Plywood adhesives using amylaceous extenders comprising finely ground cereal-derived high fiber by-product

Claim 2

An adhesive consisting of a combination of urea-formaldehyde resin present in the range of 20-40%, water in the range of 25-60%, filler in the range of 2-4%, catalyst in the range of 1-4%, and an amylaceous extender in the range of 10-40%, said amylaceous extender including 30-100% of a finely ground cereal-derived high fiber by-product containing less than 50% starch and 0-70% of an auxiliary amylaceous material said high fiber by-product being selected from the group comprising corn bran, sorghum bran, oat hulls, barley hulls, rice hulls, rice bran, wheat bran, oilseed processing by-products such as soy bean hulls and cottonseed hulls, spent brewers grains, expelled or extracted corn germ, and malt husks and said auxiliary amylaceous material being selected from the group of cereal flour, starch, or fraction thereof, derived from a cereal grain, the high fiber by-product being of a type having substantially greater water absorption properties than the auxiliary amylaceous material.

Claim 3

An adhesive as claimed in claim 1 in which the auxiliary amylaceous material comprises cereal flours, starches, or fractions thereof, derived from the group comprising corn, sorghum, wheat, rice, barley, oats, and cereal grains.

Claim 4

An adhesive consisting of a combination of urea-formaldehyde resin present in the range of 20-40%, water in the range of 25-60%, filler in the range of 2-4%, catalyst in the range of 1-4%, and an extender in the range of 10-40%, which comprises a finely ground fibrous by-product from the group of corn bran, soy hulls, malt husks, oat feed, wheat bran, barley hulls and extracted corn germ, and said fibrous by-product being blended with an auxiliary amylaceous material in the form of cereal flours, starches, or fractions thereof, derived from the group comprising corn, sorghum, wheat, rice, barley, oats, and other cereal grains to provide a room temperature to 32° C viscosity of between 1,000 and 5,000 CPS at 20 rpm for the combination.

Claim 5

An adhesive consisting of a combination of urea-formaldehyde resin present in the range of 20-40%, water in the range of 25-60%, filler in the range of 2-4%, catalyst in the range of 1-4%, and an extender in the range of 10-40%, which comprises a finely ground fibrous by-product from the group of corn bran, soy hulls, malt husks, oat feed, wheat bran, barley hulls and extracted corn germ, and said fibrous by-product being blended with an auxiliary amylaceous material in the form of cereal flours, starches, or fractions thereof, derived from the group comprising corn, sorghum, wheat, rice, barley, oats, and other cereal grains to provide a room temperature to 32° C viscosity of between 1,000 and 5,000 CPS at 20 rpm for the combination.

Claim 6

An adhesive consisting of a combination of urea-formaldehyde resin present in the range of 20-40%, water in the range of 25-60%, filler in the range of 2-4%, catalyst in the range of 1-4%, and an extender in the range of 10-40%, which comprises a finely ground fibrous by-product from the group of corn bran, soy hulls, malt husks, oat feed, wheat bran, barley hulls and extracted corn germ, and said fibrous by-product being blended with an auxiliary amylaceous material in the form of cereal flours, starches, or fractions thereof, derived from the group comprising corn, sorghum, wheat, rice, barley and oats to provide a room temperature to 32° C viscosity of between 1,000 and 5,000 CPS at 20 rpm for the combination and wherein the combination is neutral or slightly acidic and said high fiber by-product has substantially greater water absorption properties than the auxiliary amylaceous material.

Claim 7

An adhesive consisting of a combination of urea-formaldehyde resin present in the range of 20-40%, water in the range of 25-60%, filler in the range of 2-4%, catalyst in the range of 1-4%, and an extender in the range of 10-40%, which comprises a finely ground fibrous by-product from the group of corn bran, soy hulls, malt husks, oat feed, wheat bran, barley hulls and extracted corn germ, and said fibrous by-product being blended with an auxiliary amylaceous material in the form of cereal flours, starches, or fractions thereof, derived from the group comprising corn, sorghum, wheat, rice, barley and oats to provide a room temperature to 32° C viscosity of between 1,000 and 5,000 CPS at 20 rpm for the combination and wherein the combination is neutral or slightly acidic and said high fiber by-product has substantially greater water absorption properties than the auxiliary amylaceous material.

Claim 8

An adhesive with a water absorption viscosity system and employing starches in a neutral to acidic mix, the combination of urea-formaldehyde resin present in the range of 20-40%, water in the range of 25-60%, filler in the range of 2-4%, catalyst in the range of 1-4%, and an extender in the range of 10-40%, which comprises a finely ground fibrous by-product having generally a viscosity above the desired adhesive viscosity selected from the group of corn bran, soy, hulls, malt husks, oat feed, wheat bran, barley hulls and extracted corn germ, and said fibrous by-product being blended with an auxiliary amylaceous material in the form of cereal flours, starches, or fractions thereof, derived from the group comprising corn, sorghum, wheat, rice, barley, oats, and other cereal grains having a generally lower viscosity than said fibrous by-product to provide room temperature to 32° C viscosity of between 1,000 and 5,000 CPS at 20 rpm for the combination.

Claim 9

An adhesive with a water absorption viscosity system and employing starches in a neutral to acidic mix, the combination of urea-formaldehyde resin present in the range of 20-40%, water in the range of 25-60%, filler in the range of 2-4%, catalyst in the range of 1-4%, and an extender in the range of 10-40%, which comprises a finely ground fibrous by-product having generally a viscosity above the desired adhesive viscosity selected from the group of corn bran, soy, hulls, malt husks, oat feed, wheat bran, barley hulls and extracted corn germ, and said fibrous by-product being blended with an auxiliary amylaceous material in the form of cereal flours, starches, or fractions thereof, derived from the group comprising corn, sorghum, wheat, rice, barley, oats, and other cereal grains having a generally lower viscosity than said fibrous by-product to provide room temperature to 32° C viscosity of between 1,000 and 5,000 CPS at 20 rpm for the combination.

Claim 10

An adhesive in accordance with claim 1 wherein said filler is from the group of ground clays, wood-fiber base products, bark walnut shell and coconut shell, flours and the fibrous residues from the production of furfural.

Claim 11

An adhesive with a water absorption viscosity system and employing starches in a neutral to acidic mix, the combination of urea-formaldehyde resin present in the range of 20-40%, water in the range of 25-60%, filler in the range of 2-4%, catalyst in the range of 1-4%, and an extender in the range of 10-40% which comprises a blend of 0-80% finely ground cereal-derived high fiber by-product and 100-0% of an auxiliary amylaceous extender to provide a room temperature to 32° C viscosity of between 1,000 and 5,000 CPS at 20 rpm for the combination.

Claim 12

An adhesive with a water absorption viscosity system and employing starches in a neutral to acidic mix, the combination of urea-formaldehyde resin present in the range of 20-40%, water in the range of 25-60%, filler in the range of 2-4%, catalyst in the range of 1-4%, and an extender in the range of 10-40% which comprises a blend of 0-80% finely ground cereal-derived high fiber by-product and 100-0% of an auxiliary amylaceous extender to provide a room temperature to 32° C viscosity of between 1,000 and 5,000 CPS at 20 rpm for the combination.

Claim 13

An adhesive with a water absorption viscosity system and employing starches in a neutral to acidic mix, the combination of urea-formaldehyde resin present in the range of 20-40%, water in the range of 25-60%, filler in the range of 2-4%, catalyst in the range of 1-4%, and an extender in the range of 10-40% which comprises a blend of 0-80% corn bran, 100-0% sorghum hulls to provide a room temperature to 32° C viscosity of between 1,000 and 5,000 CPS at 20 rpm for the combination.

Claim 14

An adhesive with a water absorption viscosity system and employing starches in a neutral to acidic mix, the combination of urea-formaldehyde resin present in the range of 20-40%, water in the range of 25-60%, filler in the range of 2-4%, catalyst in the range of 1-4%, and an extender in the range of 10-40% which comprises a blend of 0-80% corn bran, 100-0% sorghum hulls to provide a room temperature to 32° C viscosity of between 1,000 and 5,000 CPS at 20 rpm for the combination.

Claim 15

In a method of manufacturing a plywood adhesive with a water absorption viscosity system and employing starches in a neutral to acidic mix, wherein urea-formaldehyde resin is present in the range of 20-40%, water in the range of 25-60%, filler in the range of 2-4%, catalyst in the range of 1-4%, and an amylaceous extender in the range of 10-40% are combined, the improvement comprising the step of controlling the viscosity of the adhesive by blending the amylaceous extender from a finely ground fibrous by-product having generally a viscosity above the desired viscosity selected from the group of corn bran, soy hulls, malt husks, oat feed, wheat bran, barley hulls and extracted corn germ, with an auxiliary amylaceous material having a generally lower viscosity than said fibrous by-product, said auxiliary amylaceous material comprising cereal flours, starches, or fractions thereof, derived from the group comprising corn, sorghum, wheat, rice, barley, oats, and cereal grains, to provide room temperature to 32° C viscosity of between 1,000 and 5,000 CPS at 20 rpm for the combination.

Claim 16

In a method of manufacturing a plywood adhesive with a water absorption viscosity system and employing starches in a neutral to acidic mix, wherein urea-formaldehyde resin is present in the range of 20-40%, water in the range of 25-60%, filler in the range of 2-4%, catalyst in the range of 1-4%, and an amylaceous extender in the range of 10-40% are combined, the improvement comprising the step of controlling the viscosity of the adhesive by blending the amylaceous extender from a finely ground fibrous by-product having generally a viscosity above the desired viscosity selected from the group of corn bran, soy hulls, malt husks, oat feed, wheat bran, barley hulls and extracted corn germ, with an auxiliary amylaceous material having a generally lower viscosity than said fibrous by-product, said auxiliary amylaceous material comprising cereal flours, starches, or fractions thereof, derived from the group comprising corn, sorghum, wheat, rice, barley, oats, and cereal grains, to provide room temperature to 32° C viscosity of between 1,000 and 5,000 CPS at 20 rpm for the combination.