Abstract
Abstract A process for the preparation of expansible beads which are convertible by firing into cellular glass bodies, such process comprising the steps of preparing a slip having a liquid medium continuous phase and a disperse phase, the slip containing particles of glass or glass-forming material, a cellulating agent, and a binder, the disperse phase of the slip including at least most of the particles, dividing the slip into drops, and subjecting the drops while in divided condition to a heat treatment including heating and cooling stages so as to cause evaporation of liquid from the drops and conversion thereof into self-sustaining beads in which the glass or glass-forming particles are held together by the binder and which contain the cellulating agent or gas derived therefrom.
Inventors
- 👤 Daniel De Vos
- 👤 Paul-Marie Michel
- 👤 Alfred Berger
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 19:35
CPC Classifications
C; C03; C03B; C03B19/00; C03B19/10; C03B19/108; C03B19/1085
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
142 words
A process for the preparation of expansible beads which are convertible by firing into cellular glass bodies, said process comprising the steps of: preparing a slip having a liquid medium continuous phase and a disperse phase, said slip containing particles of glass or glass-forming material, a cellulating agent, and a binder, the disperse phase of said slip including at least most of said particles, dividing said slip into drops, said slip which is divided into drops having a viscosity in the range 200 to 10,000 cp, and subjecting said drops while in divided condition to a heat treatment including heating and cooling stages so as to cause evaporation of liquid from said drops and conversion thereof into self-sustaining beads in which said glass or glass-forming particles are held together by said binder and which contain said cellulating agent or gas derived therefrom.
Claim 2
Dependent Claim
142 words
A process for the preparation of expansible beads which are convertible by firing into cellular glass bodies, said process comprising the steps of: preparing a slip having a liquid medium continuous phase and a disperse phase, said slip containing particles of glass or glass-forming material, a cellulating agent, and a binder, the disperse phase of said slip including at least most of said particles, dividing said slip into drops, said slip which is divided into drops having a viscosity in the range 200 to 10,000 cp, and subjecting said drops while in divided condition to a heat treatment including heating and cooling stages so as to cause evaporation of liquid from said drops and conversion thereof into self-sustaining beads in which said glass or glass-forming particles are held together by said binder and which contain said cellulating agent or gas derived therefrom.
Claim 3
Dependent Claim
24 words
A process according to claim 1, wherein the drops into which said slip is divided are in the size range 100 to 3000 microns.
Claim 4
Dependent Claim
12 words
A process according to claim 1, wherein the liquid medium includes water.
Claim 5
Dependent Claim
28 words
A process according to claim 3, wherein the water is present in a proportion of less than 50% by weight based on the total weight of said slip.
Claim 6
Dependent Claim
18 words
A process according to claim 4, wherein the water proportion is in a range of 20 to 40%.
Claim 7
Dependent Claim
18 words
A process according to claim 1, wherein the division of said slip into drops is achieved by spraying.
Claim 8
Dependent Claim
31 words
A process according to claim 1, wherein said drops are projected into a furnace and are kept in separated condition, during the heating and cooling stages, by a gas stream therein.
Claim 9
Dependent Claim
19 words
A process according to claim 1, wherein the temperature in said heating stage is not more than 600° C.
Claim 10
Dependent Claim
15 words
A process according to claim 1, wherein said particles consist of particles of soda-lime glass.
Claim 11
Dependent Claim
25 words
A process according to claim 1, wherein the glass or glass-forming particles in said slip are in the size range of 10 to 250 microns.
Claim 12
Dependent Claim
22 words
A process according to claim 1, wherein said binder is dissolved in the liquid medium forming the continuous phase of said slip.
Claim 13
Dependent Claim
33 words
A process according to claim 1, wherein said binder is of a composition such that it can be chemically integrated with said particles by heating said self-sustaining beads to temperatures above glass-forming temperature.
Claim 14
Dependent Claim
12 words
A process according to claim 1, wherein said binder comprises sodium silicate.
Claim 15
Dependent Claim
27 words
A process according to claim 1, wherein said cellulating agent comprises a material which decomposes with evolution of gas during the heating stage of said heating treatment.
Claim 16
Dependent Claim
15 words
A process according to claim 1, wherein said cellulating agent comprises a carbonate or nitrate.
Claim 17
Dependent Claim
12 words
A process according to claim 1, wherein said cellulating agent comprises urea.
Claim 18
Dependent Claim
19 words
A process according to claim 1, wherein said cellulating agent forms at least a part of said liquid medium.
Claim 19
Dependent Claim
14 words
A process according to claim 1, wherein said cellulating agent comprises a combustible substance.
Claim 20
Dependent Claim
42 words
A process according to claim 18, wherein said combustible substance comprises a substance which burns only when the beads resulting from the process are subsequently heated to a temperature above that which is reached in the heating stage of said heating treatment.
Claim 21
Dependent Claim
31 words
A process according to claim 18, wherein said combustible substance is selected from the group consisting of carbon, fine coal, graphite, coke, lignite, shale containing combustible residue, tar, charcoal and wood.
Claim 22
Dependent Claim
44 words
A process of forming cellulated vitreous bodies, comprising the steps of forming expansible beads by a process according to claim 1 and then heating said beads sufficiently to cause softening and coalescence of the glass particles of formation of glass from the glass-forming particles.
Claim 23
Dependent Claim
24 words
A process according to claim 21, wherein said beads are kept in separated condition during the heating thereof and during a subsequent cooling stage.
Claim 24
Dependent Claim
28 words
A process according to claim 21, wherein said beads are kept in contact during the heating thereof so that the beads become united into a monolithic vitreous mass.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-11-21 | 1981-05-23 | 1981-11-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-11-21 | 1985-05-23 | 1985-11-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-11-21 | 1989-05-23 | 1989-11-22 | $7700.00 | Window Closed / Lapsed |