US4071357A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for recovering zinc from steel-making flue dust
Assignee: Hazen Research Inc
•
Filing: 1976-09-23
•
Granted: 1978-01-31
•
Expires: 1996-09-23
Abstract
Abstract A method for recovering a substantially impurity-free zinc oxide product from steel-making flue dust or a similar material which comprises leaching the flue dust with concentrated ammonia and carbon dioxide to dissolve zinc and unwanted impurities, cementing the leach filtrate with zinc to remove copper, cadmium, and lead impurities, conducting a steam distillation on the cementation filtrate to precipitate basic zinc carbonate, remove the ammonia and carbon dioxide, and iron impurities, and filtering to provide a residue of essentially basic zinc carbonate, sulfur, and chromium. This residue is then washed to remove soluble sulfates, dried, and calcined at high temperatures to break down the basic zinc carbonate into zinc oxide, water washed to remove chromium and the residue of the water wash dried to produce the desired impurity-free zinc oxide product. The two water washes may be combined into one step performed after the calcining step to remove both sulfur and chromium in one wash step.
Inventors
- 👤 Mark A. Peters
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 11:08
CPC Classifications
C; C22; C22B; C22B19/00; C22B19/20; C22B19/24; C22B19/34; C22B7/00; C22B7/02; Y; Y02; Y02P; Y02P10/00; Y02P10/20; Y10; Y10S; Y10S75/00; Y10S75/961
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
187 words
A process for recovering metal values from a steel-making flue dust containing zinc, iron, lead, copper, chromium and cadmium as impurities comprising: a. leaching the feed material with ammonia and carbon dioxide in high concentration and filtering to produce a leach residue and a filtrate containing zinc values and the impurities; b. cementing the leach filtrate from step (a) with zinc to remove lead, copper and cadmium and performing a liquid/solids separation on the resulting slurry; c. steam distilling the cementation filtrate from step (b) to precipitate basic zinc carbonate; d. performing an initial liquid/solids separation on the steam distillation slurry of step (c) immediately after steam distillation has begun to scavenge out the iron content of the slurry and then continuing the steam distillation until all of the zinc has precipitated as zinc carbonate; e. calcining the zinc carbonate precipitate of step (d) at a temperature between 200° C-1100° C to convert the zinc carbonate to zinc oxide; and f. washing the zinc oxide product of step (e) in water to remove sulfate and chromium converted to the soluble form by the calcination of step (e).
Claim 2
Dependent Claim
187 words
A process for recovering metal values from a steel-making flue dust containing zinc, iron, lead, copper, chromium and cadmium as impurities comprising: a. leaching the feed material with ammonia and carbon dioxide in high concentration and filtering to produce a leach residue and a filtrate containing zinc values and the impurities; b. cementing the leach filtrate from step (a) with zinc to remove lead, copper and cadmium and performing a liquid/solids separation on the resulting slurry; c. steam distilling the cementation filtrate from step (b) to precipitate basic zinc carbonate; d. performing an initial liquid/solids separation on the steam distillation slurry of step (c) immediately after steam distillation has begun to scavenge out the iron content of the slurry and then continuing the steam distillation until all of the zinc has precipitated as zinc carbonate; e. calcining the zinc carbonate precipitate of step (d) at a temperature between 200° C-1100° C to convert the zinc carbonate to zinc oxide; and f. washing the zinc oxide product of step (e) in water to remove sulfate and chromium converted to the soluble form by the calcination of step (e).
Claim 3
Dependent Claim
27 words
The process of claim 1 in which in step (d) the initial filtration step is performed when approximately one percent of the total precipitate has been formed.
Claim 4
Dependent Claim
23 words
The process of claim 1 in which the zinc carbonate precipitate of step (d) is washed with water to remove sulfate before calcining.
Claim 5
Dependent Claim
59 words
In the process for recovering zinc from metal impurities with which it is associated by dissolving the zinc and metal impurities in ammonium carbonate followed by precipitating the zinc as zinc carbonate by steam distillation, the improvement which comprises immediately filtering the steam distillation slurry after steam distillation has begun to scavenge out the iron content of the slurry.
Claim 6
Dependent Claim
59 words
In the process for recovering zinc from metal impurities with which it is associated by dissolving the zinc and metal impurities in ammonium carbonate followed by precipitating the zinc as zinc carbonate by steam distillation, the improvement which comprises immediately filtering the steam distillation slurry after steam distillation has begun to scavenge out the iron content of the slurry.
Claim 7
Dependent Claim
42 words
In the process of producing zinc oxide from zinc carbonate by calcination, the improvement for producing a chromium-free zinc oxide which comprises calcining the zinc carbonate at a temperature between 200° C-1100° C and washing the formed zinc oxide product in water.
Claim 8
Dependent Claim
42 words
In the process of producing zinc oxide from zinc carbonate by calcination, the improvement for producing a chromium-free zinc oxide which comprises calcining the zinc carbonate at a temperature between 200° C-1100° C and washing the formed zinc oxide product in water.
References Cited (Backward Citations)
US803472A
Cited
US1706143A
Cited
US1879834A
Cited
US1780323A
Cited
US2144299A
Cited
US3849121A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-01-30 | 1981-08-01 | 1982-01-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-01-30 | 1985-08-01 | 1986-01-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-01-30 | 1989-08-01 | 1990-01-31 | $7700.00 | Window Closed / Lapsed |