Polyolefin catalyst and method for its preparation
Assignee: Chemplex Co
•
Filing: 1976-03-04
•
Granted: 1977-10-11
•
Expires: 1996-03-04
Abstract
Abstract A new catalyst and a method of polymerizing olefins in which the catalyst is prepared by forming a mixture by dispersing on a finely divided, difficult to reduce, inorganic support of the class consisting of silica, alumina, thoria, zirconia, titania, magnesia and mixtures or composites thereof, an organic chromium compound pyrolytically decomposable in the substantial absence of oxygen to deposit a catalytically active residue along with a carbon residue as a contaminant on the support, then activating the mixture by subjecting the mixture to non-oxidative pyrolysis to and at a temperature within the range of about 600 DEG -2000 DEG F., thereby depositing on the support the chromium-bearing residue and carbon residue as a by-product from the pyrolytic decomposition of the organic chromium compound, and subjecting the activated catalyst after this activating to heat and an oxidizing gas such as air, oxygen, carbon dioxide, nitrous oxide, and the like, to burn off a substantial amount of the carbon residue and to modify and improve the characteristics of the activated catalyst.
Inventors
- 👤 Joseph Liu
- 👤 Howard L. Grimmett
- 👤 Yu-Tang Hwang
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 20:14
CPC Classifications
C; C08; C08F; C08F10/00; Y; Y10; Y10S; Y10S502/00; Y10S502/506; Y10S502/513
Claims Analysis
Total Claims: 42
Claim 1
Independent Claim
168 words
The method of preparing a polyolefin catalyst, comprising: preparing a mixture by dispersing on a finely divided, difficult to reduce, inorganic support of the class consisting of silica, alumina, thoria, zirconia, titania, magnesia and mixtures and composites thereof an organic chromium compound pyrolytically decomposable in the substantial absence of oxygen to deposit a catalyst residue including as a contaminant a carbon residue on said support; activating said mixture by subjecting the mixture to non-oxidative pyrolysis to and at an activating temperature within the range of about 600°-2000° F., thereby depositing on said support a catalytically active residue for the polymerizing of 1-olefins of 2-8 carbon atoms and copolymerizing said olefins with 1-olefins of 2-20 carbon atoms, said residue including a black carbon deposit residue; and substantially removing said black carbon deposit by burning in an oxidizing gas at an elevated temperature for a short period of time sufficient to burn off said black carbon deposit residue, thereby simultaneously modifying and improving the characteristics of the resulting activated catalyst.
Claim 2
Independent Claim
168 words
The method of preparing a polyolefin catalyst, comprising: preparing a mixture by dispersing on a finely divided, difficult to reduce, inorganic support of the class consisting of silica, alumina, thoria, zirconia, titania, magnesia and mixtures and composites thereof an organic chromium compound pyrolytically decomposable in the substantial absence of oxygen to deposit a catalyst residue including as a contaminant a carbon residue on said support; activating said mixture by subjecting the mixture to non-oxidative pyrolysis to and at an activating temperature within the range of about 600°-2000° F., thereby depositing on said support a catalytically active residue for the polymerizing of 1-olefins of 2-8 carbon atoms and copolymerizing said olefins with 1-olefins of 2-20 carbon atoms, said residue including a black carbon deposit residue; and substantially removing said black carbon deposit by burning in an oxidizing gas at an elevated temperature for a short period of time sufficient to burn off said black carbon deposit residue, thereby simultaneously modifying and improving the characteristics of the resulting activated catalyst.
Claim 3
Dependent Claim
32 words
The method of claim 1 wherein said support prior to the dispersing thereon of said organic chromium compound is calcined at an elevated temperature until substantially all volatile matter is driven off.
Claim 4
Dependent Claim
23 words
The method of claim 2 wherein said calcining is done in a dry, inert atmosphere at an elevated temperature of about 300°-2000° F.
Claim 5
Dependent Claim
30 words
The method of claim 1 wherein said mixture is prepared by dissolving said organic chromium compound in a solvent and impregnating said support with the resulting solution followed by drying.
Claim 6
Dependent Claim
38 words
The method of claim 1 wherein said dispersing is accomplished by dry blending the organic chromium compound with the support and said activating is accomplished by heating in a fluid bed maintained in suspension with a non-oxidizing gas.
Claim 7
Dependent Claim
21 words
The method of claim 1 wherein said dispersing is accomplished by vaporizing and adsorbing said organic chromium compound onto the support.
Claim 8
Dependent Claim
31 words
The method of claim 1 wherein said activating is in a fluid bed using a non-oxidizing gas to maintain the mixture of support and organic chromium compound in a fluid condition.
Claim 9
Dependent Claim
158 words
The method of claim 1 wherein said organic chromium compound comprises a chromium chelate of a beta-dicarbonyl compound essentially of the formula of the class consisting of ##STR6## wherein each R is individually selected from hydrogen, alkyl, alkenyl, aryl, cycloalkyl and cycloalkenyl radicals and combinations of these radicals with each R containing 0-20 carbon atoms and a corresponding valence-satisfying number of hydrogen atoms, R' is selected from alkylene, alkenylene, arylene, cycloalkylene and cycloalkenylene radicals and combinations of these bivalent radicals with R' containing 1-20 carbon atoms and a corresponding valence-satisfying number of hydrogen atoms, m is a whole number from 1 to 3, n is a whole number from 0 to 2 with m plus n being a whole number from 2 to 3 and X is an inorganic or organic negative group relative to chromium, and said activating is accomplished by heating to and at an elevated temperature of from about 800°-2000° F. in a non-oxidizing atmosphere.
Claim 10
Dependent Claim
66 words
The method of claim 1 wherein said organic chromium compound comprises a π-bonded chromium compound essentially of the structure (L).sub.x -- Cr -- (L').sub.y wherein L and L' are the same or different organic ligands which are adapted to being pi-bonded to the chromium atom, and x and y are each integers of 0 to 3 inclusive, and x plus y equals 2 to 6, inclusive.
Claim 11
Dependent Claim
62 words
The method of claim 1 wherein said organic chromium compound comprises a tetravalent organochromium compound essentially of the structure Y 4 Cr wherein Y is selected individually from alkyl, alkenyl, cycloalkyl, cycloalkenyl, cycloalkyl-substituted alkyl, and aryl-substituted alkyl radicals containing 1 to about 14 carbon atoms and the tetravalent chromium atom is directly bonded to one of the carbon atoms in each Y.
Claim 12
Dependent Claim
19 words
The method of claim 1 wherein said organic chromium compound comprises the reaction product of ammonium chromate and pinacol.
Claim 13
Dependent Claim
34 words
The method of claim 1 wherein said organic chromium compound comprises a bis(trihydrocarbylsilyl)chromate essentially of the formula ##STR7## wherein R is hydrogen or a hydrocarbyl group containing from 1 to about 14 carbon atoms.
Claim 14
Dependent Claim
32 words
The method of claim 1 wherein said organic chromium comprises a bis(trihydrocarbylmethyl)chromate essentially of the formula ##STR8## wherein R is hydrogen or a hydrocarbyl radical containing 1 to about 14 carbon atoms.
Claim 15
Dependent Claim
40 words
The method of claim 1 wherein said organic chromium compound comprises a chromyl bis(trihydrocarbyltitanate) essentially of the formula ##STR9## wherein R is individually selected from alkyl, arylalkyl, cycloalkyl, alkenyl and cycloalkenyl radicals containing from 1 to about 14 carbon atoms.
Claim 16
Dependent Claim
166 words
A catalyst, prepared by the method comprising: preparing a mixture by dispersing on a finely divided, difficult to reduce, inorganic support of the class consisting of silica, alumina, thoria, zirconia, titania, magnesia, and mixtures and composites thereof an organic chromium compound pyrolytically decomposable in the substantial absence of oxygen to deposit a catalyst residue including as a contaminant a carbon residue on said support; activating said mixture by subjecting the mixture to non-oxidative pyrolysis to and at an activating temperature within the range of about 600°-2000° F., thereby depositing on said support a catalytically active residue for the polymerizing of 1-olefins of 2-8 carbon atoms and copolymerizing said olefins with 1-olefins of 2-20 carbon atoms, said residue including a black carbon deposit residue; and substantially removing said black carbon deposit by burning in an oxidizing gas at an elevated temperature for a short period of time sufficient to burn off said black carbon deposit residue, thereby simultaneously modifying and improving the characteristics of the activated catalyst.
Claim 17
Dependent Claim
166 words
A catalyst, prepared by the method comprising: preparing a mixture by dispersing on a finely divided, difficult to reduce, inorganic support of the class consisting of silica, alumina, thoria, zirconia, titania, magnesia, and mixtures and composites thereof an organic chromium compound pyrolytically decomposable in the substantial absence of oxygen to deposit a catalyst residue including as a contaminant a carbon residue on said support; activating said mixture by subjecting the mixture to non-oxidative pyrolysis to and at an activating temperature within the range of about 600°-2000° F., thereby depositing on said support a catalytically active residue for the polymerizing of 1-olefins of 2-8 carbon atoms and copolymerizing said olefins with 1-olefins of 2-20 carbon atoms, said residue including a black carbon deposit residue; and substantially removing said black carbon deposit by burning in an oxidizing gas at an elevated temperature for a short period of time sufficient to burn off said black carbon deposit residue, thereby simultaneously modifying and improving the characteristics of the activated catalyst.
Claim 18
Dependent Claim
32 words
The catalyst of claim 15 wherein said support prior to the dispersing thereon of said organic chromium compound is calcined at an elevated temperature until substantially all volatile matter is driven off.
Claim 19
Dependent Claim
23 words
The catalyst of claim 16 wherein said calcining is done in a dry, inert atmosphere at an elevated temperature of about 300°-2000° F.
Claim 20
Dependent Claim
30 words
The catalyst of claim 15 wherein said mixture is prepared by dissolving said organic chromium compound in a solvent and impregnating said support with the resulting solution followed by drying.
Claim 21
Dependent Claim
38 words
The catalyst of claim 15 wherein said dispersing is accomplished by dry blending the organic chromium compound with the support and said activating is accomplished by heating in a fluid bed maintained in suspension with a non-oxidizing gas.
Claim 22
Dependent Claim
21 words
The catalyst of claim 15 wherein said dispersing is accomplished by vaporizing and adsorbing said organic chromium compound onto the support.
Claim 23
Dependent Claim
31 words
The catalyst of claim 15 wherein said activating is in a fluid bed using a non-oxidizing gas to maintain the mixture of support and organic chromium compound is a fluid condition.
Claim 24
Dependent Claim
158 words
The catalyst of claim 15 wherein said organic chromium compound comprises a chromium chelate of a beta-dicarbonyl compound essentially of the formula of the class consisting of ##STR10## wherein each R is individually selected from hydrogen, alkyl, alkenyl, aryl, cycloalkyl and cycloalkenyl radicals and combinations of these radicals with each R containing 0-20 carbon atoms and a corresponding valence-satisfying number of hydrogen atoms, R' is selected from alkylene, alkenylene, arylene, cycloalkylene and cycloalkenylene radicals and combinations of these bivalent radicals with R' containing 1-20 carbon atoms and a corresponding valence-satisfying number of hydrogen atoms, m is a whole number from 1 to 3, n is a whole number from 0 to 2 with m plus n being a whole number of 2 to 3 and X is an inorganic or organic negative group relative to chromium, and said activating is accomplished by heating to and at an elevated temperature of from about 800°-2000° F. in a non-oxidizing atmosphere.
Claim 25
Dependent Claim
66 words
The catalyst of claim 15 wherein said organic chromium compound comprises a π-bonded chromium compound essentially of the structure (L).sub.x -- Cr -- (L').sub.y wherein L and L' are the same or different organic ligands which are adapted to being pi-bonded to the chromium atom, and x and y are each integers of 0 to 3 inclusive, and x plus y equals 2 to 6, inclusive.
Claim 26
Dependent Claim
62 words
The catalyst of claim 15 wherein said organic chromium compound comprises a tetravalent organochromium compound essentially of the structure Y 4 Cr wherein Y is selected individually from alkyl, alkenyl, cycloalkyl, cycloalkenyl, cycloalkyl-substituted alkyl, and aryl-substituted alkyl radicals containing 1 to about 14 carbon atoms and the tetravalent chromium atom is directly bonded to one of the carbon atoms in each Y.
Claim 27
Dependent Claim
19 words
The catalyst of claim 15 wherein said organic chromium compound comprises the reaction product of ammonium chromate and pinacol.
Claim 28
Dependent Claim
35 words
The catalyst of claim 15 wherein said organic chromium compound comprises a bis(trihydrocarbylsilyl) chromate essentially of the formula ##STR11## wherein R is hydrogen or a hydrocarbyl group containing from 1 to about 14 carbon atoms.
Claim 29
Dependent Claim
34 words
The catalyst of claim 15 wherein said organic chromium compound comprises a bis(trihydrocarbylmethyl)chromate essentially of the formula ##STR12## wherein R is hydrogen or a hydrocarbyl group containing from 1 to about 14 carbon atoms.
Claim 30
Dependent Claim
40 words
The catalyst of claim 15 wherein said organic chromium compound comprises a chromyl bis(trihydrocarbyltitanate) essentially of the formula ##STR13## wherein R is individually selected from alkyl, arylalkyl, cycloalkyl, alkenyl, and cycloalkenyl radicals containing from 1 to about 14 carbon atoms.
Claim 31
Dependent Claim
12 words
The method of claim 8 wherein said chromium chelate comprises chromium acetylacetonate.
Claim 32
Dependent Claim
12 words
The catalyst of claim 22 wherein said chromium chelate comprises chromium acetylacetonate.
Claim 33
Dependent Claim
13 words
The method of claim 9 wherein said π-bonded chromium compound comprises bis(cyclopentadienyl)chromium (II).
Claim 34
Dependent Claim
12 words
The catalyst of claim 23 wherein said π-bonded chromium compound comprises bis(cyclopentadienyl)chromium(II).
Claim 35
Dependent Claim
11 words
The method of claim 12 wherein said bis(trihydrocarbylsilyl) chromate comprises bis(triphenylsilyl)chromate.
Claim 36
Dependent Claim
11 words
The catalyst of claim 26 wherein said bis(trihydrocarbylsilyl) chromate comprises bis(triphenylsilyl)chromate.
Claim 37
Dependent Claim
32 words
The method of claim 1 wherein said burning off of carbon residue is accomplished by using a gas that is either dry air, oxygen, carbon dioxide, nitrous oxide, or a mixture thereof.
Claim 38
Dependent Claim
26 words
The method of claim 35 wherein said gas is diluted with an inert gas of the nature of nitrogen, helium, argon, neon or mixtures of these.
Claim 39
Dependent Claim
32 words
The catalyst of claim 15 wherein said burning off of carbon residue is accomplished by using a gas that is either dry air, oxygen, carbon dioxide, nitrous oxide, or a mixture thereof.
Claim 40
Dependent Claim
26 words
The catalyst of claim 37 wherein said gas is diluted with an inert gas of the nature of nitrogen, helium, argon, neon or mixtures of these.
Claim 41
Dependent Claim
18 words
The method of claim 1 wherein said burning is at a temperature of about 900°-1700° F. in air.
Claim 42
Dependent Claim
18 words
The catalyst of claim 15 wherein said burning is at a temperature of about 900°-1700° F. in air.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-10-10 | 1981-04-11 | 1981-10-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-10-10 | 1985-04-11 | 1985-10-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-10-10 | 1989-04-11 | 1989-10-11 | $7700.00 | Window Closed / Lapsed |