Curable, storage-stable liquid organopolysiloxane compositions
Assignee: Rhone Poulenc Industries SA
•
Filing: 1976-02-09
•
Granted: 1977-12-20
•
Expires: 1996-02-09
Abstract
Abstract Curable, storage-stable liquid organopolysiloxane compositions are formulated by [A] admixing (a) a diorganopolysiloxane oil having a viscosity ranging from between 400 and 3,000 cps at 25° C., said diorganopolysiloxane being terminated at its chain ends with a moiety selected from the group consisting of (CH 3 ) 3 SiO 0 .5, (CH 3 ) 2 CH 2 =CHSiO 0 .5 and (CH 3 ) 2 C 6 H 5 SiO 0 .5, and the organo radicals comprising the said diorganopolysiloxane being selected from the group consisting of methyl, vinyl and phenyl, with (b) silica having a specific surface area in excess of 80 m 2 /g, (c) water, and (d) a Si-N bonded silylating agent; [B] next devolatilizing the mixtures [A]; and thence [C] admixing with the devolatilized product [B], (e) an α,ω-dihydroxypolysiloxane oil having a viscosity ranging from between 2,000 and 60,000 cps at 25° C. and (f) an inorganic filler. Organopolysiloxane elastomers useful as molding compositions are prepared by curing the aforesaid formulations.
Inventors
- 👤 Andre Gibard
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 15:44
CPC Classifications
C; C09; C09C; C09C1/00; C09C1/28; C09C1/30; C09C1/3081; C08; C08G; C08G77/00; C08G77/04; C08G77/38; C08K; C08K3/00; C08K3/34; C08K3/36; C08K5/00; C08K5/54; C08L; C08L83/00; C08L83/04; C01; C01P; C01P2006/00; C01P2006/12; C08G77/14; C08G77/16; C08G77/20; C08G77/22; C08G77/26; C08G77/70
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
298 words
A method for the formulation of a curable, storagestable liquid organopolysiloxane composition of matter, which method comprises admixing for at least two hours at a temperature of less than about 60° C. (a) 100 parts by weight of a diorganopolysiloxane oil having a viscosity ranging from between 400 and 3,000 cps at 25° C. wherein the organo radicals comprising the said diorganopolysiloxane are selected from the group consisting of methyl, vinyl and phenyl and are at least 40% methyl, up to 58% phenyl and up to 2% vinyl, said diorganopolysiloxane being terminated at its chain ends with a moiety selected from the group consisting of (CH 3 ) 3 SiO 0 .5, (CH 3 ) 2 CH 2 ═CHSiO 0 .5 and (CH 3 ) 2 C 6 H 5 SiO 0 .5, with (b) 30 to 75 parts by weight of silica having a specific surface area in excess of 80 2 m/g, (c) 1.5 to 7 parts by weight of water, and (d) 4 to 18 parts by weight of a Si-N bonded silylating agent selected from the group consisting of R(CH 3 ) 2 SiNH-Si(CH 3 ) 2 R and R(CH 3 ) 2 SiNHR', wherein each R is either the same or different and is methyl, ethyl, vinyl or phenyl, and R' is methyl or ethyl; next devolatilizing the mixture at a temperature of from about 70° C. to 200° C. under a pressure no greater than atmospheric; and thence admixing with the devolatilized product, 45 to 120 parts of (e) an α,ω-dihydroxypolysiloxane oil having a viscosity ranging from between 2,000 and 60,000 cps at 25° C. and 25 to 120 parts by weight of (f) a filler which is a silica having a specific surface area of less than 50 m 2 /g.
Claim 2
Independent Claim
298 words
A method for the formulation of a curable, storagestable liquid organopolysiloxane composition of matter, which method comprises admixing for at least two hours at a temperature of less than about 60° C. (a) 100 parts by weight of a diorganopolysiloxane oil having a viscosity ranging from between 400 and 3,000 cps at 25° C. wherein the organo radicals comprising the said diorganopolysiloxane are selected from the group consisting of methyl, vinyl and phenyl and are at least 40% methyl, up to 58% phenyl and up to 2% vinyl, said diorganopolysiloxane being terminated at its chain ends with a moiety selected from the group consisting of (CH 3 ) 3 SiO 0 .5, (CH 3 ) 2 CH 2 ═CHSiO 0 .5 and (CH 3 ) 2 C 6 H 5 SiO 0 .5, with (b) 30 to 75 parts by weight of silica having a specific surface area in excess of 80 2 m/g, (c) 1.5 to 7 parts by weight of water, and (d) 4 to 18 parts by weight of a Si-N bonded silylating agent selected from the group consisting of R(CH 3 ) 2 SiNH-Si(CH 3 ) 2 R and R(CH 3 ) 2 SiNHR', wherein each R is either the same or different and is methyl, ethyl, vinyl or phenyl, and R' is methyl or ethyl; next devolatilizing the mixture at a temperature of from about 70° C. to 200° C. under a pressure no greater than atmospheric; and thence admixing with the devolatilized product, 45 to 120 parts of (e) an α,ω-dihydroxypolysiloxane oil having a viscosity ranging from between 2,000 and 60,000 cps at 25° C. and 25 to 120 parts by weight of (f) a filler which is a silica having a specific surface area of less than 50 m 2 /g.
Claim 3
Dependent Claim
14 words
The method as defined by claim 1, wherein the α,ω-dihydroxypolysiloxane (e) is a dihydroxydimethylpolysiloxane.
Claim 4
Dependent Claim
27 words
The method as defined by claim 2, wherein the silica (b) is selected from the group consisting of pyrogenic silica, silica aerogel, silica xerogel and precipitated silica.
Claim 5
Dependent Claim
25 words
The method as defined by claim 3, wherein the inorganic filler (f) is selected from the group consisting of diatomaceus silica and ground quartz silica.
Claim 6
Dependent Claim
26 words
The method as defined by claim 1, further comprising the addition of from about 1 to 4% by weight of gelling agent to the resultant formulation.
Claim 7
Dependent Claim
15 words
The method as defined by claim 5, wherein the gelling agent is hydrogenated castor oil.
Claim 8
Dependent Claim
45 words
The method as defined by claim 1, wherein there are additionally admixed from 0.5 to 6.0% by weight of an α,ω-dihydroxydiorganopolysiloxane oil (g) having a viscosity ranging from between 5 and 100 cps at 25° C., based upon the weight of the α,ω-dihydroxypolysiloxane oil (e).
Claim 9
Dependent Claim
84 words
The method as defined by claim 1, wherein the diorganopolysiloxane oil (a) has a viscosity between 500 and 2,500 cps at 25° C., the α,ω-dihydroxypolysiloxane oil (e) has a viscosity between 3,000 and 50,000 cps at 25° C., and wherein there are admixed 100 parts by weight of the diorganopolysiloxane oil (a), per 35 to 70 parts by weight of the silica (b), per 2 to 6 parts by weight of the water (c), per 5 to 15 parts of the silylating agent (d).
Claim 10
Dependent Claim
34 words
The method as defined by claim 8, wherein there are admixed 48 to 115 parts by weight of the α,ω-dihydroxypolysiloxane oil (e), and 30 to 115 parts by weight of the inorganic filler (f).
Claim 11
Dependent Claim
23 words
The method for the preparation of organopolysiloxane elastomers, which method comprises curing the formulation prepared by the process as defined by claim 1.
Claim 12
Dependent Claim
17 words
The method as defined by claim 10, wherein the curing is effected by means of catalytic cross-linking.
Claim 13
Dependent Claim
85 words
The method as defined by claim 11, wherein the cross-linking agent is a member selected from the group consisting of monomers of the formula Q w Si[(OCH 2 CH 2 ) t OG] 4-w wherein Q is a hydrocarbon having from 1 to 8 carbon atoms, G is alkyl having from 1 to 4 carbon atoms, and w and t are either 0 or 1, and polymers resulting from the partial hydrolysis of monomers of the formula Si(OG) 4 , wherein G is as above.
Claim 14
Dependent Claim
33 words
The method as defined by claim 12, wherein the catalyst is a metal catalyst selected from the group consisting of organo-tin derivatives, metal salts of carboxylic acids and polymeric .tbd. TiOSn .tbd. compositions.
Claim 15
Dependent Claim
10 words
The product of the method as defined by claim 1.
Claim 16
Dependent Claim
10 words
The product of the method as defined by claim 10.
Claim 17
Dependent Claim
11 words
A shaped article comprising the product as defined by claim 15.
References Cited (Backward Citations)
US3642685A
Cited
US3933729A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-12-19 | 1981-06-20 | 1981-12-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-12-19 | 1985-06-20 | 1985-12-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-12-19 | 1989-06-20 | 1989-12-20 | $7700.00 | Window Closed / Lapsed |