Aluminous refractory composition containing carbon
Assignee: Chicago Fire Brick Co
•
Filing: 1977-02-18
•
Granted: 1978-01-03
•
Expires: 1997-02-18
Abstract
Abstract A plastic refractory lining composition which can be applied by hand or trowel to refractory or bare metal surfaces and is particularly resistant to slag and hot metal erosion and to metal skulling is comprised of a blend of high alumina or aluminum silicate coarse aggregates with a fine matrix of calcined alumina, carbon, and bentonite employing a phosphate binder and tetrasodium pyrophosphate for modification and stabilization of plasticity characteristics. Finely divided silicon metal can be included to impart oxidation resistance to the carbon. This refractory is sufficiently "sticky" for ease of building a lining.
Inventors
- 👤 Harold L. Rechter
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 22:48
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/622; C04B35/626; C04B35/63; C04B35/6303; C04B35/6316; C04B35/01; C04B35/10; C04B35/101; C04B35/6306; C04B35/6309; C04B35/632; C04B35/6325; C04B35/66; C04B2111/00; C04B2111/00034; C04B2111/00086; C04B2111/00474; C04B2111/0087; C04B2235/00; C04B2235/02; C04B2235/30; C04B2235/32; C04B2235/3217; C04B2235/3231; C04B2235/3244; C04B2235/34; C04B2235/3418; C04B2235/38; C04B2235/3817; C04B2235/3826; C04B2235/42; C04B2235/422; C04B2235/70; C04B2235/96; C04B2235/9669; C04B2235/9676
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
67 words
A plastic refractory composition comprising in percent by weight on the basis of the solids: ______________________________________
-2/3 inch aggregate of alumina or
aluminum silicate 35-60
-60 mesh tabular or calcined alumina
20-40
Bentonite 4-8
-20 mesh carbon particles 10-18
Phosphate bonding agent 3-10
-325 mesh aluminum trihydrate
0-3
-20 mesh tetrasodium pyrophosphate
0.2-1.5
-20 mesh silicon metal 0-15
and water to bring to a plastic consistency.
______________________________________
Claim 2
Dependent Claim
67 words
A plastic refractory composition comprising in percent by weight on the basis of the solids: ______________________________________
-2/3 inch aggregate of alumina or
aluminum silicate 35-60
-60 mesh tabular or calcined alumina
20-40
Bentonite 4-8
-20 mesh carbon particles 10-18
Phosphate bonding agent 3-10
-325 mesh aluminum trihydrate
0-3
-20 mesh tetrasodium pyrophosphate
0.2-1.5
-20 mesh silicon metal 0-15
and water to bring to a plastic consistency.
______________________________________
Claim 3
Dependent Claim
83 words
A composition in accordance with claim 1 wherein the coarse aggregate is selected from the group of refractory materials consisting of tabular alumina, fused alumina, calcined bauxite, calcined clay, kyanite, quartz, crushed fire brick and mixtures thereof, the carbon particles are graphite, the phosphate bonding agent is phosphoric acid, or monoaluminum dihydrogen phosphate having a P 2 O 5 content equivalent to 75 percent phosphoric acid and the water is present in 10 to 16 percent of the total weight of the composition.
Claim 4
Dependent Claim
49 words
A composition in accordance with claim 1 wherein the -1/4 inch aggregate is calcined bauxite in 40-45 percent by weight, the -60 mesh material is -325 mesh calcined alumina, the phosphate bonding material is 75 percent phosphoric acid, and the -325 mesh aluminum trihydrate is present in 1-2 percent.
Claim 5
Dependent Claim
21 words
A composition in accordance with claim 3 in which silicon metal powder is present in up to 15 percent by weight.
Claim 6
Dependent Claim
31 words
In a refractory plastic composition comprising alumina or aluminum silicate, bentonite, carbon, and a phosphate bonding agent, the improvement of having present tetrasodium pyrophosphate in amount effective to increase storage life.
Claim 7
Dependent Claim
31 words
In a refractory plastic composition comprising alumina or aluminum silicate, bentonite, carbon, and a phosphate bonding agent, the improvement of having present tetrasodium pyrophosphate in amount effective to increase storage life.
Claim 8
Dependent Claim
31 words
The composition of claim 5 in which the alumina or aluminum silicate is calcined, the bentonite is Western bentonite, the carbon is graphite, and the phosphate bonding agent is phosphoric acid.
References Cited (Backward Citations)
US3810768A
Cited
US3842760A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-01-02 | 1981-07-04 | 1982-01-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-01-02 | 1985-07-04 | 1986-01-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-01-02 | 1989-07-04 | 1990-01-03 | $7700.00 | Window Closed / Lapsed |