US4059142A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Continuous casting of a metallic product by electromagnetic centrifuging
Assignee: Institut de Recherches de la Siderurgie Francaise IRSID
•
Filing: 1977-01-18
•
Granted: 1977-11-22
•
Expires: 1997-01-18
Abstract
Abstract A metallic product is cast continuously by injecting a liquid metal into a cooled ingot mold, applying a magnetic field turning about the axis of the mold to rotate the metal, and extracting the partially solidified metal product from the mold. Effective stirring is obtained by rotating the magnetic field at a frequency of rotation of 4 to 15 Hertz and using a copper alloy of structural rigidity for the mold, the wall thickness of the mold being kept thin, preferably below 15 mm. The process is particularly useful for casting round metallic products and especially those which are subjected to after-treatments requiring good surface characteristics and a core free of faults.
Inventors
- 👤 Robert Alberny
- 👤 Jean Pierre Birat
- 👤 Roger Ventavoli
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 02:56
CPC Classifications
B; B22; B22D; B22D11/00; B22D11/10; B22D11/11; B22D11/114; B22D11/115
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
199 words
In a process of continuously casting a metallic product by electromagnetic centrifuging, wherein a liquid metal is injected into a cooled ingot mold having an axis, the metal is rotated by applying thereto a magnetic field turning about the axis of the mold, the magnetic field being produced by a polyphase inductor placed in the immediate proximity of the cast product, and the metal is extracted from the mold in partially solidified condition, the step of obtaining a maximal stirring intensity of the liquid metal in the mold by a. rotating the magnetic field at a frequency of rotation of 4 to 15 Hertz, b. using a copper alloy of structural rigidity for the mold wall, and c. keeping the thickness of the mold wall below a value calculated by the formula ##STR3## wherein e = the thickness of the wall; d = the diameter of the mold; α = linear expansion coefficient, λ = thermal conductivity in cal/cm/sec. ° C, e = young's modulus in kg/mm 2 , μ = Poisson's coefficient and Re= elastic limit in kg/mm 2 of the wall material; and Φ = thermal flux at the level of the meniscus in cal/cm 2 /sec.
Claim 2
Dependent Claim
199 words
In a process of continuously casting a metallic product by electromagnetic centrifuging, wherein a liquid metal is injected into a cooled ingot mold having an axis, the metal is rotated by applying thereto a magnetic field turning about the axis of the mold, the magnetic field being produced by a polyphase inductor placed in the immediate proximity of the cast product, and the metal is extracted from the mold in partially solidified condition, the step of obtaining a maximal stirring intensity of the liquid metal in the mold by a. rotating the magnetic field at a frequency of rotation of 4 to 15 Hertz, b. using a copper alloy of structural rigidity for the mold wall, and c. keeping the thickness of the mold wall below a value calculated by the formula ##STR3## wherein e = the thickness of the wall; d = the diameter of the mold; α = linear expansion coefficient, λ = thermal conductivity in cal/cm/sec. ° C, e = young's modulus in kg/mm 2 , μ = Poisson's coefficient and Re= elastic limit in kg/mm 2 of the wall material; and Φ = thermal flux at the level of the meniscus in cal/cm 2 /sec.
Claim 3
Dependent Claim
23 words
In the process of claim 1, the step of rotating the magnetic field at a frequency of rotation of 6 to 12 Hertz.
Claim 4
Dependent Claim
19 words
In the process of claim 1, the step of keeping the thickness of the mold wall below 15 mm.
Claim 5
Dependent Claim
21 words
In the process of claim 3, the step of keeping the thickness of the mold wall equal to about 8 mm.
Claim 6
Dependent Claim
24 words
In the process of claim 1, wherein the magnetic field is produced by a polyphase electromagnetic inductor with a pair of poles per phase.
Claim 7
Dependent Claim
20 words
In the process of claim 1, wherein the turning magnetic field has an effective intensity of at least 800 Gauss.
Claim 8
Dependent Claim
20 words
In the process of claim 6, wherein the turning magnetic field has an effective intensity of 1000 to 2000 G.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-11-21 | 1981-05-23 | 1981-11-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-11-21 | 1985-05-23 | 1985-11-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-11-21 | 1989-05-23 | 1989-11-22 | $7700.00 | Window Closed / Lapsed |