Creping process using two-position adhesive application
Assignee: Kimberly Clark Tissue Co
•
Filing: 1976-02-09
•
Granted: 1977-12-20
•
Expires: 1996-02-09
Abstract
Abstract Mechanical creping of fibrous webs is improved by employing two creping adhesives applied at different points in the papermaking process and having relatively different adhesive properties for adhering the web to the creping surface. The process crepes the web from a conventional creping surface by applying a layer of a first creping adhesive directly onto the creping surface while applying a second creping adhesive to the web, followed by pressing the web onto the already formed layer of first creping adhesive and then creping the web from the creping surface.
Inventors
- 👤 Nicholas W. Lazorisak
- 👤 Fredric A. Christiansen
- 👤 John M. Harriz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 15:10
CPC Classifications
D; D21; D21H; D21H21/00; D21H21/14; D21H21/146; B; B31; B31F; B31F1/00; B31F1/12; B31F1/126; D21H17/00; D21H17/20; D21H17/33; D21H17/34; D21H17/36; D21H17/46; D21H17/54; D21H17/55
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
155 words
A method of creping a web from a heated creping surface comprising: applying a layer of a first creping adhesive directly onto the heated creping surface; applying a second creping adhesive to the web; pressing the web onto the already formed layer of first creping adhesive to contact the second creping adhesive with the first creping adhesive for adhesively attaching the web to the creping surface; creping the web from the creping surface; said first creping adhesive being softer than said second creping adhesive and wherein said creping of the web from the creping surface is accomplished with a creping blade urged against the creping surface with sufficient force to crepe by shearing said layer of first creping adhesive whereby said second creping adhesive is essentially removed from the creping surface and a layer consisting essentially of said first creping adhesive is retained on said creping surface after creping the web from the creping surface.
Claim 2
Independent Claim
155 words
A method of creping a web from a heated creping surface comprising: applying a layer of a first creping adhesive directly onto the heated creping surface; applying a second creping adhesive to the web; pressing the web onto the already formed layer of first creping adhesive to contact the second creping adhesive with the first creping adhesive for adhesively attaching the web to the creping surface; creping the web from the creping surface; said first creping adhesive being softer than said second creping adhesive and wherein said creping of the web from the creping surface is accomplished with a creping blade urged against the creping surface with sufficient force to crepe by shearing said layer of first creping adhesive whereby said second creping adhesive is essentially removed from the creping surface and a layer consisting essentially of said first creping adhesive is retained on said creping surface after creping the web from the creping surface.
Claim 3
Dependent Claim
72 words
The method of claim 1, wherein said heated creping surface is a rotating creping surface and said pressing of the web onto the creping surface is at a point disposed in the direction of rotation away from the point on the creping surface where the layer of first creping adhesive is being applied whereby a definitive layer of first creping adhesive is formed by heating before pressing the web onto the layer.
Claim 4
Dependent Claim
92 words
The method of claim 1, wherein the creping of the web from the creping surface is controlled by changing the ratio of the quantity of first creping adhesive applied directly onto the heated creping surface to the quantity of second creping adhesive applied to the web, and the quantity of first creping adhesive is from about 0.01% to about 1.0% based upon the air dry weight of the web and the quantity of second creping adhesive is from about 0.05% to about 4.0% based upon the air dry weight of the web.
Claim 5
Dependent Claim
39 words
The method of claim 1, wherein the first creping adhesive is a latex that produces a water redispersible layer containing the solid components of the latex, said latex having a lower glass transition temperature than the second creping adhesive.
Claim 6
Dependent Claim
29 words
The method of claim 3 wherein said first creping adhesive is a latex that produces a water redispersible layer having a glass transition temperature lower than about +10° C.
Claim 7
Dependent Claim
33 words
The method of claim 3 wherein the first creping adhesive is a latex and the layer has a glass transition temperature of less than about +10° C and comprises essentially non-cross linking polymers.
Claim 8
Independent Claim
197 words
A method of creping a web from a heated rotating creping surface comprising: applying a water emulsion of a first adhesive directly onto the heated creping surface to produce an adhesive layer of the emulsified components on the heated creping surface; applying a second creping adhesive to the web; pressing the web onto the already formed adhesive layer in order to contact the second creping adhesive with the adhesive layer for adhesively attaching the web to the creping surface; and creping the web from the creping surface; wherein a film of the emulsified components of the first creping adhesive has a glass transition temperature of less than about +10° C said first creping adhesive being softer than said second creping adhesive and wherein the creping of the web from the creping surface is performed with a creping doctor blade urged against the surface with sufficient force to crepe by shearing said layer of first creping adhesive so that the second creping adhesive is essentially removed from the creping surface with the creped web and a retained layer consisting essentially of the first creping adhesive remains on the creping surface after creping the web from the creping surface.
Claim 9
Independent Claim
197 words
A method of creping a web from a heated rotating creping surface comprising: applying a water emulsion of a first adhesive directly onto the heated creping surface to produce an adhesive layer of the emulsified components on the heated creping surface; applying a second creping adhesive to the web; pressing the web onto the already formed adhesive layer in order to contact the second creping adhesive with the adhesive layer for adhesively attaching the web to the creping surface; and creping the web from the creping surface; wherein a film of the emulsified components of the first creping adhesive has a glass transition temperature of less than about +10° C said first creping adhesive being softer than said second creping adhesive and wherein the creping of the web from the creping surface is performed with a creping doctor blade urged against the surface with sufficient force to crepe by shearing said layer of first creping adhesive so that the second creping adhesive is essentially removed from the creping surface with the creped web and a retained layer consisting essentially of the first creping adhesive remains on the creping surface after creping the web from the creping surface.
Claim 10
Dependent Claim
23 words
The method of claim 7, further comprising removing a part of the retained layer from the creping surface with a cleaning doctor blade.
Claim 11
Dependent Claim
21 words
The method of claim 7 wherein the first creping adhesive is applied as a water based emulsion of a thermoplastic polymer.
References Cited (Backward Citations)
US962505A
Cited
US1914869A
Cited
US2494723A
Cited
US2343930A
Cited
US2610935A
Cited
US3065486A
Cited
US3812000A
Cited
US3821068A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-12-19 | 1981-06-20 | 1981-12-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-12-19 | 1985-06-20 | 1985-12-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-12-19 | 1989-06-20 | 1989-12-20 | $7700.00 | Window Closed / Lapsed |