Method for making a porous tantalum pellet
Assignee: Vishay Sprague Inc
•
Filing: 1976-08-09
•
Granted: 1977-11-22
•
Expires: 1996-08-09
Abstract
Abstract A quantity of tantalum powder is heated to a temperature greater than 400 DEG C in a non-oxidizing atmosphere to dissolve the tantalum oxide film existing on the surfaces of the tantalum particles. The treated powder without conventional organic binders is compressed to form a unitary pellet in a mold maintained in an inert atmosphere. The pellet is subsequently heated in a vacuum to sinter the particles together and to provide a porous tantalum pellet having carbon-free tantalum surfaces and a large exposed surface area per unit weight of tantalum. Electrolytic capacitors made from these pellets exhibit a larger CV product per unit weight of tantalum and/or a lower leakage current than for comparable capacitors known heretofore.
Inventors
- 👤 Walter J. Bernard
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 19:57
CPC Classifications
H; H01; H01G; H01G9/00; H01G9/004; H01G9/04; H01G9/048; H01G9/052; B; B22; B22F; B22F3/00; B22F3/10; B22F3/11; B22F3/02; B22F2003/026; B22F2998/00; B22F2998/10; B22F2999/00
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
103 words
A method for making a porous tantalum pellet comprising the sequential steps of: a. heating a quantity of tantalum powder particles having a surface oxide to a temperature greater than 400° C and no greater than 1200° C in a non-oxidizing atmosphere to dissolve said surface oxide into the bulk of said particles; b. dispensing said powder into a molding press cavity; c. providing a protective atmosphere for said powder from said heating through said dispensing; d. compressing said powder in said cavity to provide a porous tantalum pellet; and e. vacuum firing said pellet to sinter said compressed particles to each other.
Claim 2
Independent Claim
103 words
A method for making a porous tantalum pellet comprising the sequential steps of: a. heating a quantity of tantalum powder particles having a surface oxide to a temperature greater than 400° C and no greater than 1200° C in a non-oxidizing atmosphere to dissolve said surface oxide into the bulk of said particles; b. dispensing said powder into a molding press cavity; c. providing a protective atmosphere for said powder from said heating through said dispensing; d. compressing said powder in said cavity to provide a porous tantalum pellet; and e. vacuum firing said pellet to sinter said compressed particles to each other.
Claim 3
Dependent Claim
20 words
The method of claim 1 wherein said firing is accomplished at a temperature of between 1550° C and 1800° C.
Claim 4
Dependent Claim
28 words
The method of claim 1 wherein said heating is for about from 30 minutes to 2 hours and said heating temperature is from 1200° C to 700° C.
Claim 5
Dependent Claim
18 words
The method of claim 1 wherein said non-oxidizing atmosphere is a vacuum of less than 10 -4 torr.
Claim 6
Dependent Claim
20 words
The method of claim 1 wherein said non-oxidizing atmosphere is comprised of an inert gas selected from helium and argon.
Claim 7
Dependent Claim
17 words
The method of claim 1 wherein said non-oxidizing atmosphere contains less than 2×10 -5 torr of oxygen.
Claim 8
Dependent Claim
43 words
The method of claim 1 further comprising the step of directing a blast of non-oxidizing gas into said cavity prior to said dispensing, for the purpose of blowing away any particles of tantalum that may be adhering to the walls of said cavity.
Claim 9
Dependent Claim
24 words
The method of claim 1 further comprising the step of applying a lubricant to the walls of said press cavity prior to said compressing.
Claim 10
Dependent Claim
23 words
The method of claim 8 wherein said lubricant is an organic solvent having a boiling point of from 80° C to 110° C.
Claim 11
Dependent Claim
10 words
The method of claim 8 wherein said lubricant is trichloroethylene.
Claim 12
Dependent Claim
26 words
The method of claim 1 further comprising adjusting said pressing force until said pellet has a density of from 6.5 to 11 grams per cubic centimeter.
Claim 13
Dependent Claim
34 words
The method of claim 1 further comprising partially inserting a tantalum wire into said cavity prior to said compressing such that after said compressing, a portion of said wire is embedded in said pellet.
Claim 14
Dependent Claim
15 words
The method of claim 1 wherein said molding press cavity is a split cavity type.
Claim 15
Dependent Claim
26 words
The method of claim 1 wherein said providing a protective atmosphere is accomplished in part by flooding said powder with an inert gas during said dispensing.
Claim 16
Dependent Claim
18 words
The method of claim 14 wherein said inert gas is selected from helium, argon, nitrogen and carbon dioxide.
Claim 17
Dependent Claim
13 words
The method of claim 1 wherein said particles are cold-welded during said compressing.
Claim 18
Dependent Claim
29 words
The method of claim 1 wherein said providing a protective atmosphere is accomplished in part by surrounding said powder with an inert gas from said heating to said dispensing.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-11-21 | 1981-05-23 | 1981-11-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-11-21 | 1985-05-23 | 1985-11-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-11-21 | 1989-05-23 | 1989-11-22 | $7700.00 | Window Closed / Lapsed |