Refractory compositions

Claim 2

In a solid refractory composition comprising an inorganic refractory material and a substantially carbonized organic resin as a carbonaceous binder therefor, the improvement wherein the resin comprises a condensate resin of a phenol and an aldehyde chemically modified by reaction under heating with an extending agent selected from the group consisting of sulfite pulp lignin, kraft pulp lignin, molasses and mixtures thereof, the amount of lignin employed being about 5 to about 300 parts by weight per hundred parts by weight of the phenol, the amount of molasses employed being about 5 to about 500 parts by weight per hundred parts by weight of the phenol, and the amount of refractory material employed being about 0.5 to about 1,000 parts by weight per 100 parts by weight of extending agent.

Claim 3

The composition as claimed in claim 1 wherein the phenol-aldehyde resin is a novolac resin.

Claim 4

The composition as claimed in claim 2 wherein the extending agent is incorporated in the composition by reaction with the phenol, in the presence of a catalytic amount of an acid catalyst for said reaction, prior to condensation of the phenol with the aldehyde.

Claim 5

The composition as claimed in claim 2 wherein the extending agent is incorporated in the composition by reaction with the phenol-aldehyde condensate in the presence of a catalytic amount of an acid catalyst for said reaction.

Claim 6

The composition as claimed in claim 1 wherein the phenol-aldehyde condensate is a resol resin and the extending agent is incorporated in the composition by reaction with the phenol in the presence of a catalytic amount of an acid catalyst for said reaction prior to condensation of the phenol with the aldehyde.

Claim 7

The composition as claimed in claim 1 wherein the refractory material is selected from the group consisting of silica, clay, alumina, carbon, magnesia and dolomite, the aldehyde reactant is formaldehyde and the phenol reactant is selected from the group consisting of phenol and alkyl phenols having 1 to 4 carbon atoms in the alkyl substituent.

Claim 8

The composition of claim 6 wherein the phenol reactant is phenol and the extending agent is molasses.

Claim 9

The composition of claim 6 wherein the phenol reactant is phenol and the extending agent is a lignin selected from the group consisting of sulfite pulp lignin and kraft pulp lignin.

Claim 10

The process of producing a solid molded refractory composition comprising inorganic refractory material and a carbonaceous binder therefor which comprises the steps of 1) forming a mixture of a particulate inorganic refractory material and an organic resin in the presence of a volatile organic or inorganic liquid, wherein said refractory material is substantially insoluble, in an amount sufficient to provide a plastic mixture, said organic resin comprising the condensate resin of phenol and an aldehyde chemically modified by reaction under heating with an extending agent selected from the group consisting of sulfite pulp lignin, kraft pulp lignin, molasses and mixtures thereof, the amount of lignin employed being about 5 to about 300 parts by weight per hundred parts by weight of the phenol and the amount of molasses being about 5 to about 500 parts by weight per hundred parts by weight of the phenol, 2) molding the resultant plastic mixture to a desired shape, 3) removing said liquid from said mixture by evaporation to harden the resin, and 4) calcining said mixture at an elevated temperature under a non-oxidizing atmosphere to carbonize substantially all of said resin and obtain said refractory composition.

Claim 11

The process of producing a solid molded refractory composition comprising inorganic refractory material and a carbonaceous binder therefor which comprises the steps of 1) forming a mixture of a particulate inorganic refractory material and an organic resin in the presence of a volatile organic or inorganic liquid, wherein said refractory material is substantially insoluble, in an amount sufficient to provide a plastic mixture, said organic resin comprising the condensate resin of phenol and an aldehyde chemically modified by reaction under heating with an extending agent selected from the group consisting of sulfite pulp lignin, kraft pulp lignin, molasses and mixtures thereof, the amount of lignin employed being about 5 to about 300 parts by weight per hundred parts by weight of the phenol and the amount of molasses being about 5 to about 500 parts by weight per hundred parts by weight of the phenol, 2) molding the resultant plastic mixture to a desired shape, 3) removing said liquid from said mixture by evaporation to harden the resin, and 4) calcining said mixture at an elevated temperature under a non-oxidizing atmosphere to carbonize substantially all of said resin and obtain said refractory composition.

Claim 12

The process as claimed in claim 9 wherein the solid molded refractory composition product is calcined at about 400° to about 1200° Centigrade to carbonize the resin.

Claim 13

A solid molded refractory composition impregnated with a condensate resin of a phenol and an aldehyde chemically modified by reaction under heating with an extending agent selected from the group consisting of sulfite pulp lignin, kraft pulp lignin, molasses and mixtures thereof, the amount of lignin employed being about 5 to about 300 parts by weight per hundred parts by weight of the phenol and the amount of molasses employed being about 5 to about 500 parts by weight per hundred parts by weight of the phenol.

Claim 14

A solid molded refractory composition impregnated with a condensate resin of a phenol and an aldehyde chemically modified by reaction under heating with an extending agent selected from the group consisting of sulfite pulp lignin, kraft pulp lignin, molasses and mixtures thereof, the amount of lignin employed being about 5 to about 300 parts by weight per hundred parts by weight of the phenol and the amount of molasses employed being about 5 to about 500 parts by weight per hundred parts by weight of the phenol.