Continuous heat treatment of cold rolled steel strip
Assignee: Centre de Recherches Metallurgiques CRM ASBL
•
Filing: 1976-01-16
•
Granted: 1977-12-27
•
Expires: 1996-01-16
Abstract
Abstract Cold-rolled steel strip is heated to a temperature higher than its recrystallization temperature, preferably faster than 4° C/s. The strip is then held for more than 30 seconds. The strip is then cooled by immersion in an aqueous bath maintained at substantially its boiling temperature within a temperature range of 80°-150° C.
Inventors
- 👤 Philippe Paulus
- 👤 Mario Econompoulos
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 21:08
CPC Classifications
C; C21; C21D; C21D8/00; C21D8/02; C21D8/04; C21D8/0447; C21D8/0473; C21D1/00; C21D1/56; C21D1/60; C21D9/00; C21D9/52; C21D1/18; C21D1/62; C21D1/63; C21D9/54; C21D9/56; C21D9/573
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
160 words
In a process for continuously heat-treating steel elongated products to increase the limit of elasticity, ductility and homogeneity of properties throughout its width, including the steps of heating the product to a first temperature between its recrystallization temperature and 1000° C, maintaining the process at the first temperature for at least 30 seconds to recrystallize the product and quenching the product, the improvement being that the product is a cold-rolled strip, and providing an aqueous bath quenching medium maintained at a temperature selected to yield a strip product exhibiting a deviation in elastic limit in the direction of width less than ± 3% from the value at the longitudinal axis, which temperature is substantially the boiling point of the bath within a range of 80° to 150° C, immersing the strip in said bath for a time of from 10 seconds to 2 minutes to cool the strip to a second temperature, then further cooling the strip to ambient temperature.
Claim 2
Dependent Claim
160 words
In a process for continuously heat-treating steel elongated products to increase the limit of elasticity, ductility and homogeneity of properties throughout its width, including the steps of heating the product to a first temperature between its recrystallization temperature and 1000° C, maintaining the process at the first temperature for at least 30 seconds to recrystallize the product and quenching the product, the improvement being that the product is a cold-rolled strip, and providing an aqueous bath quenching medium maintained at a temperature selected to yield a strip product exhibiting a deviation in elastic limit in the direction of width less than ± 3% from the value at the longitudinal axis, which temperature is substantially the boiling point of the bath within a range of 80° to 150° C, immersing the strip in said bath for a time of from 10 seconds to 2 minutes to cool the strip to a second temperature, then further cooling the strip to ambient temperature.
Claim 3
Dependent Claim
21 words
The process as claimed in claim 1, in which the heating step is performed at a rate higher than 4° C/s.
Claim 4
Dependent Claim
16 words
The process as claimed in claim 1, in which the aqueous bath consists of water only.
Claim 5
Dependent Claim
31 words
The process as claimed in claim 1, in which the aqueous bath contains in solution or suspension at least one material which modifies the heat transfer coefficient of the aqueous bath.
Claim 6
Dependent Claim
46 words
The process as claimed in claim 4, in which the material is a salt selected from the group consisting of calcium chloride and borax or a surfactant selected from the group consisting of sodium palmitate, potassium palmitate, sodium stearate, potassium stearate, sodium oleate and potassium oleate.
Claim 7
Dependent Claim
26 words
The process as claimed in claim 1, in which the aqueous bath contains in solution or suspension at least one material reducing corrosion of the strip.
Claim 8
Dependent Claim
24 words
The process as claimed in claim 1, in which the cooling rate of the strip in the aqueous bath is 35° to 250° C/s.
Claim 9
Dependent Claim
21 words
The process as claimed in claim 1, further comprising heating the cooled strip to a temperature of 300° to 500° C.
Claim 10
Dependent Claim
18 words
The process as claimed in claim 7, in which the temperature is maintained for longer than 15 seconds.
References Cited (Backward Citations)
US3022205A
Cited
US3030240A
Cited
US3254990A
Cited
US3785878A
Cited
US3669762A
Cited
US3877684A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-12-26 | 1981-06-27 | 1981-12-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-12-26 | 1985-06-27 | 1985-12-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-12-26 | 1989-06-27 | 1989-12-27 | $7700.00 | Window Closed / Lapsed |