Thermistor with leads and method of making
Assignee: Sprague Electric Co
•
Filing: 1976-12-20
•
Granted: 1977-10-11
•
Expires: 1996-12-20
Abstract
Abstract A PTCR thermistor has a doped barium titanate body, and two base metal lead wires being bonded to and ohmically connected to two separate surface regions of the body by means of two conductive electrodes, respectively. The electrodes are comprised of aluminum particles being bound within a matrix of a lead borate glass. The glass amounts to from 20 to 60% by weight. The simple method of making the thermistor may include the selective application of heat to the electrode regions to avoid oxidizing the base metal leads. These thermistors are capable of undergoing many self-heating switching operations in service without deterioration of the lead to body connections.
Inventors
- 👤 George H. Rodriguez
- 👤 John P. Maher
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 16:36
CPC Classifications
H; H01; H01C; H01C17/00; H01C17/28; H01C17/281; H01C17/283; H01C17/286; H01C7/00; H01C7/02; H01C7/022; H10; H10W; H10W72/00; H10W72/071; H10W72/075; H10W72/07551; H10W72/07554; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49082; Y10T29/49085; Y10T29/49101; Y10T428/00; Y10T428/25; Y10T428/256
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
99 words
A thermistor having a fatigue resistant lead joint comprising a PTCR titanate ceramic body; at least one electrode being bonded to and making ohmic contact with one surface region of said body; a base-metal lead having a portion thereof being bonded by and completely embedded within said one electrode; and another electrode being in contact with another surface region of said body, said one electrode being comprised of aluminum particles that are bound by a matrix of a lead-aluminoborate glass, said glass amounting to from 20 to 60% by weight of the sum of said glass and said aluminum.
Claim 2
Dependent Claim
99 words
A thermistor having a fatigue resistant lead joint comprising a PTCR titanate ceramic body; at least one electrode being bonded to and making ohmic contact with one surface region of said body; a base-metal lead having a portion thereof being bonded by and completely embedded within said one electrode; and another electrode being in contact with another surface region of said body, said one electrode being comprised of aluminum particles that are bound by a matrix of a lead-aluminoborate glass, said glass amounting to from 20 to 60% by weight of the sum of said glass and said aluminum.
Claim 3
Dependent Claim
11 words
The thermistor of claim 1 wherein said aluminum particles are spherical.
Claim 4
Dependent Claim
18 words
The thermistor of claim 1 wherein said aluminum particles have an average diameter of at least 5 microns.
Claim 5
Dependent Claim
46 words
The thermistor of claim 1 wherein said glass consists by weight of from 75 to 99.8% of a first group of oxides comprising 23 - 95% PbO 5-40% B 2 O 3 , and 0 - 40% SiO 2 ; and from 0.2 to 25% alumina.
Claim 6
Dependent Claim
16 words
The thermistor of claim 1 wherein said glass contains at least 10% SiO 2 by weight.
Claim 7
Dependent Claim
21 words
The thermistor of claim 1 wherein said base metal of said leads is selected from iron, copper, nickel and alloys thereof.
Claim 8
Dependent Claim
13 words
The thermistor of claim 1 wherein said base metal leads are silver plated.
Claim 9
Independent Claim
106 words
A method for making a thermistor having a fatigue resistant lead joint comprising positioning a portion of a base metal lead adjacent to a surface region of a PTCR titanate body; dispensing an electroding paste over said lead portion and said adjacent surface region of said body, said electroding paste comprising a mixture of a lead-borate glass powder, aluminum particles and an organic vehicle, and said glass amounting to from 20% to 60% by weight of the sum of said glass and said aluminum; and heating said dispensed electroding paste to melt said glass and to ohmically and physically attach said lead to said semiconducting body.
Claim 10
Independent Claim
106 words
A method for making a thermistor having a fatigue resistant lead joint comprising positioning a portion of a base metal lead adjacent to a surface region of a PTCR titanate body; dispensing an electroding paste over said lead portion and said adjacent surface region of said body, said electroding paste comprising a mixture of a lead-borate glass powder, aluminum particles and an organic vehicle, and said glass amounting to from 20% to 60% by weight of the sum of said glass and said aluminum; and heating said dispensed electroding paste to melt said glass and to ohmically and physically attach said lead to said semiconducting body.
Claim 11
Dependent Claim
11 words
The method of claim 8 wherein said aluminum particles are spherical.
Claim 12
Dependent Claim
18 words
The method of claim 8 wherein said aluminum particles have an average diameter of at least 5 microns.
Claim 13
Dependent Claim
18 words
The method of claim 8 wherein said heating is accomplished at a temperature from 660° to 850° C.
Claim 14
Dependent Claim
38 words
The method of claim 8 wherein said heating is accomplished by selectively directing said heat to the region of said electrode in order to avoid substantial heating and oxidizing of the extending portions of said base metal leads.
Claim 15
Dependent Claim
46 words
The method of claim 8 additionally comprising forming a film of said electroding paste on said surface region of said body and firing said film, said positioning being accomplished by placing said portion of said lead in contact with said fired film, prior to said dispensing.
Claim 16
Dependent Claim
35 words
The method of claim 8 wherein said glass contains by weight 23 - 95% PbO 5 - 40% b 2 o 3 0 - 40% siO 2 0 - 5% al 2 O 3 .
References Cited (Backward Citations)
US2752663A
Cited
US3019198A
Cited
US3231522A
Cited
US3310718A
Cited
US3457539A
Cited
US3547835A
Cited
US3676211A
Cited
US3808046A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-10-10 | 1981-04-11 | 1981-10-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-10-10 | 1985-04-11 | 1985-10-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-10-10 | 1989-04-11 | 1989-10-11 | $7700.00 | Window Closed / Lapsed |