Gold electroplating process
Assignee: AT&T Inc
•
Filing: 1977-03-21
•
Granted: 1978-01-10
•
Expires: 1997-03-21
Abstract
Abstract Certain reducible species are found in gold electroplating solutions which interfere with efficient electroplating of gold and make uncertain gold thickness predictions based on current throughput. A gold electroplating process is described which minimizes formation of undesirable reducible species. This process uses an anode of titanium having a coating of the oxides of ruthenium, iridium, rhodium, titanium or mixtures thereof. In addition, a procedure is described for removing such chemical species from the gold plating bath which does not adversely affect the gold electroplating solution.
Inventors
- 👤 Yutaka Okinaka
- 👤 Catherine Wolowodiuk
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 06:08
CPC Classifications
C; C25; C25D; C25D17/00; C25D17/10; C25D3/00; C25D3/02; C25D3/48
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
113 words
A process for electroplating gold on surfaces using: anode, surface to be plated as cathode, gold plating solution and an electrical source of energy comprising the step of activating the source of electrical energy so that current flows through the anode, the gold plating solution and the cathode; characterized in that the formation of gold III species is minimized by use of an anode structure which comprises a base made of titanium with metal oxide on the surface in which at least 25 percent by weight of the metal oxide is at least one oxide selected from the group consisting of ruthenium oxide, iridium oxide, rhodium oxide, and titanium oxide or mixtures thereof.
Claim 2
Dependent Claim
113 words
A process for electroplating gold on surfaces using: anode, surface to be plated as cathode, gold plating solution and an electrical source of energy comprising the step of activating the source of electrical energy so that current flows through the anode, the gold plating solution and the cathode; characterized in that the formation of gold III species is minimized by use of an anode structure which comprises a base made of titanium with metal oxide on the surface in which at least 25 percent by weight of the metal oxide is at least one oxide selected from the group consisting of ruthenium oxide, iridium oxide, rhodium oxide, and titanium oxide or mixtures thereof.
Claim 3
Dependent Claim
22 words
The process of claim 1 in which the active material is selected from the group consisting of ruthenium oxide and iridium oxide.
Claim 4
Dependent Claim
13 words
The process of claim 2 in which the active material is ruthenium oxide.
Claim 5
Dependent Claim
15 words
The process of claim 3 in which the metal oxide consists essentially of ruthenium oxide.
Claim 6
Dependent Claim
19 words
The process of claim 1 in which the gold plating solution has a pH in the range from 3-10.
Claim 7
Dependent Claim
18 words
The process of claim 5 in which the gold plating solution comprises potassium gold cyanide with citrate buffer.
Claim 8
Dependent Claim
20 words
The process of claim 5 in which the gold plating solution contains potassium gold cyanide and phosphate as the buffer.
Claim 9
Dependent Claim
20 words
The process of claim 5 in which the gold plating solution contains a hardening ion to produce hard gold plating.
Claim 10
Dependent Claim
23 words
The process of claim 1 in which hydrazine is added to the gold plating solution to reduce the concentration of gold III species.
Claim 11
Dependent Claim
24 words
The process of claim 9 in which polarographic measurements are made to estimate the amount of hydrazine needed to reduce the gold III species.
Claim 12
Dependent Claim
19 words
The process of claim 1 in which active charcoal is used to reduce impurities in the gold plating solution.
References Cited (Backward Citations)
US3428544A
Cited
NL6616173A
Cited
US3616445A
Cited
US3491014A
Cited
US3711385A
Cited
US3926751A
Cited
US3865703A
Cited
US3980531A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-01-09 | 1981-07-11 | 1982-01-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-01-09 | 1985-07-11 | 1986-01-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-01-09 | 1989-07-11 | 1990-01-10 | $7700.00 | Window Closed / Lapsed |