Abstract
Abstract A process for the continuous manufacture of linear, high molecular weight, polybutylene terephthalates, in which dimethyl terephthalate is trans-esterified with 1,4-butanediol, if desired in the presence of up to 40 mole% of other starting materials which form linear polyesters, in the molar ratio of from 1:1.2 to 1:1.5, in a plurality of successive stages at temperatures rising from 160° to 230° C, the mixture thus obtained is passed, at from 230° to 270° C and from 2 mm Hg to 20 mm Hg, upward through a bundle of stationary heated tubes, and immediately thereafter through a hold tank, with the proviso that the volume of the hold tank is at least 1/4 and at most 2.5 times the volume of the tube bundle and the mean residence time in the tube bundle and hold tank together is from 10 to 60 minutes, and the precondensate thus obtained is polycondensed at from 240° to 260° C and from 0.1 to 2 mm Hg. with continuous formation of thin films. The polybutylene terephthalates manufactured by the above process may be used for the manufacture of products such as fibers, films, sheeting and injection moldings.
Inventors
- 👤 Hugo Strehler
- 👤 Ludwig Beer
- 👤 Eduard Heil
- 👤 Friedrich Urbanek
- 👤 Hermann Fischer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 15:26
CPC Classifications
C; C08; C08G; C08G63/00; C08G63/78; C08G63/82; C08G63/85
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
243 words
A process for the continuous manufacture of linear, high molecular weight polybutylene terephthalates, wherein a. dimethyl terephthalate is reacted with 1,4-butanediol, if desired in the presence of up to 40 mole% of further starting materials which form linear polyesters, in the molar ratio of from 1:1.2 to 1:1.5 in a plurality of successive stages at temperatures rising from 160° to 230° C in the presence of trans-esterification catalysts, and methanol is distilled off continuously. b. the resulting mixture of dihydroxybutyl terephthalate and its oligomers is subsequently passed, at from 230° to 270° C and from 20 to 2 mm Hg, upward through a bundle of stationary heated tubes, and the resulting mixture of vapor and liquid is passed through a hold tank located immediately above the tube ends, the volume of the hold tank being at least 1/4 and at most 2.5 times the volume of the tube bundle and the mean residence time in the tube bundle and hold tank together being from 10 to 60 minutes, most of the amount of heat required to heat the reaction mixture and vaporize the volatile constituents of the reaction mixture being supplied to the reaction mixture in the tubes, and the mixing of the reaction mixture being effected predominantly by the vapor bubbles rising from the tubes, and c. the precondensate thus obtained is polycondensed at from 240° to 260° C and from 0.1 to 2 mm Hg, with continuous formation of thin films.
Claim 2
Dependent Claim
243 words
A process for the continuous manufacture of linear, high molecular weight polybutylene terephthalates, wherein a. dimethyl terephthalate is reacted with 1,4-butanediol, if desired in the presence of up to 40 mole% of further starting materials which form linear polyesters, in the molar ratio of from 1:1.2 to 1:1.5 in a plurality of successive stages at temperatures rising from 160° to 230° C in the presence of trans-esterification catalysts, and methanol is distilled off continuously. b. the resulting mixture of dihydroxybutyl terephthalate and its oligomers is subsequently passed, at from 230° to 270° C and from 20 to 2 mm Hg, upward through a bundle of stationary heated tubes, and the resulting mixture of vapor and liquid is passed through a hold tank located immediately above the tube ends, the volume of the hold tank being at least 1/4 and at most 2.5 times the volume of the tube bundle and the mean residence time in the tube bundle and hold tank together being from 10 to 60 minutes, most of the amount of heat required to heat the reaction mixture and vaporize the volatile constituents of the reaction mixture being supplied to the reaction mixture in the tubes, and the mixing of the reaction mixture being effected predominantly by the vapor bubbles rising from the tubes, and c. the precondensate thus obtained is polycondensed at from 240° to 260° C and from 0.1 to 2 mm Hg, with continuous formation of thin films.
Claim 3
Dependent Claim
22 words
A process as claimed in claim 1, wherein from 0.02 to 0.3% by weight of catalyst, based on dimethyl terephthalate, is used.
Claim 4
Dependent Claim
15 words
A process as claimed in claim 1, wherein titanic acid esters are used as catalysts.
Claim 5
Dependent Claim
21 words
A process as claimed in claim 1, wherein the precondensation stage b) is carried out at from 240° to 260° C.
Claim 6
Dependent Claim
22 words
A process as claimed in claim 1, wherein the precondensation stage b) is carried out at from 2 to 10 mm Hg.
Claim 7
Dependent Claim
22 words
A process as claimed in claim 1, wherein the residence time in the precondensation stage b) is from 10 to 25 minutes.
Claim 8
Dependent Claim
21 words
A process as claimed in claim 1, wherein the polycondensation stage c) is carried out at from 245° to 250° C.
Claim 9
Dependent Claim
22 words
A process as set forth in claim 1, wherein the residence time in precondensation stage c) is from 1 to 3 hours.
Claim 10
Dependent Claim
25 words
A process as set forth in claim 1, wherein the polybutylene terephthalate obtained from stage c) has a relative viscosity of from 1.3 to 1.9.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-10-31 | 1981-05-02 | 1981-11-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-10-31 | 1985-05-02 | 1985-11-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-10-31 | 1989-05-02 | 1989-11-01 | $7700.00 | Window Closed / Lapsed |