US4052182A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for producing air blown glass fiber strand mat
Assignee: Owens Corning
•
Filing: 1974-04-08
•
Granted: 1977-10-04
•
Expires: 1994-04-08
Abstract
Abstract A process of making a mat of glass fibers wherein a strand of glass fibers frictionally engages the surface of a revolving cylinder from which the strand is tangentially discharged onto a moving conveyor. The strand is caused to be randomly looped upon the conveyor by alternate blasts of air which laterally impinge upon the strand to throw the strand in a looped fashion from side to side across the conveyor. More efficient and sustained operation in the processing of glass fiber mat is obtained by wetting the individual filaments of glass with a water solution comprising organosilane, nonionic lubricants, and acidic salt, which water solution eliminates wheel wrap of the glass fiber strand around the revolving cylinder without adversely affecting other desirable properties of the strand and the mat.
Inventors
- 👤 Joseph P. Stalego
- 👤 William H. Rigby, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 14:45
CPC Classifications
D; D04; D04H; D04H3/00; D04H3/02; D04H3/03; C; C03; C03C; C03C25/00; C03C25/10; C03C25/24; C03C25/26
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
148 words
In the process of making mats of glass fiber strands, comprising the steps of attenuating molten streams of glass into fibers, gathering the fibers into strands, passing the strands over respective revolving wheels which wheels attenuate the glass fibers and deliver the strands downwardly to a moving foraminous collection surface, causing the strands to be traversed back and forth across the moving foraminous collection surface at a rate that is a fraction of the rate of the delivery downwardly by the revolving wheel, and depositing the strands upon the collection surface by air flow downwardly through the conveyor to form a mat, the improvement comprising contacting the fibers with an aqueous solution consisting essentially of water, an organosilane, a polyhydric alcohol adduct and an inorganic acidic salt, said acidic salt being present in said solution in an amount sufficient to improve the processibility of said fibers during attenuation.
Claim 2
Dependent Claim
148 words
In the process of making mats of glass fiber strands, comprising the steps of attenuating molten streams of glass into fibers, gathering the fibers into strands, passing the strands over respective revolving wheels which wheels attenuate the glass fibers and deliver the strands downwardly to a moving foraminous collection surface, causing the strands to be traversed back and forth across the moving foraminous collection surface at a rate that is a fraction of the rate of the delivery downwardly by the revolving wheel, and depositing the strands upon the collection surface by air flow downwardly through the conveyor to form a mat, the improvement comprising contacting the fibers with an aqueous solution consisting essentially of water, an organosilane, a polyhydric alcohol adduct and an inorganic acidic salt, said acidic salt being present in said solution in an amount sufficient to improve the processibility of said fibers during attenuation.
Claim 3
Dependent Claim
22 words
The process of claim 1 wherein said solution contains from about 0.01 to about 0.40 percent by weight of said acidic salt.
Claim 4
Dependent Claim
49 words
The process of claim 1 wherein said solution contains from about 0.015 to about 0.85 percent by weight of said organosilane, from about 0.05 to about 1.50 percent by weight of said polyhydric alcohol adduct, and from about 0.01 to about 0.40 percent by weight of said acidic salt.
Claim 5
Dependent Claim
52 words
The process of claim 1 further comprising the steps of applying a binder composition to the mat, draining excess composition from the mat and curing the binder at cross-over points formed by the strands comprising the mat, whereby a mat having substantially equal strength longitudinally and transversely of the mat is produced.
Claim 6
Dependent Claim
35 words
The process of claim 1 wherein the acidic salt is selected from the group consisting of ammonium sulfate, ammonium phosphate, ammonium chloride, ammonium nitrate, ammonium perchlorate, ammonium sulphonate, ammonium phosphonate and combinations of said salts.
Claim 7
Dependent Claim
44 words
The process of claim 1 in which said organosilane is selected from the group consisting of aminosilanes and hydrolyzable organosilanes in which the organo radical attached to the silicon group is selected from the group consisting of epoxy, alkenyl, acrylate, mercapto and carboxyl radicals.
Claim 8
Dependent Claim
16 words
The process of claim 1 in which polyhydric alcohol adduct is a polyoxyethylene polyhydric alcohol adduct.
Claim 9
Dependent Claim
13 words
The process of claim 1 in which said polyhydric alcohol adduct is octylphenoxypoly(ethyleneoxy)ethanol.
Claim 10
Dependent Claim
24 words
The process of claim 1 in which said organosilane is gammaaminopropyltriethoxysilane, said polyhydric alcohol adduct is octylphenoxypoly(ethyleneoxy)ethanol and said acidic salt is ammonium sulfate.
Claim 11
Dependent Claim
24 words
A composition consisting essentially of a. at least one glass fiber; b. an organosilane; c. a polyhydric alcohol adduct; and, d. an acidic salt.
Claim 12
Dependent Claim
24 words
A composition consisting essentially of a. at least one glass fiber; b. an organosilane; c. a polyhydric alcohol adduct; and, d. an acidic salt.
Claim 13
Dependent Claim
167 words
In the process of making mats of glass fibers in which said fibers are sized with an aqueous solution prior to the deposition of said fibers in the form of a mat, the improvement comprising contacting said fibers with an aqueous solution consisting essentially of water, an organosilane, a polyhydric alcohol adduct and an inorganic acid salt, said solution containing about 0.015 to about 0.85 percent by weight of said organosilane, from about 0.05 to about 1.50 percent by weight of said polyhydric alcohol adduct and from about 0.01 to about 0.40 percent by weight of said inorganic acid salt, said salt being selected from the group consisting of ammonium sulfate, ammonium phosphate, ammonium chloride, ammonium nitrate, ammonium perchlorate, ammonium sulphonate, ammonium phosphonate and combinations of said ammonium salts, and said organosilane being selected from the group consisting of aminosilanes and hydrolyzable organosilanes in which the organo radical attached to the silicon group is selected from the group consisting of epoxy, alkenyl, acrylate, mercapto and carboxyl radicals.
Claim 14
Dependent Claim
167 words
In the process of making mats of glass fibers in which said fibers are sized with an aqueous solution prior to the deposition of said fibers in the form of a mat, the improvement comprising contacting said fibers with an aqueous solution consisting essentially of water, an organosilane, a polyhydric alcohol adduct and an inorganic acid salt, said solution containing about 0.015 to about 0.85 percent by weight of said organosilane, from about 0.05 to about 1.50 percent by weight of said polyhydric alcohol adduct and from about 0.01 to about 0.40 percent by weight of said inorganic acid salt, said salt being selected from the group consisting of ammonium sulfate, ammonium phosphate, ammonium chloride, ammonium nitrate, ammonium perchlorate, ammonium sulphonate, ammonium phosphonate and combinations of said ammonium salts, and said organosilane being selected from the group consisting of aminosilanes and hydrolyzable organosilanes in which the organo radical attached to the silicon group is selected from the group consisting of epoxy, alkenyl, acrylate, mercapto and carboxyl radicals.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-10-03 | 1981-04-04 | 1981-10-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-10-03 | 1985-04-04 | 1985-10-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-10-03 | 1989-04-04 | 1989-10-04 | $7700.00 | Window Closed / Lapsed |