US4052359A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Dilutable resole resin solutions having stabilized dispersed inert salts
Assignee: Monsanto Co
•
Filing: 1976-02-18
•
Granted: 1977-10-04
•
Expires: 1996-02-18
Abstract
Abstract This invention relates to stable water dilutable resoles. Said resoles are catalyzed with alkaline earth metal hydroxides and neutralized with oxalic acid or its acid salts providing inert insoluble oxalate salts dispersed in said resoles. Said salts are size controlled and stabilized by the presence of particular anionic type dispersing agents. A method for manufacture is disclosed.
Inventors
- 👤 Harold P. Higginbottom
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 02:48
CPC Classifications
C; C08; C08G; C08G8/00; C08G8/04; C08G8/08; C08G8/10; C08K; C08K5/00; C08K5/04; C08K5/09; C08K5/098; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/2938
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
181 words
A stable dilutable aqueous solution of a resole resin having pH of 3 to 8.5 comprising: a. said resole resin having a number average molecular weight is less than about 250, a water tolerance greater than 500 percent, a combined formaldehyde to phenol ratio in the range of from about 1.0:1 to 2.9:1, b. a dispersion of insoluble oxalate salt particles, wherein, said resole being prepared with a catalyst comprising alkaline earth metal hydroxides selected from the group consisting of magnesium, calcium, barium strontium and mixtures thereof, said pH being adjusted with a compound selected from the group consisting of oxalic acid, ammonium oxalate and mixtures thereof providing a dispersion of insoluble oxalate salt particles of said alkaline earth metal ions in said solution, and c. said solution having present an anionic dispersing agent in an amount of from about 0.10 to 20 percent based on the weight of said resole resin, said dispersing agent being selected so as to prevent flocculation of said particles when water, up to the water tolerance of said resole resin is added to said solution.
Claim 2
Dependent Claim
181 words
A stable dilutable aqueous solution of a resole resin having pH of 3 to 8.5 comprising: a. said resole resin having a number average molecular weight is less than about 250, a water tolerance greater than 500 percent, a combined formaldehyde to phenol ratio in the range of from about 1.0:1 to 2.9:1, b. a dispersion of insoluble oxalate salt particles, wherein, said resole being prepared with a catalyst comprising alkaline earth metal hydroxides selected from the group consisting of magnesium, calcium, barium strontium and mixtures thereof, said pH being adjusted with a compound selected from the group consisting of oxalic acid, ammonium oxalate and mixtures thereof providing a dispersion of insoluble oxalate salt particles of said alkaline earth metal ions in said solution, and c. said solution having present an anionic dispersing agent in an amount of from about 0.10 to 20 percent based on the weight of said resole resin, said dispersing agent being selected so as to prevent flocculation of said particles when water, up to the water tolerance of said resole resin is added to said solution.
Claim 3
Dependent Claim
28 words
An aqueous solution of claim 1, wherein said resole resin is present in amounts of from about 2 to 90 percent by weight based on said aqueous solution.
Claim 4
Dependent Claim
33 words
An aqueous solution of claim 1, having present a formaldehyde scavenger selected from the group consisting of ammonia, primary and secondary amines, urea, substituted ureas, primary amides, dicyandiamide, guanidines, aminotriazines and mixtures thereof.
Claim 5
Dependent Claim
31 words
An aqueous solution of claim 3, wherein said formaldehyde scavenger is present in amounts of from about 0.5 to 1.5 mole equivalents per mole of free formaldehyde in said aqueous solution.
Claim 6
Dependent Claim
16 words
An aqueous solution of claim 1, wherein said anionic dispersing agent is a sulfo-acid salt type.
Claim 7
Dependent Claim
45 words
An aqueous solution of claim 1, wherein said anionic dispersing agent is selected from the polymeric group consisting of lignosulfonates, naphthalene sulfonates, alkyl naphthalene sulfonates, alkyl benzoid, sulfonates, succinate sulfonates, amino azine sulfonates, sodium, potassium, calcium and ammonium salts of said group and mixtures thereof.
Claim 8
Dependent Claim
21 words
An aqueous solution of claim 1, wherein said dispersed oxalate salt particles have an average particle size of less then 2μ.
Claim 9
Dependent Claim
23 words
An aqueous solution of claim 1, wherein said dispersed oxalate salt particles have an average particle size ranging from about 0.02 to 0.8μ.
Claim 10
Dependent Claim
73 words
An aqueous solution of claim 1, wherein said pH range is 6 to 8.5, the resole resin having an average molecular weight of from about 150 to 250, a water tolerance greater than 500 percent, a combined formaldehyde to phenol ratio of from about 1.0:1 to 2.9:1, wherein the inert oxalate salt is calcium or barium oxalate and wherein said anionic dispersing agent is a lignosulfonate, a sulfonated naphthalene-formaldehyde resin or salts thereof.
Claim 11
Dependent Claim
184 words
A process for preparing stable dilutable aqueous resole resin solutions which comprises: a. reacting 1.0 mole of phenol with from about 1.0 to 3.5 moles of formaldehyde under basic conditions so as to produce a resole resin having a number average molecular weight in the range of from about 150 to 250, said basic conditions being provided by a alkaline earth hydroxide catalyst selected from the group consisting of magnesium, calcium, barium, strontium and mixtures thereof, b. adjusting the pH of said solution to about 3 and 8.5 with a compound selected from the group consisting of oxalic acid, ammonium oxalate and mixtures thereof in the presence of from about 0.10 to 20 percent by weight, based on said resole resin, of an anionic dispersing agent. c. producing a stable dispersion of insoluble particles of oxalate salts of said alkaline earth metal ions in said solution, said dispersing agent being selected to optimize the particle size of said salts and to inhibit the flocculation of said slats when water up to the water tolerance of said resole resin is added to said resole solutions.
Claim 12
Dependent Claim
184 words
A process for preparing stable dilutable aqueous resole resin solutions which comprises: a. reacting 1.0 mole of phenol with from about 1.0 to 3.5 moles of formaldehyde under basic conditions so as to produce a resole resin having a number average molecular weight in the range of from about 150 to 250, said basic conditions being provided by a alkaline earth hydroxide catalyst selected from the group consisting of magnesium, calcium, barium, strontium and mixtures thereof, b. adjusting the pH of said solution to about 3 and 8.5 with a compound selected from the group consisting of oxalic acid, ammonium oxalate and mixtures thereof in the presence of from about 0.10 to 20 percent by weight, based on said resole resin, of an anionic dispersing agent. c. producing a stable dispersion of insoluble particles of oxalate salts of said alkaline earth metal ions in said solution, said dispersing agent being selected to optimize the particle size of said salts and to inhibit the flocculation of said slats when water up to the water tolerance of said resole resin is added to said resole solutions.
Claim 13
Dependent Claim
22 words
A process of claim 10, wherein said reacting of step (a) is carried out at temperatures of from 40° to 80° C.
Claim 14
Dependent Claim
26 words
A process of claim 10, wherein said basic conditions are provided by from about 0.02 to 0.30 mole equivalents of said catalyst per mole of phenol.
Claim 15
Dependent Claim
78 words
A process of claim 10, wherein said catalyst comprises said alkaline earth hydroxides used in combination with a compound selected from the group consisting of lithium hydroxide, sodium hydroxide, potassium hydroxide, sodium carbonate, potassium carbonate, organic amines, aqueous ammonia and mixtures thereof wherein about 0.02 to 0.30 mole equivalents of combined catalyst are used per mole of phenol charged, said alkaline earth catalysts constituting about 50 to 95 percent of the mole equivalents provided by said combined catalyst.
Claim 16
Dependent Claim
21 words
A process of claim 10, wherein said formaldehyde is an aqueous formalin solution containing from about 30 to 70 percent formaldehyde.
Claim 17
Dependent Claim
29 words
A process of claim 10, wherein said reacting is carried out so that an aqueous solution containing 40 to 70 percent by weight of said resole resin is formed.
Claim 18
Dependent Claim
40 words
A process of claim 15, wherein the percent by weight of the resole resin in said aqueous solution is determined by the vacuum stripping of water formed in step (a) in amounts sufficient to provide the percent by weight desired.
Claim 19
Dependent Claim
35 words
A process of claim 15, wherein the percent by weight of the resole resin in said aqueous solution is determined by the addition of water in amounts sufficient to provide the percent by weight desired.
Claim 20
Dependent Claim
36 words
A process of claim 10, wherein a formaldehyde scavenger is added at the end of step (a) and reacted with the free aldehyde in said aqueous solution at temperatures ranging from about 20° to 60° C.
Claim 21
Dependent Claim
29 words
A process of claim 18, wherein said scavenger is added in amounts of from about 0.5 to 1.5 mole equivalents per mole of free formaldehyde in said aqueous solution.
Claim 22
Dependent Claim
19 words
A process of claim 10, wherein said anionic dispersing agent is added after adjusting said pH in step (b).
Claim 23
Dependent Claim
28 words
A process of claim 10, wherein step (b) is carried out with sufficient agitation to produce dispersed inert salts having an average particle size of less than 2μ.
Claim 24
Dependent Claim
20 words
A process of claim 10, wherein step (b) is carried out at temperatures of from about 25° to 75° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-10-03 | 1981-04-04 | 1981-10-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-10-03 | 1985-04-04 | 1985-10-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-10-03 | 1989-04-04 | 1989-10-04 | $7700.00 | Window Closed / Lapsed |