Assignee: RCA Licensing Corp
•
Filing: 1977-02-28
•
Granted: 1977-12-06
•
Expires: 1997-02-28
Abstract
Abstract The method comprises applying to a surface to be etched a coating of a liquid composition comprising an acid-precipitated casein, alkali dichromate photosensitizer, sodium borate and water. The layer is dried, photoexposed, developed and baked to produce an etch-resistant stencil.
Inventors
- 👤 Abraham Goldman
- 👤 Pabitra Datta
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 08:44
CPC Classifications
G; G03; G03F; G03F7/00; G03F7/004; G03F7/04; C; C23; C23F; C23F1/00; C23F1/02; H; H01; H01J; H01J9/00; H01J9/02; H01J9/14; H01J9/142; H01J9/144
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
90 words
A method for producing an etch-resistant stencil upon a surface comprising applying to said surface a coating of a liquid composition comprising i. acid precipitated casein, as the sole sensitizable protein material in said liquid composition, ii. alkali dichromate photosensitizer for said casein, iii. sodium borate, as the sole alkalizing agent in said liquid composition, iv. and water, drying said coating, photoexposing said dry coating to a light image, developing said exposed coating to produce said stencil, and then baking said stencil in air to render said stencil etch resistant.
Claim 2
Independent Claim
90 words
A method for producing an etch-resistant stencil upon a surface comprising applying to said surface a coating of a liquid composition comprising i. acid precipitated casein, as the sole sensitizable protein material in said liquid composition, ii. alkali dichromate photosensitizer for said casein, iii. sodium borate, as the sole alkalizing agent in said liquid composition, iv. and water, drying said coating, photoexposing said dry coating to a light image, developing said exposed coating to produce said stencil, and then baking said stencil in air to render said stencil etch resistant.
Claim 3
Dependent Claim
29 words
The method defined in claim 1 wherein said sodium borate being present in such proportions as to produce a pH of about 6.7 to 7.3 in said liquid composition.
Claim 4
Dependent Claim
21 words
The method defined in claim 1 wherein said sodium borate comprises about 0.05 to 0.20 of the weight of said casein.
Claim 5
Dependent Claim
13 words
The method defined in claim 1 wherein said casein is lactic-acid precipitated casein.
Claim 6
Dependent Claim
14 words
The method defined in claim 1 wherein said casein is hydrochloric acid precipitated casein.
Claim 7
Dependent Claim
153 words
In a method for producing an apertured mask for a cathode-ray tube, the steps comprising a. applying to each major surface of a metal sheet a coating of a liquid, water-based coating composition having a pH of about 6.7 to 7.3 and consisting essentially of i. acid-precipitated casein as the sole photosensitizable protein material present, ii. alkali dichromate photosensitizer for said casein, iii. anhydrous sodium borate, as the sole alkalizing agent in said coating composition, said sodium borate comprising about 0.05 to 0.20 of the weight of said casein, iv. and water, b. drying said coatings, c. exposing said dry coatings to light images, d. developing said exposed coatings to produce stencils on each of said major surfaces, e. baking said stencils in air to render said stencils etch resistant, f. and then applying an etchant for said metal sheet to both of said surfaces until said sheet is etched a desired amount.
Claim 8
Dependent Claim
153 words
In a method for producing an apertured mask for a cathode-ray tube, the steps comprising a. applying to each major surface of a metal sheet a coating of a liquid, water-based coating composition having a pH of about 6.7 to 7.3 and consisting essentially of i. acid-precipitated casein as the sole photosensitizable protein material present, ii. alkali dichromate photosensitizer for said casein, iii. anhydrous sodium borate, as the sole alkalizing agent in said coating composition, said sodium borate comprising about 0.05 to 0.20 of the weight of said casein, iv. and water, b. drying said coatings, c. exposing said dry coatings to light images, d. developing said exposed coatings to produce stencils on each of said major surfaces, e. baking said stencils in air to render said stencils etch resistant, f. and then applying an etchant for said metal sheet to both of said surfaces until said sheet is etched a desired amount.
Claim 9
Dependent Claim
19 words
The method defined in claim 6 wherein said photosensitizer comprises 0.05 to 0.30 of the weight of said casein.
Claim 10
Dependent Claim
19 words
The method defined in claim 6 wherein said stencil is baked in air at about 260° to 350° C.
Claim 11
Dependent Claim
19 words
The method defined in claim 6 wherein said sheet is of cold-rolled steel and said etchant includes ferric chloride.
Claim 12
Dependent Claim
21 words
The method defined in claim 6 wherein said sodium borate comprises about 0.10 to 0.18 of the weight of said casein.
References Cited (Backward Citations)
US3011890A
Cited
US3929532A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-12-05 | 1981-06-06 | 1981-12-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-12-05 | 1985-06-06 | 1985-12-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-12-05 | 1989-06-06 | 1989-12-06 | $7700.00 | Window Closed / Lapsed |