Assignee: General Electric Co
•
Filing: 1976-08-20
•
Granted: 1978-01-17
•
Expires: 1996-08-20
Abstract
Abstract A phosphor screen for converting x-rays to light includes a large number of discrete columns of the phosphor material, say doped CsI, with the spaces therebetween preferably filled with a reflective substance, which itself may be phosphor (e.g., Gd 2 O 2 S or La 2 O 2 S). Because of the resulting inhibition of lateral spread of light within the phosphor screen, it may be made thicker than conventional screens while achieving at least as high resolution and contrast, thereby increasing brightness (and thus requiring lower x-ray "doses"). A method for making the screen includes using a patterned substrate and wide-angle vapor deposition (as in a hot-wall evaporator) so as to deposit the phosphor only on the raised portions of the substrate.
Inventors
- 👤 Stanley J. Lubowski
- 👤 Robert K. Swank
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 02:15
CPC Classifications
C; C09; C09K; C09K11/00; C09K11/08; C09K11/77; C09K11/7701; C09K11/0827; C09K11/0833; C09K11/61; C09K11/615; C09K11/616; G; G21; G21K; G21K4/00; H; H01; H01J; H01J29/00; H01J29/02; H01J29/10; H01J29/36; H01J29/38; H01J29/385; H01J9/00; H01J9/02; H01J9/12
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
167 words
A method for making an improved phosphor screen of the type which absorbs one type of radiation and re-emits a different type of radiation, comprising the steps of: patterning a generally planar substrate so as to form a large plurality of relatively raised portions, each separated by a relatively recessed portion, throughout a substantial area of said substrate; vapor depositing a phosphor material on said patterned substrate at substantial angles relative to the normal to said substrate so that only said raised portions are covered by a substantial thickness of said phosphor material and said recessed portions receive substantially none, thereby yielding a phosphor layer comprising columns of phosphor material substantially separated from each other; and heat annealing said column-type phosphor screen so as to cause the phosphor material thereof to become substantially transparent by substantially eliminating any small bubbles which could otherwise cause radiation scattering within the material, whereby a phosphor screen including a series of spaced substantially transparent columns of the phosphor material is formed.
Claim 2
Independent Claim
167 words
A method for making an improved phosphor screen of the type which absorbs one type of radiation and re-emits a different type of radiation, comprising the steps of: patterning a generally planar substrate so as to form a large plurality of relatively raised portions, each separated by a relatively recessed portion, throughout a substantial area of said substrate; vapor depositing a phosphor material on said patterned substrate at substantial angles relative to the normal to said substrate so that only said raised portions are covered by a substantial thickness of said phosphor material and said recessed portions receive substantially none, thereby yielding a phosphor layer comprising columns of phosphor material substantially separated from each other; and heat annealing said column-type phosphor screen so as to cause the phosphor material thereof to become substantially transparent by substantially eliminating any small bubbles which could otherwise cause radiation scattering within the material, whereby a phosphor screen including a series of spaced substantially transparent columns of the phosphor material is formed.
Claim 3
Dependent Claim
14 words
A method according to claim 1, in which: said phosphor material comprises cesium iodide.
Claim 4
Dependent Claim
27 words
A method according to claim 1, in which: said phosphor material comprises cesium iodide doped with a metal selected from the group consisting of thallium and sodium.
Claim 5
Dependent Claim
49 words
A method according to claim 1, in which: said phosphor material is deposited by a hot-wall evaporator, so that most of the phosphor material reaching said substrate bounces off the side walls of the evaporator and is incident on said substrate at a large angle relative to its normal.
Claim 6
Dependent Claim
34 words
A method according to claim 1, in which: after vapor depositing of said phosphor material but before heat annealing, said column-type phosphor layer is heat treated to increase the spaces between said phosphor columns.
Claim 7
Dependent Claim
34 words
A method according to claim 5, in which: said heat treating step comprises heating said composite substrate and phosphor material to a temperature of between approximately 450°-500° C for about 20 to 60 minutes.
Claim 8
Dependent Claim
29 words
A method according to claim 5, in which: both said vapor depositing and said intermediate treating steps are repeated at least once before said heat annealing step is effected.
Claim 9
Dependent Claim
38 words
A method according to claim 1, in which: said heat annealing step comprises heating said phosphor material for a substantial period of time to a temperature near its melting point under conditions which limit its tendency to sublime.
Claim 10
Dependent Claim
37 words
A method according to claim 8, in which: said phosphor material is cesium iodide and said heat annealing step comprises heating to about 615° C for about 2-3 hours under about one atmosphere of an inert gas.
Claim 11
Dependent Claim
58 words
A method according to claim 1, in which: after said heat annealing step, the spaces between said phosphor material columns are filled with a substance which is highly reflective of the radiation emitted by said phosphor material, so that radiation escaping from a side wall of a column from which it originates is reflected back into that column.
Claim 12
Dependent Claim
17 words
A method according to claim 10, in which: said reflective substance comprises titanium dioxide (TiO 2 ).
Claim 13
Dependent Claim
21 words
A method according to claim 10, in which: said reflective substance comprises a second phosphor material which also exhibits reflecting properties.
Claim 14
Dependent Claim
34 words
A method according to claim 12, in which: said reflective phosphor substance is chosen from the group consisting of gadolinium oxysulfide (Gd 2 O 2 S) and lanthanum oxysulfide (La 2 O 2 S).
Claim 15
Dependent Claim
35 words
A method according to claim 10, in which: after said space-filling step, a transparent material is coated on top of said columns and reflective substance, so as to form a flat, relatively smooth upper surface.
Claim 16
Dependent Claim
37 words
A method according to claim 1, in which: said raised portions of said substrate are about a few mils square in dimension and said recessed portions and their relative depth are on the order of a mil.
References Cited (Backward Citations)
US3360450A
Cited
US3769059A
Cited
US3783297A
Cited
US3783299A
Cited
US3783298A
Cited
US3857036A
Cited
US3930065A
Cited
US3868512A
Cited
US3873065A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-01-16 | 1981-07-18 | 1982-01-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-01-16 | 1985-07-18 | 1986-01-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-01-16 | 1989-07-18 | 1990-01-17 | $7700.00 | Window Closed / Lapsed |