Process of forming a polypropylene coated substrate from an aqueous suspension of polypropylene particles
Assignee: BP Corp North America Inc
•
Filing: 1976-06-25
•
Granted: 1977-12-06
•
Expires: 1996-06-25
Abstract
Abstract Aqueous coating composition comprising a dispersion of a resinous addition polymer of an alpha, beta-ethylenically unsaturated carboxylic acid compound and suspended particles of a resinous polymer of propylene. Coating methods and coated articles are also disclosed.
Inventors
- 👤 Wassily Poppe
- 👤 Ivor R. Fielding
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 03:14
CPC Classifications
C; C09; C09D; C09D133/00; C09D133/02; C09D123/00; C09D123/02; C09D123/04; C09D123/08; C09D123/0846; C09D123/0869; C09D123/10; C09D123/12; C09D133/04; C09D133/06; C09D133/062; C09D133/064; C08; C08L; C08L2205/00; C08L2205/03; C08L2205/14; C08L2205/18; C08L23/00; C08L23/02; C08L23/10; C08L23/12; C08L33/00; C08L33/04; C08L33/06; C08L33/10; C08L77/00; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31855; Y10T428/31935; Y10T428/31938
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
175 words
The method of forming a coated substrate, which comprises depositing an aqueous coating composition comprising a dispersion of a resinous polymer of an alpha, beta-ethylenically unsaturated carboxylic acid compound and suspended particles of a resinous polymer of propylene to a substrate and fusing the resinous polymer of propylene at a temperature of from about 190° to 250° C. until the resinous polymer of propylene coalesces, wherein said resinous addition polymer of an alpha, beta-ethylenically unsaturated carboxylic acid compound comprises at least one member selected from the group consisting of alpha, beta-ethylenically unsaturated carboxylic acid and alpha, beta-ethylenically unsaturated carboxylic ester, and is present in a concentration of from about 5 to 200 parts by weight per each 100 parts by weight resinous polymer of propylene, said resinous polymer of propylene contains at least 75% by weight propylene, said particles have a maximum average particle diameter size of 500 microns, and the polymeric components of said coating composition comprise from 10 to 75 parts by weight per each 100 parts by weight of the coating composition.
Claim 2
Independent Claim
175 words
The method of forming a coated substrate, which comprises depositing an aqueous coating composition comprising a dispersion of a resinous polymer of an alpha, beta-ethylenically unsaturated carboxylic acid compound and suspended particles of a resinous polymer of propylene to a substrate and fusing the resinous polymer of propylene at a temperature of from about 190° to 250° C. until the resinous polymer of propylene coalesces, wherein said resinous addition polymer of an alpha, beta-ethylenically unsaturated carboxylic acid compound comprises at least one member selected from the group consisting of alpha, beta-ethylenically unsaturated carboxylic acid and alpha, beta-ethylenically unsaturated carboxylic ester, and is present in a concentration of from about 5 to 200 parts by weight per each 100 parts by weight resinous polymer of propylene, said resinous polymer of propylene contains at least 75% by weight propylene, said particles have a maximum average particle diameter size of 500 microns, and the polymeric components of said coating composition comprise from 10 to 75 parts by weight per each 100 parts by weight of the coating composition.
Claim 3
Dependent Claim
31 words
The process of claim 1, wherein said resinous polymer of an alpha, beta-ethylenically unsaturated carboxylic acid compound comprises from 0.5 to 50% by weight of an alpha, beta-ethylemically unsaturated carboxylic acid.
Claim 4
Dependent Claim
34 words
The process of claim 2, wherein said alpha, beta-ethylenically unsaturated carboxylic acid comprises at least 5 weight percent of at least one acid selected from the group consisting of acrylic acid and methacrylic acid.
Claim 5
Dependent Claim
34 words
The process of claim 2 wherein said resinous polymer of an alpha, beta-ethylenically unsaturated carboxylic acid compound comprises from 25 to 99.5 weight percent soft alkyl ester of an alpha, beta-ethylenically unsaturated carboxylic acid.
Claim 6
Dependent Claim
25 words
The process of claim 2 wherein said resinous polymer of an alpha, beta-ethylenically unsaturated carboxylic acid compound comprises from 25 to 99.5 weight percent ethylene.
Claim 7
Dependent Claim
28 words
The process of claim 2 wherein said composition additionally contains up to 50 parts by weight per 100 parts by weight resinous polymer of propylene of a polycarbonamide.
Claim 8
Dependent Claim
21 words
The process of claim 1, wherein said composition is pigment free and said temperature is from about 190° to 230° C.
Claim 9
Dependent Claim
9 words
The article produced by the process of claim 1.
Claim 10
Dependent Claim
31 words
The article of claim 8, wherein said resinous polymer of an alpha, beta-ethylenically unsaturated carboxylic acid compound comprises from 0.5 to 50% by weight of an alpha, beta-ethylenically unsaturated carboxylic acid.
Claim 11
Dependent Claim
34 words
The article of claim 9, wherein said alpha, beta-ethylenically unsaturated carboxylic acid comprises at least 5 weight percent of at least one acid selected from the group consisting of acrylic acid and methacrylic acid.
Claim 12
Dependent Claim
34 words
The article of claim 9, wherein said resinous polymer of an alpha, beta-ethylenically unsaturated carboxylic acid compound comprises from 25 to 99.5 weight percent soft alkyl ester of an alpha, beta-ethylenically unsaturated carboxylic acid.
Claim 13
Dependent Claim
25 words
The article of claim 9, wherein said resinous polymer of an alpha, beta-ethylenically unsaturated carboxylic acid compound comprises from 25 to 99.5 weight percent ethylene.
Claim 14
Dependent Claim
28 words
The article of claim 9 wherein said film additionally contains up to 50 parts by weight per 100 parts by weight resinous polymer of propylene of a polycarbonamide.
References Cited (Backward Citations)
US2302332A
Cited
US2844489A
Cited
US3264272A
Cited
US3283036A
Cited
US3356627A
Cited
US3968280A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-12-05 | 1981-06-06 | 1981-12-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-12-05 | 1985-06-06 | 1985-12-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-12-05 | 1989-06-06 | 1989-12-06 | $7700.00 | Window Closed / Lapsed |