Process for improving the fragmentation capability of metallurgical slags and cinders
Assignee: Entreprise Gagneraud Pere et Fils
•
Filing: 1977-01-18
•
Granted: 1977-12-13
•
Expires: 1997-01-18
Abstract
Abstract The process consists essentially of injecting into slags and cinders derived from the manufacture and various treatments of irons, cast irons, steels, and non-ferrous metals while they are molten and before or during cooling thereof, dry pulverulent mineral compounds capable of releasing non-polluting gases by thermal dissociation (metallic carbonates in particular). The easily fragmented slags and cinders obtained are usable in many fields such as: building and construction, ground coverings, abrasives, water filtering, fertilizers for agriculture, etc.
Inventors
- 👤 Maryan Kunicki
- 👤 Michel Roussel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 13:15
CPC Classifications
C; C04; C04B; C04B5/00; C04B5/06; C21; C21B; C21B3/00; C21B3/04; C21B3/06; C21B2400/00; C21B2400/02; C21B2400/022; Y; Y02; Y02W; Y02W30/00; Y02W30/50; Y10; Y10S; Y10S75/00; Y10S75/958
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
132 words
A process for treating metallurgical slags and cinders to modify their physical-chemical characteristics while conserving energy consumption, and to increase their fragmentability and crushability, comprising: injecting into the slag, by means of compressed air directed substantially perpendicularly to the sheet of molten slag being poured in the molten state from the ladle into the cooling pit, a jet of pulverulent dry material compounds capable of releasing non-polluting gases into the slag by endothermal reaction utilizing a part of the sensible heat of the molten mass of the slag, wherein the temperature of the slag being poured is sufficiently high to permit said endothermal reaction and sufficiently low to permit capture of the gases so produced while the slag is solidifying; and fragmenting or crushing the solidified slag so produced for further use.
Claim 2
Dependent Claim
132 words
A process for treating metallurgical slags and cinders to modify their physical-chemical characteristics while conserving energy consumption, and to increase their fragmentability and crushability, comprising: injecting into the slag, by means of compressed air directed substantially perpendicularly to the sheet of molten slag being poured in the molten state from the ladle into the cooling pit, a jet of pulverulent dry material compounds capable of releasing non-polluting gases into the slag by endothermal reaction utilizing a part of the sensible heat of the molten mass of the slag, wherein the temperature of the slag being poured is sufficiently high to permit said endothermal reaction and sufficiently low to permit capture of the gases so produced while the slag is solidifying; and fragmenting or crushing the solidified slag so produced for further use.
Claim 3
Dependent Claim
14 words
A process in accordance with claim 1 wherein said mineral compounds are metallic carbonates.
Claim 4
Dependent Claim
15 words
A process in accordance with claim 2 wherein said metallic carbonates are non-alkali metal carbonates.
Claim 5
Dependent Claim
26 words
A process in accordance with claim 3 wherein said metallic carbonates are selected from the group consisting of alkaline-earth carbonates and iron, copper and zinc carbonates.
Claim 6
Dependent Claim
22 words
A process in accordance with claim 2 wherein said carbonates are used in combination in the form of the corresponding mineral ores.
Claim 7
Dependent Claim
29 words
A process in accordance with claim 2 wherein said carbonates are in the form of mineral ores selected from the group consisting of limestone, calcite, aragonite, siderite, and smithsonite.
Claim 8
Dependent Claim
26 words
A process in accordance with claim 1 wherein said pulverulent mineral compounds have particle diameters the majority of which are between 20 microns and 10 mm.
Claim 9
Dependent Claim
15 words
A process in accordance with claim 1, wherein the slag is a steel mill slag.
Claim 10
Dependent Claim
24 words
A process in accordance with claim 1, wherein the quantity of injected mineral compounds is between 0.5 and 3% by weight of the slag.
Claim 11
Dependent Claim
16 words
A process in accordance with claim 1, wherein the slag is a phosphated steel mill slag.
Claim 12
Dependent Claim
14 words
A process in accordance with claim 1, wherein the slag is a non-phosphated slag.
Claim 13
Dependent Claim
27 words
A process in accordance with claim 1, further including the step of recycling the solidified fragmented slag, to the metallurgical process by which the slag was produced.
Claim 14
Dependent Claim
23 words
A process in accordance with claim 10, wherein said fragmenting or crushing step comprises crushing to a fine powder for use in fertilizer.
Claim 15
Dependent Claim
133 words
In a process of making non-phosphates steel in a steel mill in which the molten steel and slag produced are separated and solidified and at least a portion of the slag is fragmented step, recycled to the process for making steel, the improvement whereby the fragmentability of the solidified slag is increased, comprising: pouring the molten slag into a cooling area; and injecting into the slag, during said pouring step, pulverulent dry mineral compounds capable of releasing non-polluting gases into the slag by endothermal reaction utilizing a part of the sensible heat of the molten mass of the slag; wherein the temperature of the slag during said injecting step is sufficiently high to permit said endothermal reaction and sufficiently low to permit capture of the gases so produced while the slag is solidifying.
Claim 16
Dependent Claim
133 words
In a process of making non-phosphates steel in a steel mill in which the molten steel and slag produced are separated and solidified and at least a portion of the slag is fragmented step, recycled to the process for making steel, the improvement whereby the fragmentability of the solidified slag is increased, comprising: pouring the molten slag into a cooling area; and injecting into the slag, during said pouring step, pulverulent dry mineral compounds capable of releasing non-polluting gases into the slag by endothermal reaction utilizing a part of the sensible heat of the molten mass of the slag; wherein the temperature of the slag during said injecting step is sufficiently high to permit said endothermal reaction and sufficiently low to permit capture of the gases so produced while the slag is solidifying.
References Cited (Backward Citations)
US2732293A
Cited
GB227848A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-12-12 | 1981-06-13 | 1981-12-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-12-12 | 1985-06-13 | 1985-12-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-12-12 | 1989-06-13 | 1989-12-13 | $7700.00 | Window Closed / Lapsed |