US4056304A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Light modulation employing single crystal optical waveguides of niobium-doped lithium tantalate
Assignee: RCA Corp
•
Filing: 1976-11-22
•
Granted: 1977-11-01
•
Expires: 1996-11-22
Abstract
Abstract An optical waveguide of niobium-doped lithium tantalate single crystal has excellent low loss waveguiding properties with strong electro-optic behavior. The waveguides are made by depositing a film of niobium on a polished lithium tantalate crystal, annealing the crystal so as to diffuse the niobium into the crystal and cooling the crystal.
Inventors
- 👤 William Phillips
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 01:18
CPC Classifications
G; G02; G02F; G02F1/00; G02F1/01; G02F1/03; G02F1/035; G02F1/29; G02F1/295; G02F1/2955
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
95 words
In a light modulator comprising a source of coherent light, an optical waveguide, a plurality of electrodes disposed in said waveguide, optical input means disposed on one side of said electrodes and optical output means disposed on the other side of said electrodes, the improvement which comprises employing as said optical waveguide a crystal prepared by depositing a film of niobium oxide on one surface of a polished single crystal of lithium tantalate, annealing the single cyrstal of lithium tantalate so as to allow the niobium to diffuse into the crystal and cooling the crystal.
Claim 2
Dependent Claim
95 words
In a light modulator comprising a source of coherent light, an optical waveguide, a plurality of electrodes disposed in said waveguide, optical input means disposed on one side of said electrodes and optical output means disposed on the other side of said electrodes, the improvement which comprises employing as said optical waveguide a crystal prepared by depositing a film of niobium oxide on one surface of a polished single crystal of lithium tantalate, annealing the single cyrstal of lithium tantalate so as to allow the niobium to diffuse into the crystal and cooling the crystal.
Claim 3
Dependent Claim
96 words
In a light modulator comprising a source of coherent light, an optical waveguide, a plurality of electrodes disposed on said waveguide, optical input means disposed on one side of said electrodes and optical output means disposed on the other side of said electrodes, the improvement which comprises employing as said optical waveguide a crystal prepared by depositing a film of niobium on one surface of a polished single crystal of lithium tantalate, oxidizing the niobium, annealing the crystal at an elevated temperature to allow the niobium to diffuse into the crystal, and cooling to room temperature.
Claim 4
Dependent Claim
96 words
In a light modulator comprising a source of coherent light, an optical waveguide, a plurality of electrodes disposed on said waveguide, optical input means disposed on one side of said electrodes and optical output means disposed on the other side of said electrodes, the improvement which comprises employing as said optical waveguide a crystal prepared by depositing a film of niobium on one surface of a polished single crystal of lithium tantalate, oxidizing the niobium, annealing the crystal at an elevated temperature to allow the niobium to diffuse into the crystal, and cooling to room temperature.
Claim 5
Dependent Claim
20 words
A light modulator according to claim 2 wherein the deposited niobium film is from about 25 to 5,000 Angstroms thick.
Claim 6
Dependent Claim
23 words
A light modulator according to claim 2 wherein the annealing step is carried out at a temperature from about 1,050° to 1,250° C.
Claim 7
Dependent Claim
23 words
A light modulator according to claim 2 wherein the annealing step is carried out at a temperature from about 1,100° to 1,200° C.
Claim 8
Dependent Claim
21 words
A light modulator according to claim 2 wherein the annealing step is carried out in an atmosphere of argon and oxygen.
Claim 9
Dependent Claim
21 words
A light modulator according to claim 2 wherein the annealing step is carried out in an atmosphere of nitrogen and oxygen.
Claim 10
Dependent Claim
16 words
A light modulator according to claim 2 wherein the annealing step is carried out in air.
Claim 11
Dependent Claim
16 words
A light modulator according to claim, 2 wherein the niobium is oxidized at about 300°-600° C.
Claim 12
Dependent Claim
16 words
A light modulator according to claim 2 wherein the crystal is poled during the cooling step.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-10-31 | 1981-05-02 | 1981-11-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-10-31 | 1985-05-02 | 1985-11-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-10-31 | 1989-05-02 | 1989-11-01 | $7700.00 | Window Closed / Lapsed |