Expired / Lapsed
US
⏱️ 0.0 years remaining
Selective solar energy receiver and method for its production
Assignee: PPG Industries Inc
•
Filing: 1975-12-23
•
Granted: 1977-12-06
•
Expires: 1995-12-23
Abstract
Abstract A solar energy receiver comprising an aluminum panel and a coating which comprises a black metal sulfide film having a high solar absorptance but a low thermal emissivity and a method for the production of such a receiver by wet chemical deposition onto an aluminum panel of a metal sulfide film from an alkaline aqueous solution of a salt of a metal, a complexing agent for the metal ions, and a sulfur compound capable of reacting with the metal ions in the presence of aluminum to form a metal sulfide are disclosed.
Inventors
- 👤 Charles B. Greenberg
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 15:44
CPC Classifications
F; F24; F24S; F24S70/00; F24S70/20; F24S70/25; F24S70/225; Y; Y02; Y02E; Y02E10/00; Y02E10/40; Y10; Y10S; Y10S126/00; Y10S126/907; Y10S126/908
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
92 words
A method for producing a solar energy receiving surface comprising the steps of: a. cleaning a surface of an aluminum substrate; and b. contacting the surface of the substrate with an alkaline coating solution consisting essentially of: a water soluble salt of a metal selected from the group consisting of nickel, zinc, silver, cadmium, copper cobalt, lead, tin, iron, and combinations thereof; a complexing agent for the selected metal; a sulfur compound capable of reacting with the selected metal to form a sulfide; and water to form a uniform metal sulfide coating.
Claim 2
Independent Claim
92 words
A method for producing a solar energy receiving surface comprising the steps of: a. cleaning a surface of an aluminum substrate; and b. contacting the surface of the substrate with an alkaline coating solution consisting essentially of: a water soluble salt of a metal selected from the group consisting of nickel, zinc, silver, cadmium, copper cobalt, lead, tin, iron, and combinations thereof; a complexing agent for the selected metal; a sulfur compound capable of reacting with the selected metal to form a sulfide; and water to form a uniform metal sulfide coating.
Claim 3
Dependent Claim
13 words
The method according to claim 1, wherein the sulfur compound is sodium thiosulfate.
Claim 4
Dependent Claim
13 words
The method according to claim 2, wherein the complexing agent is ammonium hydroxide.
Claim 5
Dependent Claim
18 words
The method according to claim 3, wherein the water soluble salt is selected to include a nickel salt.
Claim 6
Dependent Claim
67 words
The method according to claim 1, wherein the solution comprises: a. 1 to 10 grams per liter of water of a metal salt selected from the group consisting of the sulfates and nitrates of nickel, silver, zinc and mixtures thereof; b. 10 to 150 cc per liter of water of ammonium hydroxide; c. 1 to 15 grams per liter of water of sodium thiosulfate; and d. water.
Claim 7
Dependent Claim
34 words
The method according to claim 5, wherein the metal salt is nickel sulfate and the solution further comprises a second complexing agent selected from the group consisting of alkali metal tartrates, oxalates and gluconates.
Claim 8
Dependent Claim
15 words
The method according to claim 6, wherein the second complexing agent is sodium potassium tartrate.
Claim 9
Dependent Claim
31 words
The method according to claim 7, wherein the substrate is contacted with the solution at a temperature between 50° F. and 130° F. for a period between 1 and 30 minutes.
Claim 10
Dependent Claim
12 words
An article of manufacture produced according to the method of claim 5.
Claim 11
Dependent Claim
12 words
An article of manufacture produced according to the method of claim 8.
Claim 12
Dependent Claim
38 words
An article of manufacture produced according to the method of claim 8, wherein the solar absorptance of a surface of the article is greater than 0.95 while the thermal emissivity of the same surface is less than 0.45.
Claim 13
Dependent Claim
71 words
A coating composition for the wet chemical deposition of metal sulfide films in the presence of aluminum which consists essentially of: a. 1 to 10 grams per liter of a metal salt selected from the group consisting of nickel sulfate, silver nitrate, zinc nitrate, and combinations thereof; b. 10 to 150 cubic centimeters per liter of ammonium hydroxide; c. 1 to 15 grams per liter of sodium thiosulfate; and d. water.
Claim 14
Dependent Claim
71 words
A coating composition for the wet chemical deposition of metal sulfide films in the presence of aluminum which consists essentially of: a. 1 to 10 grams per liter of a metal salt selected from the group consisting of nickel sulfate, silver nitrate, zinc nitrate, and combinations thereof; b. 10 to 150 cubic centimeters per liter of ammonium hydroxide; c. 1 to 15 grams per liter of sodium thiosulfate; and d. water.
Claim 15
Dependent Claim
30 words
The composition as recited in claim 12, wherein the metal salt is nickel sulfate and wherein the composition further comprises 2 to 30 grams per liter of sodium potassium tartrate.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-12-05 | 1981-06-06 | 1981-12-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-12-05 | 1985-06-06 | 1985-12-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-12-05 | 1989-06-06 | 1989-12-06 | $7700.00 | Window Closed / Lapsed |