US4061847A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Ethylene polymer acidification process
Assignee: Gulf Research and Development Co
•
Filing: 1973-04-12
•
Granted: 1977-12-06
•
Expires: 1993-04-12
Abstract
Abstract Without changing the physical form of the ethylene polymer, the pendant carboxylate salt groups of an ethylene polymer are converted to the acid form by introducing an article of manufacture having at least a surface comprising an ethylene polymer containing pendant metallic carboxylate salt groups into an aqueous medium containing dissolved ammonia.
Inventors
- 👤 Richard H. Hughes
- 👤 Donald R. Jamieson
- 👤 Rajindar K. Kochhar
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 18:33
CPC Classifications
C; C08; C08J; C08J7/00; C08J7/12; C08J2323/00; C08J2323/02; C08J2323/04; C08J2323/08
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
94 words
A method for chemically modifying at least the surface of a film of an ethylene copolymer containing pendant metallic carboxylate salt groups without changing the physical form of said film which consists essentially of, in combination, 1. immersing a film of an ethylene copolymer containing pendant metallic carboxylate salt groups into an aqueous ammonium hydroxide solution containing 0.5 to 28 weight % ammonia, 2. maintaining said film in said aqueous ammonium hydroxide solution at ambient temperature for a period of 1 to 30 minutes, 3. removing said film from said aqueous ammonium hydroxide solution,
Claim 2
Independent Claim
94 words
A method for chemically modifying at least the surface of a film of an ethylene copolymer containing pendant metallic carboxylate salt groups without changing the physical form of said film which consists essentially of, in combination, 1. immersing a film of an ethylene copolymer containing pendant metallic carboxylate salt groups into an aqueous ammonium hydroxide solution containing 0.5 to 28 weight % ammonia, 2. maintaining said film in said aqueous ammonium hydroxide solution at ambient temperature for a period of 1 to 30 minutes, 3. removing said film from said aqueous ammonium hydroxide solution,
Claim 3
Dependent Claim
95 words
drying the film from (3), and 5. recovering a film in which a substantial proportion of the pendant metallic carboxylate salt groups of the ethylene copolymer has been converted to the corresponding carboxylic acid groups; said ethylene copolymer consisting of at least 67 mol % of polymerized ethylene and containing from 0.01 to 0.5 mol of pendant metallic carboxylate salt groups, per mol of ethylene, the metallic cation of the carboxylate salt groups being selected from the group consisting of metallic cations which are soluble in water or which form a water-soluble complex with ammonia.
Claim 4
Dependent Claim
95 words
drying the film from (3), and 5. recovering a film in which a substantial proportion of the pendant metallic carboxylate salt groups of the ethylene copolymer has been converted to the corresponding carboxylic acid groups; said ethylene copolymer consisting of at least 67 mol % of polymerized ethylene and containing from 0.01 to 0.5 mol of pendant metallic carboxylate salt groups, per mol of ethylene, the metallic cation of the carboxylate salt groups being selected from the group consisting of metallic cations which are soluble in water or which form a water-soluble complex with ammonia.
Claim 5
Dependent Claim
22 words
The process of claim 1 wherein the pendant metallic carboxylate salt groups of the ethylene copolymer are alkali metal carboxylate salt groups.
References Cited (Backward Citations)
US3553178A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-12-05 | 1981-06-06 | 1981-12-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-12-05 | 1985-06-06 | 1985-12-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-12-05 | 1989-06-06 | 1989-12-06 | $7700.00 | Window Closed / Lapsed |