US4056501A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Cationic structured-particle latexes
Assignee: Dow Chemical Co
•
Filing: 1975-04-21
•
Granted: 1977-11-01
•
Expires: 1995-04-21
Abstract
Abstract Structured-particle latexes are prepared from nonionic or slightly cationic latexes, either preformed or polymerized in situ, by emulsion polymerizing monomeric materials which include an ethylenically unsaturated, activated-halogen monomer such as vinylbenzyl chloride in the absence of a sufficient amount of a surfactant to initiate new particles whereby the activated-halogen monomer is copolymerized on the surface of the existing particles which are dispersed in an aqueous media. The resulting structured-particle latex may then be reacted with a nucleophile such as dimethyl sulfide or trimethyl amine to form a latex having stabilizing "onium" groups such as sulfonium groups or quaternary ammonium groups chemically bound at or near the surface of the polymer particles which are dispersed in aqueous media. The cationic latexes are suitable for coatings and organic pigments.
Inventors
- 👤 Dale S. Gibbs
- 👤 Earl H. Wagener
- 👤 Ritchie A. Wessling
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 17:16
CPC Classifications
C; C08; C08C; C08C1/00; C08C1/02; C08C1/06; C08F; C08F291/00
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
160 words
A method for preparing a cationic structured-particle latex comprising the steps of reacting at a temperature from about 0° to about 80° C a water-stable, nonionic nucleophile which is capable of diffusing through aqueous media with a latex of copolymer particles having activated halogens bound to a thin layer of the copolymer at or near the particle surface; said nucleophile having a hetero atom as a center of nucleophilicity wherein each covalent bond of said hetero atom is to a carbon atom; said activated-halogens being present in an amount from about 0.01 to about 3.0 milliequivalents per gram of copolymer in the latex, with the proviso that the amount of activated-halogen bound to the thin layer at or near the particle surface is in the range of from about 0.4 to about 3.0 milliequivalents for each gram of polymer in the thin layer, whereby pH independent cationic groups are chemically bound to the particles at or near the particle surface.
Claim 2
Independent Claim
160 words
A method for preparing a cationic structured-particle latex comprising the steps of reacting at a temperature from about 0° to about 80° C a water-stable, nonionic nucleophile which is capable of diffusing through aqueous media with a latex of copolymer particles having activated halogens bound to a thin layer of the copolymer at or near the particle surface; said nucleophile having a hetero atom as a center of nucleophilicity wherein each covalent bond of said hetero atom is to a carbon atom; said activated-halogens being present in an amount from about 0.01 to about 3.0 milliequivalents per gram of copolymer in the latex, with the proviso that the amount of activated-halogen bound to the thin layer at or near the particle surface is in the range of from about 0.4 to about 3.0 milliequivalents for each gram of polymer in the thin layer, whereby pH independent cationic groups are chemically bound to the particles at or near the particle surface.
Claim 3
Dependent Claim
35 words
The method of claim 1 in which the reaction is carried out until the pH independent cationic groups are present in an amount from about 0.01 milliequivalent to about 0.5 milliequivalent per gram of copolymer.
Claim 4
Dependent Claim
40 words
The method of claim 1 which is carried out until the pH independent cationic groups are present in the thin layer in an amount of from about 0.4 milliequivalent to about 1.6 milliequivalent per gram of polymer in the layer.
Claim 5
Dependent Claim
80 words
The method of claim 1 in which the latex of copolymer particles having activated-halogens is a structured-particle latex of copolymer particles consisting of a nonionic, organic polymer core having adhered thereto a thin layer of a water-insoluble copolymer of (a) an ethylenically unsaturated, nonionic monomer which is devoid of an activated-halogen and (b) a nonionic, ethylenically unsaturated, activated-halogen monomer; the amount of the activated-halogen in the copolymer being from about 0.01 milliequivalent to about 1.4 milliequivalents per gram of copolymer.
Claim 6
Dependent Claim
35 words
The method of claim 1 in which the latex of copolymer particles having activated-halogens bound to a thin layer of the copolymer at or near the particle surface also has bound activated-halogens throughout the particles.
Claim 7
Dependent Claim
33 words
The method of claim 1 in which the activated-halogens are provided by a copolymerized monomer selected from the group consisting of vinylbenzyl chloride, 2-chloromethylbutadiene, vinyl bromide, a bromoalkyl acrylate, and a bromoalkyl methacrylate.
Claim 8
Dependent Claim
12 words
The method of claim 1 in which the nucleophile is a tetraalkylthiourea.
Claim 9
Dependent Claim
60 words
The method of claim 1 in which the nucleophile is a compound having the formula R 1 --S--R 2 wherein R 1 and R 2 individually are lower alkyl, hydroxy lower alkyl or wherein R 1 and R 2 are combined as one alkylene radical having 3 to 5 carbon atoms, whereby the chemically bound cationic groups are sulfonium groups.
Claim 10
Dependent Claim
23 words
The method of claim 8 which has the additional step of oxidizing at least a part of the sulfonium groups to sulfoxonium groups.
Claim 11
Dependent Claim
88 words
An aqueous colloidal dispersion of cationic structured-particles of polymer consisting of a nonionic, organic polymer core encapsulated by a thin layer of a water-insoluble organic copolymer having pH independent cationic groups chemically bound to the organic copolymer at or near the particle surface; said cationic groups being present in an amount from about 0.01 milliequivalent to about 0.5 milliequivalent per gram of structured particles; said amount also being in the range of from about 0.4 milliequivalent to about 2.5 milliequivalents per gram of copolymer in the thin layer.
Claim 12
Dependent Claim
88 words
An aqueous colloidal dispersion of cationic structured-particles of polymer consisting of a nonionic, organic polymer core encapsulated by a thin layer of a water-insoluble organic copolymer having pH independent cationic groups chemically bound to the organic copolymer at or near the particle surface; said cationic groups being present in an amount from about 0.01 milliequivalent to about 0.5 milliequivalent per gram of structured particles; said amount also being in the range of from about 0.4 milliequivalent to about 2.5 milliequivalents per gram of copolymer in the thin layer.
Claim 13
Dependent Claim
28 words
The aqueous colloidal dispersion of claim 10 in which the amount of cationic groups is from about 0.04 milliequivalent to about 0.35 milliequivalent per gram of structured particles.
Claim 14
Dependent Claim
28 words
The aqueous colloidal dispersion of claim 10 in which the amount of cationic groups is less than about 1.6 milliequivalents per gram of copolymer in the thin layer.
Claim 15
Dependent Claim
16 words
The aqueous colloidal dispersion of claim 10 in which the cationic groups predominantly are sulfonium groups.
Claim 16
Dependent Claim
16 words
The aqueous colloidal dispersion of claim 10 in which the cationic groups predominantly are isothiouronium groups.
Claim 17
Dependent Claim
17 words
The aqueous colloidal dispersion of claim 10 in which the cationic groups predominantly are quaternary ammonium groups.
Claim 18
Dependent Claim
15 words
The aqueous colloidal dispersion of claim 15 in which quaternary ammonium groups are pyridinium groups.
Claim 19
Dependent Claim
29 words
The aqueous colloidal dispersion of claim 10 in which colloidal stability is provided predominantly by the cationic groups chemically bound to the copolymer at or near the particle surface.
Claim 20
Dependent Claim
19 words
The aqueous colloidal dispersion of claim 10 in which at least part of the cationic groups are sulfoxonium groups.
Claim 21
Dependent Claim
144 words
The method of claim 1 in which the nucleophile is selected from the group consisting of a. monobasic aromatic nitrogen compounds b. tetra (lower alkyl) thioureas c. R 1 --S--R 2 wherein R 1 and R 2 individually are lower alkyl, hydroxy lower alkyl or wherein R 1 and R 2 are combined as one alkylene radical having 3 to 5 carbon atoms d. ##STR3## wherein R 2 and R 3 individually are lower alkyl or hydroxy lower alkyl, or are combined as one alkylene radical having 3 to 5 carbon atoms and R 1 is lower alkyl, aralkyl or aryl except when R 2 and R 3 together are an alkylene radical then R 1 is lower alkyl or hydroxy lower alkyl, and e. ##STR4## wherein R 1 , R 2 and R 3 individually are lower alkyl, hydroxy lower alkyl or aryl.
References Cited (Backward Citations)
US3123636A
Cited
US3178396A
Cited
US3236820A
Cited
US3491050A
Cited
US3522199A
Cited
US3501432A
Cited
US3534105A
Cited
US3745196A
Cited
US3637432A
Cited
US3594355A
Cited
US3926890A
Cited
US3772143A
Cited
US3873488A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-10-31 | 1981-05-02 | 1981-11-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-10-31 | 1985-05-02 | 1985-11-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-10-31 | 1989-05-02 | 1989-11-01 | $7700.00 | Window Closed / Lapsed |