkylene groups being oxypropylene, said oxyalkylene groups being present in the copolymer in a random distribution, wherein Unit B represents a blend of two high molecular weight polyoxyalkylene polyether copolymers, said blend consisting of from about 50 to about 75 percent by weight of a polyoxyalkylene polyether copolymer having an average molecular weight in the range of from about 3000 to about 3400, wherein from about 20 to about 60 weight percent of the oxyalkylene groups of said polyethylene copolymer are oxyethylene, the remainder of the oxyalkylene groups being oxypropylene, said oxyalkylene groups in the copolymer being present in a random distribution, and from about 50 to about 25 percent by weight of a polyoxyalkylene polyether copolymer having an average molecular weight in the range of from about 3800 to about 5000, wherein from about 20 to about 60 weight percent of the oxyalkylene groups of said polyether copolymer are oxyethylene, the remainder of the oxyalkylene groups being oxypropylene, said oxyalkylene groups being present in the copolymer in a random distribution, wherein said blend of Unit B has an average molecular weight in the range of from about 3400 to about 4000 and wherein said admixture of Units A and B has an average molecular weight in the range of about 1600 to about 2100.

Claim 24

A process as defined in claim 20, wherein said block copolymer consists essentially of from about 20 to about 24 percent by weight of polysiloxane blocks and from about 80 to about 76 percent by weight of polyoxyalkylene blocks and further consists of from about 40 to about 60 siloxy units of the formula (CH 3 ) 2 SiO, from about 4 to about 7 siloxy units of the formula (CH 3 ) (Q)SiO and about two siloxy units of the formula (CH 3 ) 2 SiO1/2 wherein Z represents a methyl or n-butyl radical, wherein Unit B represents a blend consisting of from 60 to about 70 percent by weight of a polyoxyalkylene polyether copolymer having an average molecular weight in the range of from about 3000 to about 3400 and from about 40 to about 30 percent by weight of a polyoxyalkylene polyether copolymer having an average molecular weight of from about 3800 to about 5000, wherein about 30 to about 55 weight percent of the oxyalkylene groups of the copolymers of Units A and B are oxyethylene, the remainder of the oxyalkylene groups being oxypropylene, wherein said blend of Unit B has an average molecular weight in the range of about 3400 to about 3800 and wherein said admixture of Units A and B has an average moleculare weight in the range of from about 1700 to about 1900.

Claim 25

A process as defined in claim 1, said block copolymer consisting essentially of from about 17 to about 26 percent by weight of polysiloxane blocks and from about 83 to about 74 percent by weight of polyoxyalkylene blocks, and further consisting essentially of from about 17 to about 24 siloxy units of the formula (CH 3 ) 2 SiO, from about 1.2 to about 1.8 siloxy units of the formula CH 3 SiO 1 .5 and from about 3 to about 4 siloxy units of the formula (CH 3 ) 2 QSiO1/2, wherein M is a --0-- bridging group, wherein said admixture consists essentially of from about 30 to about 40 percent by weight of Unit A and from about 70 to about 60 percent by weight of Unit B, wherein Unit A represents a low molecular weight polyoxyalkylene polyether copolymer having an average molecular weight in the range of from about 900 to about 1300 wherein from about 20 to about 60 weight percent of the oxyalkylene groups of said polyether copolymer are oxyethylene, the remainder of the oxyalkylene groups being oxypropylene, said oxyalkylene groups being present in the copolymer in a random distribution, wherein Unit B represents a blend of two high molecular weight polyoxyalkylene polyether copolymers, said blend consisting of from about 55 to about 70 percent by weight of a polyoxyalkylene polyether copolymer having an average molecular weight in the range of from about 3000 to about 3400 wherein from about 20 to about 60 weight percent of the oxyalkylene groups of said polyether copolymer are oxyethylene, the remainder of the oxyalkylene groups being oxypropylene, said oxyalkylene groups being present in the copolymer in a random distribution, and from about 45 to about 30 percent by weight of a polyoxyalkylene polyether copolymer having an average molecular weight in the range of from about 3800 to about 5500 wherein from about 20 to about 60 weight percent of the oxyalkylene groups of said polyether copolymer are oxyethylene, the remainder of the oxyalkylene groups being oxypropylene, said oxyalkylene groups being present in the copolymer in a random distribution, wherein said blend of Unit B has an average molecular weight in the range from about 3400 to about 4000 and wherein said admixture of Units A and B has an average molecular weight in the range of from about 1600 to about 2100.

Claim 26

A process as defined in claim 22, wherein said block copolymer consists essentially of from about 19 to about 24 percent by weight of polysiloxane blocks and about 83 to about 74 percent by weight of polyoxyalkylene blocks, wherein Z is a n-butyl radical, wherein from about 45 to about 30 percent by weight of said blend of Unit B is a polyoxyalkylene polyether copolymer having an average molecular weight in the range of from about 4000 to about 5000, wherein about 30 to about 55 weight percent of the oxyalkylene groups of the copolymers of Units A and B are oxyethylene, the remainder of the oxyalkylene groups being oxypropylene, wherein said blend of Unit B has an average molecular weight of from about 3400 to about 3800, and wherein said admixture of Units A and B has an average molecular weight of from about 1700 to about 1900.