Water dispersible, low molecular weight polyamide resin particles of uniform sizes, method of preparing same and coatings formed therefrom
Assignee: FMC Corp
•
Filing: 1976-04-30
•
Granted: 1978-01-17
•
Expires: 1996-04-30
Abstract
Abstract Finely-divided, water dispersible, low molecular weight, linear polyamide resin particles having a unique morphology and of uniform particle sizes are formed by preparing a linear polyamide of a predetermined low molecular weight in the presence of water followed by rapidly quenching the reaction mass with an aqueous medium below the freezing point of the polyamide and continuing the cooling of the mass to a temperature sufficiently low so as to prevent particle growth and structural alteration while regulating the pH of the quenched mass to provide particles of predetermined, uniform size dispersed in the aqueous medium. The particles vary from ultimate flaky sheets or lamellae to loosely packed, randomly oriented, clusters of flaky sheets. Spray dried products may be agglomerates which disintegrate readily in water to the original particles or aggregates depending upon intended uses. The dispersions and dried products are useful in the coating art and the polyamide may be polymerized to high molecular weights after application to a substrate.
Inventors
- 👤 Charles F. Ferraro
- 👤 Richard A. Javick
- 👤 James A. Robertson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 16:09
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/12; C08J3/122; C08G; C08G69/00; C08G69/46; C08J2377/00
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
135 words
As an article of manufacture, free flowing, spray dried low molecular weight, linear polyamide resin powder having a reduced viscosity of between about 0.1 and about 0.4, consisting essentially of loosely bound agglomerates of loosely packed, randomly oriented, clusters of flaky sheets, the flaky sheets having a mean particle size between 0.03 micron and about 6 microns and the particle size distribution is about d±0.8d where d is the means particle size, the agglomerates having a size within a range of between about 3 microns and about 150 microns and being further characterized in that when dispersed in water the agglomerates disintegrate into loosely packed, randomly oriented, clusters to flaky sheets having particle sizes of approximately the same size and size distribution as the original flaky sheets and form a stable dispersion of flaky sheets.
Claim 2
Dependent Claim
135 words
As an article of manufacture, free flowing, spray dried low molecular weight, linear polyamide resin powder having a reduced viscosity of between about 0.1 and about 0.4, consisting essentially of loosely bound agglomerates of loosely packed, randomly oriented, clusters of flaky sheets, the flaky sheets having a mean particle size between 0.03 micron and about 6 microns and the particle size distribution is about d±0.8d where d is the means particle size, the agglomerates having a size within a range of between about 3 microns and about 150 microns and being further characterized in that when dispersed in water the agglomerates disintegrate into loosely packed, randomly oriented, clusters to flaky sheets having particle sizes of approximately the same size and size distribution as the original flaky sheets and form a stable dispersion of flaky sheets.
Claim 3
Dependent Claim
56 words
The article of manufacture as defined in claim 1 wherein the polyamide resin is selected from the group consisting of ε-caprolactam, a copolymer of ε-caprolactam and 11-aminoundecanoic acid, a copolymer of ε-caprolactam and 12-aminododecanoic acid and a copolymer of ε-caprolactam and hexamethylenediammonium adipate, the polyamide resin having a reduced viscosity between about 0.15 and about 0.26.
Claim 4
Dependent Claim
51 words
The article of manufacture as defined in claim 2 wherein the free flowing powder includes between about 0.15% and about 0.8%, base on the weight of the polyamide resin, of a catalyst consisting of a non-volatile, strong acid or a compound which upon heating is converted to a non-volatile strong acid.
Claim 5
Dependent Claim
33 words
The article of manufacture as defined in claim 3 wherein the free flowing powder includes between about 1% and about 8%, based on the weight of the polyamide resin, of a flow promoter.
Claim 6
Independent Claim
225 words
The method of forming free-flowing, low molecular weight, linear polyamide resin powder which comprises mixing a least one polyamide forming monomer or high molecular weight, linear polyamide and water, heating the mixture under pressure to a temperature sufficiently high and for a period sufficient to form a linear polyamide of a predetermined low molecular weight, the temperature exceeding the melting point of the formed polyamide, thereafter instantaneously quenching the heated mixture in an aqueous quenching medium to instantaneously reduce the temperature of the heated mixture to a temperature below the freezing point of the formed polyamide and to bring the mass to a pH between about pH 3 and pH 9 thereby converting the formed polyamide into finely-divided, water dispersible, low molecular weight, linear polyamide resin particles having particle sizes within a narrow particle size distribution and to instantaneously reduce the temperature of the mass to a temperature where particle growth is prevented and the particle size and structure is retained, recovering a stable aqueous dispersion of the finely-divided, low molecular weight, linear polyamide resin particles in the form of loosely packed, randomly oriented clusters of flaky sheets in the aqueous medium, spray drying the recovered stable aqueous dispersion and recovering a free-flowing, low molecular weight, linear polyamide resin powder consisting essentially of loosely bound agglomerates of loosely packed, randomly oriented, clusters of flaky sheets.
Claim 7
Independent Claim
225 words
The method of forming free-flowing, low molecular weight, linear polyamide resin powder which comprises mixing a least one polyamide forming monomer or high molecular weight, linear polyamide and water, heating the mixture under pressure to a temperature sufficiently high and for a period sufficient to form a linear polyamide of a predetermined low molecular weight, the temperature exceeding the melting point of the formed polyamide, thereafter instantaneously quenching the heated mixture in an aqueous quenching medium to instantaneously reduce the temperature of the heated mixture to a temperature below the freezing point of the formed polyamide and to bring the mass to a pH between about pH 3 and pH 9 thereby converting the formed polyamide into finely-divided, water dispersible, low molecular weight, linear polyamide resin particles having particle sizes within a narrow particle size distribution and to instantaneously reduce the temperature of the mass to a temperature where particle growth is prevented and the particle size and structure is retained, recovering a stable aqueous dispersion of the finely-divided, low molecular weight, linear polyamide resin particles in the form of loosely packed, randomly oriented clusters of flaky sheets in the aqueous medium, spray drying the recovered stable aqueous dispersion and recovering a free-flowing, low molecular weight, linear polyamide resin powder consisting essentially of loosely bound agglomerates of loosely packed, randomly oriented, clusters of flaky sheets.
Claim 8
Dependent Claim
74 words
The method as defined in claim 5 wherein the mixture contains between about 30% and about 80% by weight of the monomer or polyamide with the balance water, the mixture is heated to a temperature between about 220° C. and about 280° C. for from about 4 hours to about 24 hours and the heated mixture is instantaneously quenched to reduce the temperature of the heated mixture to a temperature below about 95° C.
References Cited (Backward Citations)
US2348751A
Cited
US2742440A
Cited
US3564599A
Cited
US3476711A
Cited
US3299011A
Cited
US3481906A
Cited
US3844991A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-01-16 | 1981-07-18 | 1982-01-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-01-16 | 1985-07-18 | 1986-01-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-01-16 | 1989-07-18 | 1990-01-17 | $7700.00 | Window Closed / Lapsed |