Polyurethane composition having improved tear strength and process for preparation thereof
Assignee: Bridgestone Corp
•
Filing: 1975-10-23
•
Granted: 1977-12-13
•
Expires: 1995-10-23
Abstract
Abstract A polyurethane composition having high tear strength has been produced by mixing homogeneously 20 to 50 parts by weight of finely divided acidic silica particles, 100 parts by weight of isocyanate-terminated prepolymer and appropriate parts of curative, and curing the mixture in a manner well known in the prior art, where the ratio (l/d) of average chain distance (l) between adjacent crosslinking points of the cured polyurethane chains to average size (d) of finely divided silica particles is in the range of from 2.5 to 20.
Inventors
- 👤 Yoji Watabe
- 👤 Michio Ishii
- 👤 Yutaka Iseda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 12:37
CPC Classifications
C; C08; C08K; C08K3/00; C08K3/34; C08K3/36; G; G06; G06F; G06F3/00; G06F3/06; G06F3/0601; G06F3/0602; G06F3/061; G06F3/0614; G06F3/0619; G06F3/0628; G06F3/0646; G06F3/065; G06F3/0652; G06F3/0668; G06F3/067; H; H04; H04L; H04L67/00; H04L67/01; H04L67/10; H04L67/1095; H04L67/1097
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
97 words
A polyurethane composition for the preparation of articles having a high tear strength, comprising proportionally 100 parts by weight of prepolymer having terminal isocyanate groups, 20 to 50 parts by weight of finely divided acidic silica particles having a pH value of from 3 to 7 and appropriate parts of curative, the number average molecular weight of said prepolymer ranging from 1,000 to 5,000, the ratio (l/d) being such that the average distance (l) between adjacent crosslinking points of the cured polyurethane chains to average size (d) of the acidic silica particles ranges from 2.5 to 20.
Claim 2
Dependent Claim
97 words
A polyurethane composition for the preparation of articles having a high tear strength, comprising proportionally 100 parts by weight of prepolymer having terminal isocyanate groups, 20 to 50 parts by weight of finely divided acidic silica particles having a pH value of from 3 to 7 and appropriate parts of curative, the number average molecular weight of said prepolymer ranging from 1,000 to 5,000, the ratio (l/d) being such that the average distance (l) between adjacent crosslinking points of the cured polyurethane chains to average size (d) of the acidic silica particles ranges from 2.5 to 20.
Claim 3
Dependent Claim
39 words
A polyurethane composition according to claim 1, wherein said ratio (l/d) of average distance (l) between adjacent crosslinking points of the cured polyurethane chains to the average size (d) of the acidic silica particles ranges from 7 to 15.
Claim 4
Dependent Claim
20 words
A polyurethane composition according to claim 1, wherein pH value of the acidic silica particles ranges from 3 to 5.
Claim 5
Dependent Claim
29 words
A polyurethane composition according to claim 1, wherein the amount of the acidic silica particles per 100 parts be weight of the prepolymer ranges from 25 to 45 parts.
Claim 6
Dependent Claim
31 words
A polyurethane composition according to claim 1, wherein the prepolymer has terminal isocyanate groups and comprises at least one species selected from the group consisting of polyether, polyester and polyunsaturated hydrocarbon.
Claim 7
Dependent Claim
38 words
A polyurethane composition according to claim 1, wherein the prepolymer is prepared by reacting an organic polyisocyanate with at least one species selected from the group consisting of polyether, polyol, polyester polyol, polydiene polyol, and the mixture thereof.
Claim 8
Dependent Claim
30 words
A polyurethane composition according to claim 6, wherein material for reaction with the polyisocyanate is at least one species selected from the group consisting of polyoxypropylene glycol and polyoxytetramethylene glycol.
Claim 9
Dependent Claim
35 words
A polyurethane composition according to claim 5, wherein material for reaction with the polyisocyanate is at least one species selected from the group consisting of dihydroxypolyethylene adipate and dihydroxypoly (ethylene glycol / propylene glycol) adipate.
Claim 10
Dependent Claim
31 words
A polyurethane composition according to claim 6, wherein material for reaction with the polyisocyanate is at least one species selected from the group consisting of polybutadiene glycol and butadiene-styrene copolymer glycol.
Claim 11
Dependent Claim
28 words
A polyurethane composition according to claim 6, wherein said polyisocyanate is at least one species selected from the group consisting of aliphatic diisocyanate, alicyclic diisocyanate, and aromatic diisocyanate.
Claim 12
Dependent Claim
46 words
A polyurethane composition according to claim 6, wherein said polyisocyanate is at least one species selected from the group consisting of tolylene-2,4-diisocyanate, tolylene-2,6-diisocyanate, 1,5-naphthalene diisocyanate, diphenyl-4,4'-diisocyanate, 3,3-dimethyl biphenyl-4,4'-diisocyanate, diphenyl-methane-4,4'-diisocyanate, hexane diisocyanate, cyclohexyl-1,3-and -1,4-diisocyanate, methylene bis(4-cyclohexyl isocyanate), 1,3-and 1,4-xylene diisocyanate, 1-methylcyclohexane-2,4-diisocyanate, decaline-1,5-diisocyanate, tolaidine diisocyanate and their mixtures.
Claim 13
Dependent Claim
21 words
A polyurethane composition according to claim 1, wherein the number average molecular weight of the prepolymer ranges from 1,500 to 4,000.
Claim 14
Dependent Claim
20 words
A polyurethane composition according to claim 1, wherein the curative is selected from the group consisting of polyamines and polyols.
Claim 15
Dependent Claim
24 words
A polyurethane composition according to claim 1, wherein the curative is a compound selected from the group consisting of aromatic polyamines and aromatic polyols.
Claim 16
Dependent Claim
57 words
A method of producing a polyurethane composition according to claim 1,which method comprises mixing homogeneously 100 parts by weight of prepolymer having terminal isocyanate groups, 20 to 50 parts by weight of finely divided silica particles having pH values of from 3 to 7 and appropriate parts of curative, and kneading the mixture under strong shearing force.
Claim 17
Dependent Claim
26 words
An article of manufacture comprising a polyurethane composition of claim 1, which is produced by casting and curing the composition of claim 1 in a mould.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-12-12 | 1981-06-13 | 1981-12-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-12-12 | 1985-06-13 | 1985-12-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-12-12 | 1989-06-13 | 1989-12-13 | $7700.00 | Window Closed / Lapsed |