Method of making powdered magnetic iron oxide material
Assignee: TDK Corp
•
Filing: 1975-09-23
•
Granted: 1978-01-10
•
Expires: 1995-09-23
Abstract
Abstract A method of producing a powder magnetic material for use as a magnetic recording medium is disclosed. More particularly, the disclosed powder magnetic material is adapted to provide a magnetic recording medium of low electrical resistance. In particular, an alloy of cobalt and at least one element selected from the group consisting of vanadium, molybdenum, copper, maganese, nickel, zinc and iron are deposited onto the surface of particles of magnetic iron oxides such as Fe 3 O 4 or γFe 2 O 3 . Powdered magnetic material of high coercivity, high magnetic flux density and low electrical resistance is obtained.
Inventors
- 👤 Shinji Umeki
- 👤 Kazuhide Aue
- 👤 Yasumichi Tokuoka
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 01:24
CPC Classifications
G; G11; G11B; G11B5/00; G11B5/62; G11B5/68; G11B5/70; G11B5/706; G11B5/70626; G11B5/70642; G11B5/70652; G11B5/70668; G11B5/70673; G11B5/70678; G11B5/70684; G11B5/70689; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/2991
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
175 words
A method for making a powdered magnetic material comprising the steps of: slurrying acicular magnetic iron oxide particles, of a type selected from the group consisting of γ-Fe 2 O 3 and Fe 3 O 4 , in an aqueous solution, having a pH in the range of 8 to 12.5, containing ions of cobalt and ions selected from at least one of the group consisting of Va, Mo, Cu, Mn, Ni, Zn and Fe; reducing the ions to deposit a substantially uniform coating of an alloy on said iron oxide particles, said alloy comprising about 0.65 to 4 wt% of Co, based on the weight of said iron oxide, and about 0.15 to 3 wt%, of said at least one selected element based on the weight of said iron oxide; heat treating said coated iron oxide particles in an atmosphere consisting essentially of nitrogen gas at a temperature in a range of about 300° to 400° C to obtain said powdered magnetic material of high coercivity, high magnetic flux density and low electrical resistance.
Claim 2
Independent Claim
175 words
A method for making a powdered magnetic material comprising the steps of: slurrying acicular magnetic iron oxide particles, of a type selected from the group consisting of γ-Fe 2 O 3 and Fe 3 O 4 , in an aqueous solution, having a pH in the range of 8 to 12.5, containing ions of cobalt and ions selected from at least one of the group consisting of Va, Mo, Cu, Mn, Ni, Zn and Fe; reducing the ions to deposit a substantially uniform coating of an alloy on said iron oxide particles, said alloy comprising about 0.65 to 4 wt% of Co, based on the weight of said iron oxide, and about 0.15 to 3 wt%, of said at least one selected element based on the weight of said iron oxide; heat treating said coated iron oxide particles in an atmosphere consisting essentially of nitrogen gas at a temperature in a range of about 300° to 400° C to obtain said powdered magnetic material of high coercivity, high magnetic flux density and low electrical resistance.
Claim 3
Dependent Claim
18 words
The method of claim 1, wherein Fe 3 O 4 is selected and slurried in said aqueous solution.
Claim 4
Dependent Claim
29 words
The method of claim 2, wherein said iron oxide particles are needle-shaped and have a major axis of about 0.5μ with an axis ratio of about 6 to 8.
Claim 5
Dependent Claim
25 words
The method of claim 1, wherein ions of Cu are selected and said deposited alloy comprises about 3 wt% Co and about 0.4 wt% Cu.
Claim 6
Dependent Claim
24 words
The method of claim 1 wherein ions of Mn are selected and said deposited alloy comprises about 1.5 wt% Co and 0.3 wt% Mn.
Claim 7
Dependent Claim
24 words
The method of claim 1, wherein ions of Zn are selected and said deposited alloy comprises about 4 wt% Co and 3 wt% Zn.
Claim 8
Dependent Claim
29 words
The method of claim 1, wherein ions of V and Mo are selected and said deposited alloy comprises about 0.65-2.15 wt% Co, 0.10-0.44 wt% V, and 0.05-0.2 wt% Mo.
Claim 9
Dependent Claim
42 words
The method of claim 1, wherein said acicular magnetic iron oxide particles of the γ-Fe 2 O 3 type are selected, ions of V are selected and said deposited alloy comprises at least 1.5 wt% Co and at least 1.02 wt% V.
Claim 10
Dependent Claim
40 words
The method of claim 1, wherein said acicular magnetic iron oxide particles of the γ-Fe 2 O 3 type are selected, ions of Fe are selected and said deposited alloy comprises at least 1.33-2.71 wt% Co and 0.4-1.1 wt% Fe.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-01-09 | 1981-07-11 | 1982-01-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-01-09 | 1985-07-11 | 1986-01-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-01-09 | 1989-07-11 | 1990-01-10 | $7700.00 | Window Closed / Lapsed |