Biaxially oriented polyethylene terephthalate film and method of making such film
Assignee: EIDP Inc
•
Filing: 1975-10-20
•
Granted: 1977-11-22
•
Expires: 1995-10-20
Abstract
Abstract A biaxially oriented polyethylene terephthalate film suitable for making heat-shrinkable bands is provided having machine direction shrinkage, on heating to 100° C. for 5 seconds, of less than 8%; cross-machine direction shrinkage, on heating to 100° C. for 5 seconds, of greater than 40%; and a minimum shrink force at 100° C. of greater than 200 psi. The film further, and variously, has substantially 0% crystallinity; substantially 0% shrinkage at 78° C.; a maximum gauge deviation of less than 15%; an elongation at break of at least 25% and a tensile strength of at least 6000 psi; haze of less than 8%; and a modulus of at least 200,000 psi. A method of making such film is provided in which the film is heated, after machine direction stretching and prior to cross-machine direction stretching, to an intermediate temperature (from 100° to 105°) slightly above the temperature at which it is first stretched, to essentially remove machine direction shrinkage.
Inventors
- 👤 William James Pangonis
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 11:37
CPC Classifications
B; B29; B29C; B29C55/00; B29C55/02; B29C55/10; B29C55/12; B29C55/14; B29C55/143; B29C71/00; B29K; B29K2067/00; B29K2995/00; B29K2995/0037; B29K2995/0049
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
149 words
A method of making biaxially oriented polyethylene terephthalate film including the steps of: stretching amorphous polyethylene terephthalate film in a first direction about 1.2 to 2 times its initial length at a first temperature slightly above the glass transition temperature of the film to provide molecular orientation in that direction; heating the thus oriented film to a temperature slightly higher than such first temperature for a time sufficient to partially remove such orientation while maintaining the film in a substantially amorphous state; and thereafter, cooling the film to a temperature substantially the same as the first temperature and stretching the film in a direction transverse to the first direction about 3 to 4 times its width before stretching whereby such film has a shrinkage, on heating to 100° C for 5 seconds, of less than 8% in the first direction and greater than 40% transverse to the first direction.
Claim 2
Independent Claim
149 words
A method of making biaxially oriented polyethylene terephthalate film including the steps of: stretching amorphous polyethylene terephthalate film in a first direction about 1.2 to 2 times its initial length at a first temperature slightly above the glass transition temperature of the film to provide molecular orientation in that direction; heating the thus oriented film to a temperature slightly higher than such first temperature for a time sufficient to partially remove such orientation while maintaining the film in a substantially amorphous state; and thereafter, cooling the film to a temperature substantially the same as the first temperature and stretching the film in a direction transverse to the first direction about 3 to 4 times its width before stretching whereby such film has a shrinkage, on heating to 100° C for 5 seconds, of less than 8% in the first direction and greater than 40% transverse to the first direction.
Claim 3
Independent Claim
170 words
A method of making biaxially oriented polyethylene terephthalate film including the steps of: stretching amorphous polyethylene terephthalate film heated to a temperature slightly above its glass temperature in a first direction about 1.2 to 2 times its initial length to orient it uniaxially; heating such uniaxially oriented film to a stabilizing temperature from about 100° to 105° C in a tenter frame without stretching after it has been stretched in the first direction and before it is stretched in a second direction; thereafter, cooling the film to a temperature substantially the same as the first temperature; stretching the film in the second direction in the tenter frame about 3 to 4 times its width before stretching to orient it in that direction; and cooling the film below its stretching temperature after stretching in the second direction in the tenter frame whereby such film has a shrinkage, on heating to 100° C for 5 seconds, of less than 8% in the first direction and greater than 40% in the second direction.
Claim 4
Independent Claim
170 words
A method of making biaxially oriented polyethylene terephthalate film including the steps of: stretching amorphous polyethylene terephthalate film heated to a temperature slightly above its glass temperature in a first direction about 1.2 to 2 times its initial length to orient it uniaxially; heating such uniaxially oriented film to a stabilizing temperature from about 100° to 105° C in a tenter frame without stretching after it has been stretched in the first direction and before it is stretched in a second direction; thereafter, cooling the film to a temperature substantially the same as the first temperature; stretching the film in the second direction in the tenter frame about 3 to 4 times its width before stretching to orient it in that direction; and cooling the film below its stretching temperature after stretching in the second direction in the tenter frame whereby such film has a shrinkage, on heating to 100° C for 5 seconds, of less than 8% in the first direction and greater than 40% in the second direction.
Claim 5
Independent Claim
124 words
A method of making biaxially oriented polyethylene terephthalate film including the steps of: stretching amorphous polyethylene terephthalate film in the machine direction (MD) at a temperature and rate whereby such film has a MD shrinkage, on heating to 100° C. for 5 seconds, of between 30% to 50%; thereafter subjecting the thus stretched film to a temperature higher than the MD stretching temperature while the film is under restraint whereby such film has an MD shrinkage, on heating to 100° C. for 5 seconds, of less than 8%; and thereafter stretching the thus heated film in the cross-machine direction (TD) at a temperature and rate whereby such film has a TD shrinkage, on heating to 100° C. for 5 seconds, of greater than 40%.
Claim 6
Independent Claim
124 words
A method of making biaxially oriented polyethylene terephthalate film including the steps of: stretching amorphous polyethylene terephthalate film in the machine direction (MD) at a temperature and rate whereby such film has a MD shrinkage, on heating to 100° C. for 5 seconds, of between 30% to 50%; thereafter subjecting the thus stretched film to a temperature higher than the MD stretching temperature while the film is under restraint whereby such film has an MD shrinkage, on heating to 100° C. for 5 seconds, of less than 8%; and thereafter stretching the thus heated film in the cross-machine direction (TD) at a temperature and rate whereby such film has a TD shrinkage, on heating to 100° C. for 5 seconds, of greater than 40%.
Claim 7
Independent Claim
129 words
A method of making heat-shrinkable, heat-sealable polyethylene terephthalate film including the steps of: stretching amorphous polyethylene terephthalate film in a machine direction about 1.2 to 2 times its initial length at a temperature from slightly above its glass transition temperature to 25° C. above such glass transition temperature; heating such stretched film to an intermediate temperature higher than the temperature of the MD stretching temperature while restraining the film from the shrinkage by engaging it along its edges whereby to relax the stretched film; stretching such relaxed film in a cross-machine direction while heating it to a temperature lower than the intermediate temperature and stretching it to about 3 to 4 times its width before stretching; and cooling the film rapidly to a temperature below its glass transition temperature.
Claim 8
Independent Claim
129 words
A method of making heat-shrinkable, heat-sealable polyethylene terephthalate film including the steps of: stretching amorphous polyethylene terephthalate film in a machine direction about 1.2 to 2 times its initial length at a temperature from slightly above its glass transition temperature to 25° C. above such glass transition temperature; heating such stretched film to an intermediate temperature higher than the temperature of the MD stretching temperature while restraining the film from the shrinkage by engaging it along its edges whereby to relax the stretched film; stretching such relaxed film in a cross-machine direction while heating it to a temperature lower than the intermediate temperature and stretching it to about 3 to 4 times its width before stretching; and cooling the film rapidly to a temperature below its glass transition temperature.
Claim 9
Independent Claim
128 words
A method of making heat-sealable, heat-shrinkable, biaxially oriented polyethylene terephthalate film including the steps of: stretching an amorphous polyethylene terephthalate film of a viscosity of at least 0.5 in the machine direction from 1.5 to 2.0 times its initial length at a temperature from between about 78° to 95° C.; engaging the thus stretched film in the clips of a tenter chain in a tenter frame; subjecting the film to a temperature of from 100° C. to 105° C. without stretching; thereafter stretching the film in a cross-machine direction in the tenter frame from 3.2 to 3.5 times its width after machine direction stretching at a temperature from between about 82° to 92° C.; and immediately cooling the then stretched film below 78° C. without stretching or relaxation.
Claim 10
Independent Claim
128 words
A method of making heat-sealable, heat-shrinkable, biaxially oriented polyethylene terephthalate film including the steps of: stretching an amorphous polyethylene terephthalate film of a viscosity of at least 0.5 in the machine direction from 1.5 to 2.0 times its initial length at a temperature from between about 78° to 95° C.; engaging the thus stretched film in the clips of a tenter chain in a tenter frame; subjecting the film to a temperature of from 100° C. to 105° C. without stretching; thereafter stretching the film in a cross-machine direction in the tenter frame from 3.2 to 3.5 times its width after machine direction stretching at a temperature from between about 82° to 92° C.; and immediately cooling the then stretched film below 78° C. without stretching or relaxation.
Claim 11
Independent Claim
158 words
A method of making biaxially oriented polyethylene terephthalate film including the steps of: casting polyethylene terephthalate film onto a quenching surface; forming amorphous polyethylene terephthalate film on such surface; stripping such amorphous polyethylene terephthalate film from such surface, such amorphous polyethylene terephthalate film having a viscosity of at least 0.55; stretching such amorphous film from 1.5 to 2 times its initial length while such film is at a temperature of between about 88° to 90° C.; engaging the thus stretched film in the clips of a tenter chain in a tenter frame; heating the film to a temperature of from about 100° C. to 105° C. for approximately 5 seconds without stretching while in the tenter frame; thereafter stretching the film transversely in the tenter frame from 3.2 to 3.5 times its width while such film is at a temperature of between about 88° and 90° C.; and cooling the film below 78° C. without stretching or relaxation.
Claim 12
Independent Claim
158 words
A method of making biaxially oriented polyethylene terephthalate film including the steps of: casting polyethylene terephthalate film onto a quenching surface; forming amorphous polyethylene terephthalate film on such surface; stripping such amorphous polyethylene terephthalate film from such surface, such amorphous polyethylene terephthalate film having a viscosity of at least 0.55; stretching such amorphous film from 1.5 to 2 times its initial length while such film is at a temperature of between about 88° to 90° C.; engaging the thus stretched film in the clips of a tenter chain in a tenter frame; heating the film to a temperature of from about 100° C. to 105° C. for approximately 5 seconds without stretching while in the tenter frame; thereafter stretching the film transversely in the tenter frame from 3.2 to 3.5 times its width while such film is at a temperature of between about 88° and 90° C.; and cooling the film below 78° C. without stretching or relaxation.
References Cited (Backward Citations)
US2784456A
Cited
US2928132A
Cited
US3187075A
Cited
US3631899A
Cited
US3547748A
Cited
US3702357A
Cited
US3873664A
Cited
US3903294A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-11-21 | 1981-05-23 | 1981-11-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-11-21 | 1985-05-23 | 1985-11-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-11-21 | 1989-05-23 | 1989-11-22 | $7700.00 | Window Closed / Lapsed |