Preparation and use of high surface area transition metal catalysts
Assignee: United States Department of the Interior
•
Filing: 1976-11-03
•
Granted: 1978-01-31
•
Expires: 1996-11-03
Abstract
Abstract Highly active catalysts, suitable for use in hydrogenation and other reactions, are prepared from an alloy of one or more of the Group VIII transition metals with yttrium or a rare earth metal. The alloy is ground to the desired particle size and is thereafter reacted with a gas containing carbon monoxide and hydrogen to form an intimate physical admixture of the Group VIII metal or its corresponding carbide with the oxide of yttrium or the rare earth metal.
Inventors
- 👤 Gary B. Atkinson
- 👤 Larry J. Nicks
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 09:56
CPC Classifications
B; B01; B01J; B01J37/00; B01J37/16; B01J23/00; B01J23/70; B01J23/76; C; C07; C07C; C07C1/00; C07C1/02; C07C1/04; C07C1/0425; C07C1/0445; C07C2523/00; C07C2523/10; C07C2523/70; C07C2523/74; C07C2523/745; C07C2523/75; C07C2523/755; C07C2523/76; C07C2523/83
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
86 words
A method for preparing a catalyst which comprises: a. forming an alloy of a first metal selected from the group consisting of nickel, cobalt, iron and mixtures thereof with a second metal selected from the group consisting of yttrium, the rare earth metals and mixtures thereof, said first metal comprising from 5 to 95 wt-pct of said alloy; and b. reacting said alloy with a gas comprising hydrogen and carbon monoxide at a temperature sufficiently high for a time sufficiently long to oxidize said second metal.
Claim 2
Independent Claim
86 words
A method for preparing a catalyst which comprises: a. forming an alloy of a first metal selected from the group consisting of nickel, cobalt, iron and mixtures thereof with a second metal selected from the group consisting of yttrium, the rare earth metals and mixtures thereof, said first metal comprising from 5 to 95 wt-pct of said alloy; and b. reacting said alloy with a gas comprising hydrogen and carbon monoxide at a temperature sufficiently high for a time sufficiently long to oxidize said second metal.
Claim 3
Dependent Claim
11 words
The method of claim 1 wherein said first metal is nickel.
Claim 4
Dependent Claim
11 words
The method of claim 1 wherein said first metal is cobalt.
Claim 5
Dependent Claim
20 words
The method of claim 2 wherein said second metal is mischmetal and wherein said temperature is greater than 300° C.
Claim 6
Dependent Claim
20 words
The method of claim 2 wherein said second metal is cerium and wherein said temperature is greater than 300° C.
Claim 7
Dependent Claim
51 words
The method of claim 1 wherein the resulting catalyst is additionally subjected to a surface enhancement step, said step comprising contacting said catalyst with a gas comprising hydrogen and carbon monoxide at a temperature below the temperature required to oxidize said alloy for a time sufficient to reach an equilibrium state.
Claim 8
Dependent Claim
33 words
The method of claim 6 wherein said first metal is nickel and wherein said temperature is sufficiently high so as to avoid any substantial formation of nickel carbonyl but below about 275° C.
Claim 9
Dependent Claim
11 words
The method of claim 7 wherein said second metal is mischmetal.
Claim 10
Dependent Claim
11 words
The method of claim 7 wherein said second metal is cerium.
Claim 11
Dependent Claim
9 words
A catalyst prepared by the method of claim 1.
Claim 12
Dependent Claim
9 words
A catalyst prepared by the method of claim 6.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-01-30 | 1981-08-01 | 1982-01-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-01-30 | 1985-08-01 | 1986-01-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-01-30 | 1989-08-01 | 1990-01-31 | $7700.00 | Window Closed / Lapsed |