US4068030A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Multilevel embossing by printing with a reactive monomer
Assignee: Armstrong World Industries Inc
•
Filing: 1974-02-04
•
Granted: 1978-01-10
•
Expires: 1994-02-04
Abstract
Abstract An improvement in the process for producing a decorative surface covering having a multilevel embossed wear surface wherein, a layer of vinyl chloride resin dryblend which may be foamable or unfoamable, and which contains a polymerizable monomer having at least two olefinically unsaturated sites is formed. After sintering to achieve a solid but porous layer having substantial voids throughout, a plurality of resinous ink compositions, formulated to produce varying degrees of elevation in the final product, are applied in a design. Among the inks used are non-monomer-containing ink compositions which may include foamable and non-foamable inks and which may or may not include a catalyst for the monomer in the dryblend. The improvement of this invention comprises the inclusion in the plurality of inks printed in a design on the monomer-containing dryblend layer of an ink containing the same polymerizable monomer as that in the dryblend, and a catalyst for the monomer. Upon subsequent heat and fusion, the areas to which the inks containing the monomer and/or the catalyst for the monomer were applied will have a different height and surface texture from those produced by the other inks and from that of surrounding regions where no ink was applied; thus producing an embossed textured effect.
Inventors
- 👤 Jack H. Witman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 09:51
CPC Classifications
B; B29; B29D; B29D99/00; B29D99/0057; B32; B32B; B32B5/00; B32B5/22; B32B5/24; B32B5/245; B32B38/00; B32B38/06; B32B38/14; B32B38/145; B32B5/18; B32B5/20; B44; B44C; B44C1/00; B44C1/20; B44C1/205; D; D06; D06N; D06N3/00; D06N3/04; D06N3/06; D06N7/00; D06N7/0005; D06N7/0007; D06N7/0013; D06N7/0039; D06N7/0057; E; E04; E04F; E04F13/00; E04F13/07; E04F13/08; E04F13/18; E04F15/00; E04F15/02; E04F15/10; B29L; B29L2031/00; B29L2031/30; B29L2031/3005; B29L2031/3017; B32B2471/00; B32B2607/00; B32B2607/02; Y; Y10; Y10S; Y10S264/00; Y10S264/82; Y10T; Y10T428/00; Y10T428/24; Y10T428/24355; Y10T428/24372; Y10T428/24405; Y10T428/24479; Y10T428/24496; Y10T428/24504; Y10T428/24521; Y10T428/24537; Y10T428/24595; Y10T428/24612; Y10T428/24802; Y10T428/24893; Y10T428/24901; Y10T428/24942; Y10T428/2495; Y10T428/24967
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
95 words
A decorative surface covering comprising a base layer of fused, dryblend containing polymerized monomer therein, a plurality of fused ink-containing regions at least one of which extends upwardly from within said base layer to a point of elevation above the surface thereof, at least one of said ink-containing regions containing said monomer in cross-linked condition in both the ink and the dryblend, and at least one of the remainder of said plurality of ink-containing regions being free of said cross-linked monomer, whereby embossed wear surface areas are achieved which differ in elevation and surface texture.
Claim 2
Dependent Claim
95 words
A decorative surface covering comprising a base layer of fused, dryblend containing polymerized monomer therein, a plurality of fused ink-containing regions at least one of which extends upwardly from within said base layer to a point of elevation above the surface thereof, at least one of said ink-containing regions containing said monomer in cross-linked condition in both the ink and the dryblend, and at least one of the remainder of said plurality of ink-containing regions being free of said cross-linked monomer, whereby embossed wear surface areas are achieved which differ in elevation and surface texture.
Claim 3
Dependent Claim
17 words
The decorative surface covering of claim 1 including a clear resinous coating over the top surface thereof.
Claim 4
Dependent Claim
76 words
A decorative surface covering according to claim 1, wherein the base layer of fused dryblend is foamed, at least one of said ink-containing regions containing said monomer in cross-linked condition in both the ink and in the dryblend is of lesser thickness than said foamed base layer, and wherein at least one of the remainder of said plurality of ink-containing regions free of said cross-linked monomer is of a different thickness than said monomer-containing inked regions.
Claim 5
Dependent Claim
17 words
The decorative surface covering of claim 3 including a clear resinous coating on the top surface thereof.
Claim 6
Dependent Claim
216 words
In the process for producing a decorative surface covering having a multilevel embossed wear surface comprising forming a dryblend composition comprising vinyl chloride resin particles, plasticizer, and a polymerizable monomer having at least two olefinically unsaturated sites, forming a layer of said dryblend having a thickness in the range of about 0.005-0.080 inch, heating said layer to sinter the dryblend without fusion and to form a porous, open layer, forming design areas on at least a portion of said dryblend layer by applying thermoplastic resinous ink thereto in an amount sufficient to cause penetration thereof into the dryblend to a depth of at least 2 mils at the points of application, and finally heating to fuse all thermoplastic resins, the improvement comprising forming said design areas by applying a plurality of thermoplastic resinous inks of different compositions, at least one of said thermoplastic inks containing a polymerizable monomer having at least two olefinically unsaturated sites, and a polymerization catalyst therefor, and at least one ink having a composition free of both monomer and catalyst, said final heating step causing polymerization and cross-linking of the monomer in the monomer-containing ink and in the dryblend in the areas to which it was applied, whereby embossed design areas are achieved on the final product which produce different embossed effects.
Claim 7
Dependent Claim
216 words
In the process for producing a decorative surface covering having a multilevel embossed wear surface comprising forming a dryblend composition comprising vinyl chloride resin particles, plasticizer, and a polymerizable monomer having at least two olefinically unsaturated sites, forming a layer of said dryblend having a thickness in the range of about 0.005-0.080 inch, heating said layer to sinter the dryblend without fusion and to form a porous, open layer, forming design areas on at least a portion of said dryblend layer by applying thermoplastic resinous ink thereto in an amount sufficient to cause penetration thereof into the dryblend to a depth of at least 2 mils at the points of application, and finally heating to fuse all thermoplastic resins, the improvement comprising forming said design areas by applying a plurality of thermoplastic resinous inks of different compositions, at least one of said thermoplastic inks containing a polymerizable monomer having at least two olefinically unsaturated sites, and a polymerization catalyst therefor, and at least one ink having a composition free of both monomer and catalyst, said final heating step causing polymerization and cross-linking of the monomer in the monomer-containing ink and in the dryblend in the areas to which it was applied, whereby embossed design areas are achieved on the final product which produce different embossed effects.
Claim 8
Dependent Claim
23 words
The process according to claim 5 wherein at least one of said ink compositions contains a polymerization catalyst and is free of monomer.
Claim 9
Dependent Claim
13 words
The process according to claim 5 wherein the polymerization catalyst is benzoyl peroxide.
Claim 10
Dependent Claim
23 words
The process according to claim 5 wherein at least one of said ink compositions penetrates 100% of the thickness of said dryblend layer.
Claim 11
Dependent Claim
21 words
The process according to claim 5 wherein said polymerizable monomer in the dryblend and in the ink is trimethylol propane trimethacrylate.
Claim 12
Dependent Claim
15 words
The process according to claim 5 wherein the vinyl chloride resin particles comprise poly(vinyl chloride).
Claim 13
Dependent Claim
14 words
The process according to claim 5 wherein the dryblend composition includes a blowing agent.
Claim 14
Dependent Claim
12 words
The process according to claim 11 wherein the blowing agent is azobisformamide.
Claim 15
Dependent Claim
16 words
The process according to claim 5 wherein the resin in said ink compositions comprises poly(vinyl chloride).
Claim 16
Dependent Claim
23 words
The process according to claim 5 wherein at least one of said ink compositions not containing the polymerizable monomer includes a blowing agent.
Claim 17
Dependent Claim
12 words
The process according to claim 14 wherein the blowing agent is azobisformamide.
Claim 18
Dependent Claim
17 words
The process according to claim 3 wherein the ink composition contains an accelerator for the blowing agent.
Claim 19
Dependent Claim
25 words
The process according to claim 5 wherein a clear coat composition is applied over said printed, sintered dryblend layer prior to the final heating step.
References Cited (Backward Citations)
US592186A
Cited
US2618580A
Cited
US3042137A
Cited
US3442742A
Cited
US3365353A
Cited
US3359352A
Cited
US3538204A
Cited
US3804657A
Cited
US3778291A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-01-09 | 1981-07-11 | 1982-01-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-01-09 | 1985-07-11 | 1986-01-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-01-09 | 1989-07-11 | 1990-01-10 | $7700.00 | Window Closed / Lapsed |