US4059654A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Thermoplastic elastomer blend of EPDM, polyethylene, and a C3 -C16
Assignee: DSM Copolymer Inc
•
Filing: 1976-11-02
•
Granted: 1977-11-22
•
Expires: 1996-11-02
Abstract
Abstract A thermoplastic elastomer which is ideally suited for use in the fabrication of premium grade hose and other uses because of its smooth, soft and rubbery feel under widely varying temperature conditions, coupled with its exceptionally low compression set and good flexibility.
Inventors
- 👤 George A. Von Bodungen
- 👤 Curtis L. Meredith
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 06:58
CPC Classifications
C; C08; C08L; C08L23/00; C08L23/02; C08L23/16; C08K; C08K5/00; C08K5/04; C08K5/14; C08L23/04; C08L23/06; C08L23/10; C08L91/00; C08L2205/00; C08L2205/03; C08L2207/00; C08L2207/04; C08L2312/00; C08L2666/00; C08L2666/02; C08L2666/04
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
115 words
A thermoplastic elastomer formed of (1) an EPDM interpolymer of ethylene, a monoolefin containing from 3-16 carbon atoms, and a polyene, (2) a polymer of a monoolefin monomer containing 3-16 carbon atoms, and (3) polyethylene in which the polyethylene is present in an amount greater than 15% but not more than 25% by weight, with the remainder of 70% to less than 85% by weight divided between the EPDM interpolymer and the monoolefin polymer in the ratio of 90-10 parts by weight of EPDM polymers to 10-90 parts by weight of monoolefin polymers, said components in admixture being subjected to free radical reaction during hot working in the presence of a free radical generating catalyst.
Claim 2
Dependent Claim
115 words
A thermoplastic elastomer formed of (1) an EPDM interpolymer of ethylene, a monoolefin containing from 3-16 carbon atoms, and a polyene, (2) a polymer of a monoolefin monomer containing 3-16 carbon atoms, and (3) polyethylene in which the polyethylene is present in an amount greater than 15% but not more than 25% by weight, with the remainder of 70% to less than 85% by weight divided between the EPDM interpolymer and the monoolefin polymer in the ratio of 90-10 parts by weight of EPDM polymers to 10-90 parts by weight of monoolefin polymers, said components in admixture being subjected to free radical reaction during hot working in the presence of a free radical generating catalyst.
Claim 3
Dependent Claim
65 words
A thermoplastic elastomer as claimed in claim 1 in which the EPDM interpolymer is formed of monoolefins present in the ratio of 10-90 mole percent by weight ethylene to 90-10 mole percent by weight of a monoolefin containing 3-16 carbon atoms and in which the polyene is present in an amount to provide at least two carbon to carbon double bonds per 1000 carbon atoms.
Claim 4
Dependent Claim
18 words
A thermoplastic elastomer as claimed in claim 1 in which the monoolefin in the EPDM interpolymer is propylene,
Claim 5
Dependent Claim
15 words
A thermoplastic elastomer as claimed in claim 1 in which the monoolefin polymer is polypropylene.
Claim 6
Dependent Claim
16 words
A thermoplastic elastomer as claimed in claim 4 in which the polypropylene is an isotactic polypropylene.
Claim 7
Dependent Claim
31 words
A thermoplastic elastomer as claimed in claim 1 in which the monoolefin polymer is a copolymer of ethylene and propylene in which the bound ethylene is less than 10% by weight.
Claim 8
Dependent Claim
17 words
A thermoplastic elastomer as claimed in claim 1 in which the polyethylene is a high density polyethylene.
Claim 9
Dependent Claim
28 words
A thermoplastic elastomer as claimed in claim 1 in which the polyene is a polyunsaturated bridged ring hydrocarbon having at least one double bond in the bridged ring.
Claim 10
Dependent Claim
14 words
A thermoplastic elastomer as claimed in claim 8 in which the polyene is 5-alkylidene-2-norbornene.
Claim 11
Dependent Claim
14 words
A thermoplastic elastomer as claimed in claim 8 in which the polyene is 5-ethylidene-2-norbornene.
Claim 12
Dependent Claim
18 words
A thermoplastic elastomer as claimed in claim 1 in which the free radical generating catalyst is a peroxide.
Claim 13
Dependent Claim
29 words
A thermoplastic elastomer as claimed in claim 1 in which the free radical generating catalyst is present in an amount within the range of 0.25% to 4.0% by weight.
Claim 14
Dependent Claim
29 words
A thermoplastic elastomer as claimed in claim 1 in which the free radical generating catalyst is present in an amount within the range of 0.6% to 2.0% by weight.
Claim 15
Independent Claim
72 words
A method for preparing a thermoplastic elastomer comprising admixing an EPDM interpolymer, a polymer of a monoolefin having from 3-16 carbon atoms and polyethylene, in which the polyethylene is present in an amount greater than 15% but not in excess of 25% by weight of the polymer total, and hot working the mixture in the presence of a free radical generating catalyst to effect free radical reaction during the hot mixing step.
Claim 16
Independent Claim
72 words
A method for preparing a thermoplastic elastomer comprising admixing an EPDM interpolymer, a polymer of a monoolefin having from 3-16 carbon atoms and polyethylene, in which the polyethylene is present in an amount greater than 15% but not in excess of 25% by weight of the polymer total, and hot working the mixture in the presence of a free radical generating catalyst to effect free radical reaction during the hot mixing step.
Claim 17
Dependent Claim
31 words
The method as claimed in claim 14 in which the materials are hot worked together at a temperature and time corresponding to at least three times the half-life of the catalyst.
Claim 18
Dependent Claim
31 words
The method as claimed in claim 14 in which the materials are hot worked together at a temperature and time corresponding to five to six times the half-life of the catalyst.
Claim 19
Dependent Claim
21 words
The method as claimed in claim 14 in which the polymer of a monoolefin having from 3-16 carbon atoms is polypropylene.
Claim 20
Dependent Claim
34 words
The method as claimed in claim 14 in which the polymer of a monoolefin having from 3-16 carbon atoms is a copolymer of ethylene and propylene containing less than 10% by weight bound ethylene.
Claim 21
Dependent Claim
18 words
The method as claimed in claim 14 in which the free radical generating catalyst is a peroxide catalyst.
Claim 22
Dependent Claim
25 words
The method as claimed in claim 14 in which the catalyst is present in an amount within the range of 0.25% to 4.0% by weight.
Claim 23
Dependent Claim
25 words
The method as claimed in claim 14 in which the catalyst is present in an amount within the range of 0.6% to 2.0% by weight.
Claim 24
Dependent Claim
70 words
The method as claimed in claim 14 in which the EPDM is an interpolymer of ethylene, a monoolefin containing 3-16 carbon atoms, and a polyene in which the ethylene and monoolefin are present in the ratio of 10-90 mole percent ethylene to 90-10 mole percent monoolefin and in which the polyene is present in the amount to provide at least two carbon to carbon double bonds per 1000 carbon atoms.
Claim 25
Dependent Claim
34 words
The method as claimed in claim 22 in which the polyene is present in the interpolymer in an amount to provide from 2 to 25 carbon to carbon double bonds per 1000 carbon atoms.
Claim 26
Dependent Claim
32 words
The method as claimed in claim 22 in which the polyene present in the EPDM interpolymer is a polyunsaturated bridged ring hydrocarbon having at least one double bond in the bridged ring.
Claim 27
Dependent Claim
13 words
The method as claimed in claim 24 in which the polyene is 5-ethylidene-2-norbornene.
Claim 28
Dependent Claim
37 words
The method as claimed in claim 14 which includes the admixture of an extender oil in an amount within the range of 0 to 100 parts by weight per 100 parts by weight of the polymeric material.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-11-21 | 1981-05-23 | 1981-11-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-11-21 | 1985-05-23 | 1985-11-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-11-21 | 1989-05-23 | 1989-11-22 | $7700.00 | Window Closed / Lapsed |