U.V. Curable poly(ether-urethane) polyacrylates and wet-look polymers prepared therefrom
Assignee: Lilly Industries Inc
•
Filing: 1976-05-11
•
Granted: 1977-12-27
•
Expires: 1996-05-11
Abstract
Abstract Polyether-urethane polymers, prepared from the reaction of specific molar ratios of diisocyanates with specific mixtures of polyetherdiols, glycols, triols and tetraols, and having 4-10 reactive isocyanate groups are further reacted with hydroxyalkyl acrylates through the free isocyanate functionality to provide polymers having from about 4-10 acrylates units per each mole unit of polyurethane chain. Such polymers when crosslinked under ultraviolet radiation in the presence of photosensitizers, specific reactive monofunctional acrylate solvents and multifunctional acrylate cross-linking agents cure without air inhibition to yield superior "wet look" finishes especially useful for coating metal, wood and floor tile.
Inventors
- 👤 Vincent Wen-Hwa Ting
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 12:26
CPC Classifications
D; D06; D06N; D06N3/00; D06N3/04; D06N3/06; D06N3/08; C; C08; C08F; C08F299/00; C08F299/02; C08F299/06; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/65; C08G18/66; C08G18/6666; C08G18/667; C08G18/6674; C08G18/6677; C08G18/67; C08G18/671; C08G18/672; C08G18/70; C08G18/72; C08G18/74; C08G18/75; C08G18/751; C08G18/752; C08G18/753; C08G18/755; Y; Y10; Y10S; Y10S525/00; Y10S525/92
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
89 words
A poly(ether-urethane)polyacrylate polymer comprising the product obtained by reacting a polyurethane intermediate having 4 to 10 terminally-positioned reactive isocyanate groups with 4 to 10 molar equivalents of a hydroxy (lower) acrylate or methacrylate, said intermediate resulting from the reaction of 1 to 7 moles of a polyether diol having a molecular weight in the range of 100 to 10,000; 2 to 8 moles of a monomer polyol having 3 to 12 carbon atoms and at least 3 reactive hydroxyl groups; and 6 to 24 moles of an organic diisocyanate.
Claim 2
Dependent Claim
89 words
A poly(ether-urethane)polyacrylate polymer comprising the product obtained by reacting a polyurethane intermediate having 4 to 10 terminally-positioned reactive isocyanate groups with 4 to 10 molar equivalents of a hydroxy (lower) acrylate or methacrylate, said intermediate resulting from the reaction of 1 to 7 moles of a polyether diol having a molecular weight in the range of 100 to 10,000; 2 to 8 moles of a monomer polyol having 3 to 12 carbon atoms and at least 3 reactive hydroxyl groups; and 6 to 24 moles of an organic diisocyanate.
Claim 3
Dependent Claim
40 words
The polymer of claim 1 wherein the polyether diol is polypropyleether diol having a molecular weight in the range of 350 to 4600; the monomer polyol is trimethylol propane; the diisocyanate is isophorone diisocyanate; and the hydroxyacrylate is 2-hydroxyethyl acrylate.
Claim 4
Dependent Claim
13 words
The composition of claim 2 wherein the molar ratio of polyether:trimethyolpropane:diisocyanate:hydroxyacrylate is 2:3:9:5.
Claim 5
Dependent Claim
52 words
A U.V. curable composition comprising on a weight percent basic 30 to 70 percent of a polyurethane polymer of claim 1: 10 to 40 percent of a monofunctional acrylate monomer; 5 to 50 percent of multifunctional acrylate cross-linking agent and 3 to 5 percent of a photosensitizer, said composition totaling 100 percent.
Claim 6
Dependent Claim
41 words
The composition of claim 4 wherein the polyurethane intermediate comprises the reaction product of 2 moles of a polyether diol, 3 moles of monomer polyol and 9 moles of organic diisocyanate, said intermediate being further reacted with 5 moles of hydroxyalkylacrylate.
Claim 7
Dependent Claim
48 words
The composition of claim 4 wherein the polyurethane intermediate comprises the reaction product of 1 mole of polypropyleneether diol having a molecular weight of 1250, 2 moles of trimethylol propane and 6 moles of isophorone diisocyanate, said intermediate being further reacted with 4 moles of a hydroxyethyl acrylate.
Claim 8
Dependent Claim
20 words
The composition of claim 4 wherein the photosensitizer is selected from the group consisting of benzophenone, diethoxyacetophenone and mixtures thereof.
Claim 9
Dependent Claim
23 words
The composition of claim 5 wherein the photosensitizer is a mixture comprising 1 to 3 parts benzophenone and 1 part of diethoxy acetophenone.
Claim 10
Dependent Claim
132 words
A process for imparting a wet look coating to a substrate which comprises: a. forming a radiation curable composition comprising on a weight percent basis: i. 30 to 70 percent of a poly(ether-urethane) polymer of claim 1: ii. 10 to 40 percent of a monofunctional acrylate monomer iii. 5 to 50 percent of a multifunctional acrylate cross-linking agent; and iv. 3 to 5 percent of a photosensitizer; said composition totaling 100 percent; b. applying said mixture as a 0.1 to 10 mil thick coating to a substrate selected from the group consisting of flat stock metal, wood, fiberboard and floor tile; and c. curing said coating substrate in air at ambient temperature by passing the substrate at a rate of from 10 to 1000 foot/minute through an effective field of ultraviolet radiation.
Claim 11
Dependent Claim
96 words
The process of claim 9 wherein the poly(ether-urethane) polymer comprises the reaction product of: a. a polyether diol having a molecular weight in the range of 100 to 10,000; b. a monomer polyol selected from the group consisting of trimethylol propane, trimethylol ethane, glycerine, polycaprolactone triols, pentaerythritol and mixtures thereof; c. isophorone diisocyanate, and d. hydroxyacrylate selected from the group consisting of 2-hydroxyethylacrylate, 2-hydroxy-3-chloropropyl acrylate, 2-hydroxyethyl methacrylate, 2-hydroxypropylacrylate and mixtures thereof; wherein the ratio of a:b:c:d is 2:3:9:5; and said monofunctional acrylate monomer is selected from the group consisting of 2-phenoxyethyl acrylate, isobornyl acrylate and benzylacrylate.
Claim 12
Dependent Claim
30 words
The process of claim 9 wherein the multifunctional cross-linking agent is selected from the group consisting of melamine acrylate; pentaerythritol triacrylate, trimethylolpropane triacrylate, epoxidized soybean oil acrylate and neopentylglycol diacrylate.
Claim 13
Dependent Claim
21 words
The process of claim 10 wherein the photosensitizer is selected from the group consisting of benzophenone, diethoxy acetophenone and mixtures thereof.
Claim 14
Dependent Claim
19 words
The process of claim 12 wherein the monoacrylate monomer is isobornyl acrylate and the cross-linking agent is melamine acrylate.
Claim 15
Dependent Claim
12 words
The process of claim 10 wherein the substrate is aluminum flat stock.
Claim 16
Dependent Claim
43 words
The process of claim 10 wherein the polyether diol is a polypropyleneether diol having a molecular weight in the range of 350 to 4600; the monomer polyol is trimethylol propane; the hydroxyacrylate is 2-hydroxyethyl acrylate; and the monofunctional acrylate monomer is isobornyl acrylate.
Claim 17
Dependent Claim
37 words
The process of claim 10 wherein up to 50 molar percent of the polypropyleneether diol having a molecular weight in the range of 350 to 4600 is replaced by a polypropyleneether having a molecular weight of 3025.
References Cited (Backward Citations)
US3499852A
Cited
US3989609A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-12-26 | 1981-06-27 | 1981-12-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-12-26 | 1985-06-27 | 1985-12-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-12-26 | 1989-06-27 | 1989-12-27 | $7700.00 | Window Closed / Lapsed |