Controlled environmental deterioration of plastics
Assignee: OI Glass Inc
•
Filing: 1976-02-12
•
Granted: 1977-09-27
•
Expires: 1996-02-12
Abstract
Abstract There is disclosed the preparation of a degradable polymeric material consisting essentially of an organic polymeric base containing a degradation-promoting amount of a partially degraded organic polymer. The organic polymeric base and the degradation-promoting additive may be derived from the same or different polymers. The invention is especially useful in controlling the environmental deterioration of plastics. The rate of deterioration is a function of the environmental conditions such as light, oxygen, and temperature; the concentration of the additive; and the chemical structure(s) of both the base and the additive.
Inventors
- 👤 John W. Tobias
- 👤 Lynn J. Taylor
- 👤 Stuart J. Gaumer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 13:48
CPC Classifications
C; C08; C08K; C08K5/00; C08K5/0008; C08K5/0033; C08L; C08L101/00; Y; Y10; Y10S; Y10S260/00; Y10S260/43; Y10S526/00; Y10S526/914
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
50 words
A process for preparing a degradable plastic composition, which process comprises: a. preparing a partially oxidized organic polymer by heating an oxidizable organic polymer in the presence of gaseous oxygen; b. and then incorporating said partially oxidized organic polymer into a thermoplastic organic base polymer different from said oxidizable polymer.
Claim 2
Dependent Claim
50 words
A process for preparing a degradable plastic composition, which process comprises: a. preparing a partially oxidized organic polymer by heating an oxidizable organic polymer in the presence of gaseous oxygen; b. and then incorporating said partially oxidized organic polymer into a thermoplastic organic base polymer different from said oxidizable polymer.
Claim 3
Dependent Claim
38 words
A process according to claim 1 wherein said oxidizable organic polymer is heated to a temperature below the decomposition temperature of said oxidizable organic polymer in the presence of gaseous oxygen to form said partially oxidized organic polymer.
Claim 4
Dependent Claim
110 words
A process according to claim 2 wherein said organic base polymer and said oxidizable organic polymer are selected from the group consisting of polyethylene, polypropylene, poly (1-butene), poly (4-methyl-1-pentene), ethylene-propylene copolymers, ethylene-1-butene copolymers, ethylene-1-hexene copolymers, ethylene-vinyl acetate copolymers, ethylene-ethyl acrylate copolymers, ethylene-acrylic acid copolymers and their salts, polystyrene, polyvinyl chloride, poly (vinylidene chloride), polyvinyl fluoride, poly (vinylidene fluoride), polyoxymethylene, poly (ethylene oxide), poly (propylene oxide), polyvinyl alcohol, polyvinyl acetate, polyvinyl formal, polyvinyl butyral, poly (methyl acrylate), poly (ethyl acrylate), poly (caprolactam), poly (hexamethyleneadipamide), poly (ethylene terephthalate), vinyl chloride-vinyl acetate copolymers, styrene-butadiene copolymers, styreneisoprene copolymers, cellulose acetate, cellulose propionate, cellulose acetate butyrate, ethyl cellulose, methyl cellulose, hydroxyethyl cellulose, and hydroxypropyl cellulose.
Claim 5
Dependent Claim
48 words
A process according to claim 2 wherein about 0.1 to about 30 percent by weight of said partially oxidized organic polymer is incorporated into said thermoplastic organic base polymer, said percent by weight being based on the total weight of said partially oxidized polymer and organic base polymer.
Claim 6
Dependent Claim
21 words
A process according to claim 2 wherein said partially oxidized polymer is blended with said organic base polymer in molten form.
Claim 7
Dependent Claim
62 words
A process for degrading a thermoplastic organic base polymer, which process comprises: a. preparing a partially oxidized organic polymer by heating an oxidizable organic polymer in the presence of gaseous oxygen; b. incorporating said partially oxidized organic polymer into said thermoplastic organic base polymer; and c. exposing the resultant polymeric composition to at least one natural environmental condition to degrade said composition.
Claim 8
Dependent Claim
62 words
A process for degrading a thermoplastic organic base polymer, which process comprises: a. preparing a partially oxidized organic polymer by heating an oxidizable organic polymer in the presence of gaseous oxygen; b. incorporating said partially oxidized organic polymer into said thermoplastic organic base polymer; and c. exposing the resultant polymeric composition to at least one natural environmental condition to degrade said composition.
Claim 9
Dependent Claim
38 words
A process according to claim 6 wherein said oxidizable organic polymer is heated to a temperature below the decomposition temperature of said oxidizable organic polymer in the presence of gaseous oxygen to form said partially oxidized organic polymer.
Claim 10
Dependent Claim
110 words
A process according to claim 6 wherein said organic base polymer and said oxidizable organic polymer are selected from the group consisting of polyethylene, polypropylene, poly (1-butene), poly (4-methyl-1-pentene), ethylene-propylene copolymers, ethylene-1-butene copolymers, ethylene-1-hexene copolymers, ethylene-vinyl acetate copolymers, ethylene-ethyl acrylate copolymers, ethylene-acrylic acid copolymers and their salts, polystyrene, polyvinyl chloride, poly (vinylidene chloride), polyvinyl fluoride, poly (vinylidene fluoride), polyoxymethylene, poly (ethylene oxide), poly (propylene oxide), polyvinyl alcohol, polyvinyl acetate, polyvinyl formal, polyvinyl butyral, poly (methyl acrylate), poly (ethyl acrylate), poly (caprolactam), poly (hexamethyleneadipamide), poly (ethylene terephthalate), vinyl chloride-vinyl acetate copolymers, styrene-butadiene copolymers, styreneisoprene copolymers, cellulose acetate, cellulose propionate, cellulose acetate butyrate, ethyl cellulose, methyl cellulose, hydroxyethyl cellulose, and hydroxypropyl cellulose.
Claim 11
Dependent Claim
48 words
A process according to claim 6 wherein about 0.1 to about 30 percent by weight of said partially oxidized organic polymer is incorporated into said thermoplastic organic base polymer, said percent by weight being based on the total weight of said partially oxidized polymer and organic base polymer.
Claim 12
Dependent Claim
21 words
A process according to claim 6 wherein said partially oxidized polymer is blended with said organic base polymer in molten form.
Claim 13
Dependent Claim
24 words
A process according to claim 6 wherein said natural environmental condition is selected from the group consisting of light, oxygen, elevated temperature and humidity.
Claim 14
Dependent Claim
47 words
A process for degrading a thermoplastic organic base polymer, which comprises: a. incorporating into said organic base polymer a degradation-promoting amount of at least one partially oxidized organic polymer; and b. exposing the resultant polymeric composition to at least one natural environmental condition to degrade said composition.
Claim 15
Dependent Claim
47 words
A process for degrading a thermoplastic organic base polymer, which comprises: a. incorporating into said organic base polymer a degradation-promoting amount of at least one partially oxidized organic polymer; and b. exposing the resultant polymeric composition to at least one natural environmental condition to degrade said composition.
Claim 16
Dependent Claim
110 words
A process according to claim 12 wherein said organic base polymer and said oxidizable organic polymer are selected from the group consisting of polyethylene, polypropylene, poly (1-butene), poly (4-methyl-1-pentene), ethylene-propylene copolymers, ethylene-1-butene copolymers, ethylene-1-hexene copolymers, ethylene-vinyl acetate copolymers, ethylene-ethyl acrylate copolymers, ethylene-acrylic acid copolymers and their salts, polystyrene, polyvinyl chloride, poly (vinylidene chloride), polyvinyl fluoride, poly (vinylidene fluoride), polyoxymethylene, poly (ethylene oxide), poly (propylene oxide), polyvinyl alcohol, polyvinyl acetate, polyvinyl formal, polyvinyl butyral, poly (methyl acrylate), poly (ethyl acrylate), poly (caprolactam), poly (hexamethyleneadipamide), poly (ethylene terephthalate), vinyl chloride-vinyl acetate copolymers, styrene-butadiene copolymers, styreneisoprene copolymers, cellulose acetate, cellulose propionate, cellulose acetate butyrate, ethyl cellulose, methyl cellulose, hydroxyethyl cellulose, and hydroxypropyl cellulose.
Claim 17
Dependent Claim
48 words
A process according to claim 12 wherein about 0.1 to about 30 percent by weight of said partially oxidized organic polymer is incorporated into said thermoplastic organic base polymer, said percent by weight being based on the total weight of said partially oxidized polymer and organic base polymer.
Claim 18
Dependent Claim
21 words
A process according to claim 12 wherein said partially oxidized polymer is blended with said organic base polymer in molten form.
Claim 19
Dependent Claim
24 words
A process according to claim 12 wherein said natural environmental condition is selected from the group consisting of light, oxygen, elevated temperature and humidity.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-09-26 | 1981-03-28 | 1981-09-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-09-26 | 1985-03-28 | 1985-09-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-09-26 | 1989-03-28 | 1989-09-27 | $7700.00 | Window Closed / Lapsed |