Method and apparatus for severing and edge-sealing thermoplastic films, and product
Assignee: Individual
•
Filing: 1976-01-19
•
Granted: 1977-10-25
•
Expires: 1996-01-19
Abstract
Abstract A stack of many films of thermoplastic material is divided into sets of films by interposed layers of seal-inhibiting material. A heated cutter as of copper is used having a heat-storage portion and a blade projecting from the heat-storage portion, both shaped according to the desired edge seal. The hot blade is pressed against the stack to penetrate successive films, top to bottom. Thereafter, the blade represents a hot wall opposite to the parted edges of the film in the stack, causing transfer of heat into the stack for causing a controlled width of opposed films to become fused together. The time is not critical where the heat used is that which is stored in the cutter. The lateral surface of the blade extends from an edge, either perpendicular to the top surface of the stack or sloping away from the outline of the cut stack. The edge seal is ideally about 20% thicker than the combined thickness of the films forming a finished article, but it can be much thicker. The inner surfaces of a pair of films are face-to-face, well-suited to form a pressure-releasable valve in a spout of a container, especially a self-resealing valve.
Inventors
- 👤 Richard S. Carlisle
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 13:16
CPC Classifications
B; B29; B29C; B29C66/00; B29C66/80; B29C66/83; B29C66/834; B29C66/8351; B29C66/83531; B29C65/00; B29C65/02; B29C65/18; B29C65/74; B29C65/743; B29C65/7441; B29C66/004; B29C66/0042; B29C66/01; B29C66/05; B29C66/10; B29C66/11; B29C66/112; B29C66/1122; B29C66/13; B29C66/137; B29C66/20; B29C66/24; B29C66/244; B29C66/40; B29C66/41; B29C66/43; B29C66/431; B29C66/70; B29C66/72; B29C66/723; B29C66/73; B29C66/739; B29C66/7392; B29C66/73921; B29C66/81; B29C66/812; B29C66/8122; B29C66/814; B29C66/8141; B29C66/81411; B29C66/81415; B29C66/8341; B29C66/83421; B29C65/7437; B29C66/71; Y; Y10; Y10T; Y10T156/00; Y10T156/10; Y10T156/1052; Y10T156/1054
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
305 words
The method of making an article, including the steps of assembling at least one set of thermoplastic heat-sealable films, each film of said set having heat-sealable material that tends to become thickened when exposed to heat-sealing temperature and the assembled films of said set having their heat-sealable materials disposed against each other, heating a blade well above the fusion temperature of the heat-sealable material, appliying the blade with pressure against one face of the assembled films while so heated and while supporting the films opposite the edge of the blade against such pressure, the amount of pressure and the sharpness of the blade being less than that needed to effect die-cutting of the films in the absence of film-fusing heat, the blade thus providing severed edges of the films, and holding said films of each set together and heating to heat-sealing temperature marginal portions of the films along the severed edges far greater in width than the combined initial thickness of the set of films and thereby forming a wide marginal seal, said heating of the marginal portions of the films being effected both by exposing the films to the heated blade as aforesaid during severing and by subjecting at least one face of said set of films over the width of said marginal portions to heat-sealing temperature that diminishes progressively away from the blade to and beyond a juncture where the unsealed films merge into the marginal seal, said holding being accomplished with pressure limited so as to accommodate substantial thickening of at least part of the width of the seal, whereby the seal formed between the films of said set is of substantially greater thickness than the initial thickness of the set of films, said greater thickness extending across the seal outward from said juncture for a distance greater than said initial thickness.
Claim 2
Independent Claim
305 words
The method of making an article, including the steps of assembling at least one set of thermoplastic heat-sealable films, each film of said set having heat-sealable material that tends to become thickened when exposed to heat-sealing temperature and the assembled films of said set having their heat-sealable materials disposed against each other, heating a blade well above the fusion temperature of the heat-sealable material, appliying the blade with pressure against one face of the assembled films while so heated and while supporting the films opposite the edge of the blade against such pressure, the amount of pressure and the sharpness of the blade being less than that needed to effect die-cutting of the films in the absence of film-fusing heat, the blade thus providing severed edges of the films, and holding said films of each set together and heating to heat-sealing temperature marginal portions of the films along the severed edges far greater in width than the combined initial thickness of the set of films and thereby forming a wide marginal seal, said heating of the marginal portions of the films being effected both by exposing the films to the heated blade as aforesaid during severing and by subjecting at least one face of said set of films over the width of said marginal portions to heat-sealing temperature that diminishes progressively away from the blade to and beyond a juncture where the unsealed films merge into the marginal seal, said holding being accomplished with pressure limited so as to accommodate substantial thickening of at least part of the width of the seal, whereby the seal formed between the films of said set is of substantially greater thickness than the initial thickness of the set of films, said greater thickness extending across the seal outward from said juncture for a distance greater than said initial thickness.
Claim 3
Dependent Claim
15 words
The method set forth in claim 1 wherein said heat-sealable material is typified by polyethylene.
Claim 4
Dependent Claim
16 words
The method set forth in claim 1 wherein each film of said set consists of polyethylene.
Claim 5
Dependent Claim
33 words
The method set forth in claim 1 wherein said set of films comprises two laminated films having mutually opposed heat-sealable layers and having respective layers of higher melting temperature than said heat-sealable layers.
Claim 6
Dependent Claim
41 words
The method set forth in claim 1 further including the step of applying opposed pressure to said set of films at least over the heat-softened marginal portions thereof for promoting formation of seals of uniform width and thereby enhancing the seal.
Claim 7
Dependent Claim
47 words
The method set forth in claim 1 further including the step of applying opposed pressure to said set of films at least over thee heat-softened marginal portions thereof and over the films adjacent said marginal portions for assuring substantial face-to-face relationship between the films adjacent the seal.
Claim 8
Dependent Claim
69 words
The method set forth in claim 1 wherein said set of films comprises two laminated films having mutually opposed heat-sealable layers and having respective layers of higher melting temperature than said heat-sealable layers, and applying opposed pressure to said set of films at least over the heat-softened marginal poritons thereof and over the films adjacent said marginal poritions for assuring substantial face-to-face relationship between the films adjacent the seal.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-10-24 | 1981-04-25 | 1981-10-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-10-24 | 1985-04-25 | 1985-10-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-10-24 | 1989-04-25 | 1989-10-25 | $7700.00 | Window Closed / Lapsed |