Process for the production of propellant charge powders, especially nitroguanidine powders
Assignee: Dynamit Nobel AG
•
Filing: 1975-12-29
•
Granted: 1977-09-27
•
Expires: 1995-12-29
Abstract
Abstract A process for producing propellant charge powders from solvent-containing mixtures such as nitroguanidine powders containing nitrocellulose and/ or nitrocellulose and diglycol dinitrate or nitroglycerin and nitroguanidine and additives wherein an alcohol-containing mixture or optionally a water-containing mixture of said propellant charge powders is premixed with additional components of the propellant powder, the mixture is first dried, if necessary, and the solvent is incorporated therein and the solvent-containing premix is homogenized and preplasticized in a kneading device or the water-containing premix is homogenized and preplasticized in the kneading device and then the resultant mixture is dewatered by drying and then combined with a solvent; then the solvent-containing mixture is plasticized in an extruder and converted thereby into granular form and the resulting granular material is extruded into a final product form in a screw-type extruder. Subsequently, the solvent is evaporated therefrom.
Inventors
- 👤 Heinrich Brachert
- 👤 Joachim Kleiss
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 03:09
CPC Classifications
C; C06; C06B; C06B21/00; C06B21/0033; C06B21/0075; C06B21/0008
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
151 words
A process for the production of propellant charge powders from solvent-containing mixtures containing nitrocellulose, and components selected from the group consisting of diglycol dinitrate, nitroglycerin, nitroguanidine, penthrite, and hexogen and mixtures thereof, and further additives, which comprises premixing an alcohol-containing or a water-containing raw mixture containing nitrocellulose with additional required components of the propellant powder; then either incorporating a solvent in the alcohol-containing mixture and homogenizing and preplasticizing the solvent-containing premix of the components in a continuously operating kneading device or homogenizing and preplasticizing the water-containing premix of the components in the continuously operating kneading device, then only thereafter dewatering the mixture by drying and combining the mixture with a solvent; then plasticizing the solvent-containing preplasticized mixture in a continuously operating screw-type extruder; converting the resultant mixture into granular form; extruding the granulated material finally into a final powder form in a continuously operating screw-type extruder; and evaporating the solvent therefrom.
Claim 2
Dependent Claim
151 words
A process for the production of propellant charge powders from solvent-containing mixtures containing nitrocellulose, and components selected from the group consisting of diglycol dinitrate, nitroglycerin, nitroguanidine, penthrite, and hexogen and mixtures thereof, and further additives, which comprises premixing an alcohol-containing or a water-containing raw mixture containing nitrocellulose with additional required components of the propellant powder; then either incorporating a solvent in the alcohol-containing mixture and homogenizing and preplasticizing the solvent-containing premix of the components in a continuously operating kneading device or homogenizing and preplasticizing the water-containing premix of the components in the continuously operating kneading device, then only thereafter dewatering the mixture by drying and combining the mixture with a solvent; then plasticizing the solvent-containing preplasticized mixture in a continuously operating screw-type extruder; converting the resultant mixture into granular form; extruding the granulated material finally into a final powder form in a continuously operating screw-type extruder; and evaporating the solvent therefrom.
Claim 3
Dependent Claim
18 words
A process according to claim 1, wherein a disk-type kneader is employed as the continuously operating kneading device.
Claim 4
Dependent Claim
29 words
A process according to claim 1, wherein the process is carried out in the kneading device without the use of excess pressure at temperatures of up to 80° C.
Claim 5
Dependent Claim
20 words
A process according to claim 1, wherein the premix is preplasticized for 3 to 5 minutes in the kneading device.
Claim 6
Dependent Claim
29 words
A process according to claim 1, wherein the powder mixture, after preplasticizing in the kneading device, is allowed to mature for about 24 hours and is only thereafter extruded.
Claim 7
Dependent Claim
22 words
A process according to claim 1, wherein a premix for a single-base propellant powder is produced and this premix is further processed.
Claim 8
Dependent Claim
31 words
A process according to claim 1, wherein a premix for a triple-base propellant powder with up to 5% by weight of nitroguanidine is produced and this premix is then further processed.
Claim 9
Dependent Claim
29 words
A process according to claim 1, wherein a premix for a triple-base propellant powder with 50-60% by weight of nitroguanidine is produced and this premix is then further processed.
Claim 10
Dependent Claim
28 words
A process according to claim 1 wherein the alcohol-containing nitrocellulose is mixed with the required components under the addition of 10-25% by weight of a readily volatile solvent.
Claim 11
Dependent Claim
11 words
A process according to claim 9, wherein the solvent is acetone.
Claim 12
Dependent Claim
33 words
A process according to claim 8, wherein an aqueous raw powder mixture is utilized, the water is removed therefrom by drying, and the mixture is combined with a readily volatile solvent, preferably acetone.
Claim 13
Dependent Claim
11 words
A process according to claim 11, wherein the solvent is acetone.
Claim 14
Dependent Claim
22 words
A process according to claim 11, wherein the water is removed by drying the raw powder mixture at 40° to 60° C.
Claim 15
Dependent Claim
34 words
A process according to claim 1, wherein an aqueous raw mixture is utilized and after premixing said mixture is initially dried and then the solvent is incorporated and the homogenizing and preplasticizing are effected.
References Cited (Backward Citations)
US3928514A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-09-26 | 1981-03-28 | 1981-09-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-09-26 | 1985-03-28 | 1985-09-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-09-26 | 1989-03-28 | 1989-09-27 | $7700.00 | Window Closed / Lapsed |