Insulated glass and sealant therefor

Claim 2

Insulated glass, including as a sealant therefor, a composition comprising a plasticized cured polyurethane or a plasticized cured polyether, said composition having a moisture vapor transmission rating of no greater than about 1 g/day, an elongation of at least about 100% and low volatility.

Claim 3

Insulated glass according to claim 1 wherein said polyurethane or said polyether comprises about 20 to about 50 wt. % of said composition and said plasticizing material comprises about 20 to about 60 wt. % of said composition and wherein said moisture vapor transmission rating is no greater than about 0.5 g/day.

Claim 4

A plasticized cured composition having a moisture vapor transmission rating of no greater than about 1 g/day, an elongation of at least about 100% and low volatility and comprising: A. about 30 to about 40 wt. % of a polyurethane which is the reaction product of a hydroxyterminated polybutadiene and tolylene diisocyanate or methylene bis-(4-phenyl isocyanate); B. about 20 to about 35 wt. % of plasticizing material, said material comprising about 3 to about 20 wt. % of coal tar having a distillation point of no lower than about 500° F. or roofing asphalt having substantially no volatiles at temperatures up to about 500° F., and said coal tar and said asphalt having substantially no weight loss for 24 hours at 200° F. or polybutene having a weight loss of about 1% or less when subjected to ASTM D-972 for 10 hours at 210° F. or a mixture thereof, and about 80 to about 97 wt. % of phthalates having a boiling point of 450° F. or higher at 10 mm Hg or aromatic resins or aromatic oil or a mixture thereof; C. about 20 to about 35 wt. % of filler; D. about 2 to about 6 wt. % of thixotropic agent; and E. about 0.5 to about 2.5 wt. % of a glass adhesion promoter.

Claim 5

A plasticized cured composition having a moisture vapor transmission rating of no greater than about 1 g/day, an elongation of at least about 100% and low volatility and comprising: A. about 30 to about 40 wt. % of a polyurethane which is the reaction product of a hydroxyterminated polybutadiene and tolylene diisocyanate or methylene bis-(4-phenyl isocyanate); B. about 20 to about 35 wt. % of plasticizing material, said material comprising about 3 to about 20 wt. % of coal tar having a distillation point of no lower than about 500° F. or roofing asphalt having substantially no volatiles at temperatures up to about 500° F., and said coal tar and said asphalt having substantially no weight loss for 24 hours at 200° F. or polybutene having a weight loss of about 1% or less when subjected to ASTM D-972 for 10 hours at 210° F. or a mixture thereof, and about 80 to about 97 wt. % of phthalates having a boiling point of 450° F. or higher at 10 mm Hg or aromatic resins or aromatic oil or a mixture thereof; C. about 20 to about 35 wt. % of filler; D. about 2 to about 6 wt. % of thixotropic agent; and E. about 0.5 to about 2.5 wt. % of a glass adhesion promoter.

Claim 6

A composition according to claim 3 wherein said polyurethane is prepared by reacting said reaction product with a short chain polyol.

Claim 7

Insulated glass including the composition of claim 4 as a sealant therefor and wherein said composition has a moisture vapor transmission rating of no greater than 0.5 g/day.

Claim 8

A plasticized cured composition including a cured polyurethane or a cured polyether and wherein said composition has a moisture vapor transmission rating of no greater than about 1 g/day, an elongation of 100% and low volatility and wherein said cured polyurethane or said cured polyether is the reaction product of a water-sensitive polyether including a polyethylene or polypropylene glycol and wherein said composition comprises: A. about 30 to about 40 wt. % of said cured polyurethane or said cured polyether; B. about 35 to about 55 wt. % of plasticizing material, said material comprising about 25 to about 75 wt. % of coal tar having a distillation point of no lower than about 500° F. or roofing asphalt having substantially no volatiles at a temperature of up about 500° F., and said coal tar and said asphalt having substantially no weight loss for 24 hours at 200° F. or a mixture thereof and about 25 to about 75 wt. % of chlorinated paraffins having a chlorine content of at least about 40-70 wt. % or phthalates having a boiling point of 450° F. or higher at 10 mm Hg or a mixture thereof; C. about 5 to about 30 wt. % of filler; D. about 2 to about 6 wt. % thixotropic agent; and E. about 0.5 to about 2.5 wt. % of a glass adhesion promoter.

Claim 9

A plasticized cured composition including a cured polyurethane or a cured polyether and wherein said composition has a moisture vapor transmission rating of no greater than about 1 g/day, an elongation of 100% and low volatility and wherein said cured polyurethane or said cured polyether is the reaction product of a water-sensitive polyether including a polyethylene or polypropylene glycol and wherein said composition comprises: A. about 30 to about 40 wt. % of said cured polyurethane or said cured polyether; B. about 35 to about 55 wt. % of plasticizing material, said material comprising about 25 to about 75 wt. % of coal tar having a distillation point of no lower than about 500° F. or roofing asphalt having substantially no volatiles at a temperature of up about 500° F., and said coal tar and said asphalt having substantially no weight loss for 24 hours at 200° F. or a mixture thereof and about 25 to about 75 wt. % of chlorinated paraffins having a chlorine content of at least about 40-70 wt. % or phthalates having a boiling point of 450° F. or higher at 10 mm Hg or a mixture thereof; C. about 5 to about 30 wt. % of filler; D. about 2 to about 6 wt. % thixotropic agent; and E. about 0.5 to about 2.5 wt. % of a glass adhesion promoter.

Claim 10

Insulated glass according to claim 1 wherein said polyurethane or said polyether comprises about 30 to about 45 wt. % of the composition and wherein said plasticizing material comprises about 20 to about 40 wt. % of the composition and wherein said moisture vapor transmission rating is no greater than about 0.5 g/day and said elongation is at least about 200%.

Claim 11

Insulated glass according to claim 1 wherein said composition comprises: A. about 25 to about 50 wt. % of a polyurethane prepared from a hydroxyl-terminated diene polymer; and B. a plasticizing material, a. wherein said plasticizing material comprises about 20 to about 40 wt. % of one or more of the following liquid plasticizers: i. a phthalate having a boiling point of no less than about 450° F.; ii. a chlorinated paraffin having a chlorine content of at least about 50-70 wt. %; iii. polybutene having a molecular weight within the range of about 850 to about 2,500 and exhibiting a weight loss of 1% or lower when subjected to ASTM D-972 for 10 hours at 210° F.; or b. wherein said plasticizing material comprises about 30 to about 40 wt. % of a liquid mixture of plasticizing materials, a portion of said mixture comprising one or more of the following: i. about 30 to about 60 wt. % of coaltar having substantially no weight loss in 24 hours at 200° F. and a distillation point of no lower than about 500° F.; ii. about 30 wt. % of roofing asphalt having substantially no weight loss in 24 hours at 200° F. and having substantially no volatiles at temperatures up to about 500° F.; iii. about 20 to about 40 wt. % of aromatic oil; iv. about 40 to about 60 wt. % of an aromatic resin; and the remaining portion of said mixture comprising one or more of the liquid plasticizing materials set forth in subparagraphs (i) to (iii) to paragraph (B) (a) herein.

Claim 12

Insulated glass according to claim 8 wherein said diene polymer is polybutadiene.

Claim 13

Insulated Glass according to claim 8 wherein said phthalate is selected from the group consisting of diisodecyl phthalate and ditridecyl phthalate.

Claim 14

Insulated glass according to claim 10 wherein said diene polymer is polybutadiene.

Claim 15

Insulated glass according to claim 1 wherein said cured polyurethane or said cured polyether is the reaction product of a water-sensitive polyether including a polyethylene or polypropylene glycol and wherein said composition comprises: A. about 20 to about 50 wt. % of said cured polyurethane or said cured polyether; and B. about 40 to about 55 wt. % of a mixture of plasticizing materials, said mixture comprising: a. about 50 to about 90 wt. % of coal tar having a distillation point of no lower than about 500° F. or roofing asphalt having substantially no volatiles at temperatures up to 500° F., and said coal tar and said asphalt having substantially no weight loss for 24 hours at 200° F. or a mixture thereof; and b. about 10 to about 50 wt. % of one or more of the following liquid plasticizing materials: i. a chlorinated paraffin having a chlorine content of at least about 50-70 wt. %; ii. a phthalate having a boiling point of no less than about 450° F.; iii. polybutene having a molecular weight within the range of about 850 to about 2,500 and exhibiting a weight loss of 1% or lower when subjected to ASTM D-972 for 10 hours at 210° F.; and iv. an aromatic oil.

Claim 16

Insulated glass according to claim 12 wherein ingredient (A) is said cured polyurethane.

Claim 17

A plasticized cured composition having a moisture vapor transmission rating of no greater than about 1 g/day, an elongation of at least about 100% and low volatility and comprising: (A) about 30 to about 45 wt. % of polyurethane prepared by reacting a prepolymer of hydroxyl-terminated polybutadiene and tolylene diisocyanate with butanediol; and (B) about 25 to about 35 wt. % of a plasticizing material comprising: i. phthalate having a boiling point of 450° F. or higher at 10 mm Hg; or ii. a mixture of about 5 to about 95 wt. % of said phthalate and 5 to about 95 wt. % of asphalt having substantially no volatiles at temperatures up to about 500° F. and substantially no weight loss for 24 hours at 200° F.; or iii. a mixture of about 5 to about 95 wt. % of said phthalate and about 5 to about 95 wt. % of polybutene having a weight loss of about 1% or less when subjected to ASTM D-972 for 10 hours at 210° F.; C. about 25 to about 35 wt. % of talc or calcium carbonate filler; and D. about 0.5 to about 2.5 wt. % of glass adhesion promoter; and E. about 3 to about 5 wt. % of thixotropic agent.

Claim 18

A plasticized cured composition having a moisture vapor transmission rating of no greater than about 1 g/day, an elongation of at least about 100% and low volatility and comprising: (A) about 30 to about 45 wt. % of polyurethane prepared by reacting a prepolymer of hydroxyl-terminated polybutadiene and tolylene diisocyanate with butanediol; and (B) about 25 to about 35 wt. % of a plasticizing material comprising: i. phthalate having a boiling point of 450° F. or higher at 10 mm Hg; or ii. a mixture of about 5 to about 95 wt. % of said phthalate and 5 to about 95 wt. % of asphalt having substantially no volatiles at temperatures up to about 500° F. and substantially no weight loss for 24 hours at 200° F.; or iii. a mixture of about 5 to about 95 wt. % of said phthalate and about 5 to about 95 wt. % of polybutene having a weight loss of about 1% or less when subjected to ASTM D-972 for 10 hours at 210° F.; C. about 25 to about 35 wt. % of talc or calcium carbonate filler; and D. about 0.5 to about 2.5 wt. % of glass adhesion promoter; and E. about 3 to about 5 wt. % of thixotropic agent.

Claim 19

A composition according to claim 14 wherein said phthalate is ditridecyl phthalate or diisodecyl phthalate.

Claim 20

Insulated glass including the composition of claim 14 as a sealant therefor.

Claim 21

Insulated glass including the composition of claim 15 as a sealant therefor.

Claim 22

A composition for use as an insulated glass sealant comprising a plasticized cured polyurethane or a plasticized cured polyether and a plasticizing material, the water absorption properties of the plasticizing material, as determined by ASTM D570, being less than about 0.1 wt. %; and the volatility properties of the plasticizing material being such that the product of i. the vapor pressure of the plasticizing material in mm of Hg at 480° F and ii. the concentration of the plasticizing material in the composition in wt. % is not greater than about 1200.

Claim 23

A composition for use as an insulated glass sealant comprising a plasticized cured polyurethane or a plasticized cured polyether and a plasticizing material, the water absorption properties of the plasticizing material, as determined by ASTM D570, being less than about 0.1 wt. %; and the volatility properties of the plasticizing material being such that the product of i. the vapor pressure of the plasticizing material in mm of Hg at 480° F and ii. the concentration of the plasticizing material in the composition in wt. % is not greater than about 1200.

Claim 24

A composition according to claim 18 wherein said polyurethane or said polyether comprises about 20 to about 50 wt. % of the composition and said plasticizing material comprises about 20 to about 60 wt. % of the composition.

Claim 25

Insulated glass including the composition of claim 18 as a sealant therefor.

Claim 26

Insulated glass including the composition of claim 19 as a sealant therefor.

Claim 27

A composition according to claim 18 in which the cured polymer is said cured polyurethane.

Claim 28

A composition according to claim 22 wherein said polyurethane is prepared from a hydroxyl-terminated diene polymer.