Abstract
Abstract A water dispersion varnish suitable for electrodepositon is prepared by a process comprising reacting: The reaction product of A. a polyesterimide having a carboxyl group in its chain or at the terminus of the chain and having an ester group and an imide group in its repeating unit or a polyesteramideimide having a carboxyl group in its chain or at the terminus of the chain and having an ester group, an imide group and an amide group in its repeating unit and B. an organic compound having at least two hydroxyl groups with C. a polybasic acid or its anhydride in the presence or absence of a solvent yielding a modified polyesterimide or polyesteramideimide; Dissolving said modified polyesterimide or polyesteramideimide in an organic solvent; Dispersing said modified polyesterimide or polyesteramideimide solution in an aqueous solution containing a surfactant and a volatile base; and removing the volatile components.
Inventors
- 👤 Kyoichi Shibayama
- 👤 Hiroshi Ono
- 👤 Eiki Jidai
- 👤 Akira Fujii
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 11:29
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/02; C08J3/03; C08J3/07; C09; C09D; C09D5/00; C09D5/44; C09D5/4419; C08J2379/00; C08J2379/04; C08J2379/08
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
199 words
A process for preparing a water-dispersion varnish suitable for electrodeposition which comprises reacting The reaction product of A. a polyesterimide having a carboxyl group in its chain or at the terminus of the chain and having an ester group and an imide group in its repeating unit or a polyesteramideimide having a carboxyl group in its chain or at the terminus of the chain and having an ester group, an imide group and an amide group in its repeating unit and B. an organic compound having at least two hydroxyl groups with C. a polybasic acid or its anhydride in the presence or absence of a solvent yielding a modified polyesterimide or polyesteramideimide having a molecular weight of from 5,000-100,000 and an acid value of 10-100; dissolving said modified polyesterimide or polyesteramideimide in an organic solvent; dispersing said modified polyesterimide or polyesteramideimide solution in an aqueous solution containing a surfactant and a volatile base; and forming a water dispersion of said modified polyesterimide or polyester amideimide by passing or bubbling an inert gas through the dispersion of said modified polyesterimide or polyester amideimide solution and said aqueous solution to remove all or part of said solvent and volatile base.
Claim 2
Dependent Claim
199 words
A process for preparing a water-dispersion varnish suitable for electrodeposition which comprises reacting The reaction product of A. a polyesterimide having a carboxyl group in its chain or at the terminus of the chain and having an ester group and an imide group in its repeating unit or a polyesteramideimide having a carboxyl group in its chain or at the terminus of the chain and having an ester group, an imide group and an amide group in its repeating unit and B. an organic compound having at least two hydroxyl groups with C. a polybasic acid or its anhydride in the presence or absence of a solvent yielding a modified polyesterimide or polyesteramideimide having a molecular weight of from 5,000-100,000 and an acid value of 10-100; dissolving said modified polyesterimide or polyesteramideimide in an organic solvent; dispersing said modified polyesterimide or polyesteramideimide solution in an aqueous solution containing a surfactant and a volatile base; and forming a water dispersion of said modified polyesterimide or polyester amideimide by passing or bubbling an inert gas through the dispersion of said modified polyesterimide or polyester amideimide solution and said aqueous solution to remove all or part of said solvent and volatile base.
Claim 3
Dependent Claim
76 words
The process for preparing a water-dispersion varnish according to claim 1, wherein said polyesterimide is produced by polymerizing 9-49 equivalent % of a dibasic acid, 5-40 equivalent % of a polycarboxylic anhydride having at least 3 carboxyl groups, 16-48 equivalent % of a monobasic lower aliphatic diester of an aromatic dicarboxylic acid, 0-40 equivalent % of a polyol having at least 2 hydroxyl groups and 2.5.60 equivalent % of an amino compound having two amino groups.
Claim 4
Dependent Claim
68 words
The process for preparing a water-dispersion varnish according to claim 1, wherein said polyesteramideimide is produced by polymerizing 20-60 equivalent % of polycarboxylic anhydride having at least 3 carboxyl groups, 10-30 equivalent % of diisocyanate, 15-50 equivalent % of a monobasic lower aliphatic diester of an aromatic dicarboxylic acid, 0-40 equivalent % of a polyvalent alcohol and 3-60 equivalent % of an amino compound having two amino groups.
Claim 5
Dependent Claim
66 words
The process for preparing a water-dispersion varnish according to claim 1, wherein said organic compound having at least two hydroxyl groups is glycol, such as ethylene glycol, propylene glycol, diethylene glycol, glycerine, tris (β-hydroxyethyl)-isocyanurate, a polyalcohol or a polyester having free hydroxyl groups, and said polybasic acid or anhydride is tetrahydrophthalic acid, adipic acid, terephthalic acid, trimellitic acid, maleic acid, isophthalic acid or an anhydride thereof.
Claim 6
Dependent Claim
28 words
The process for preparing a water-dispersion varnish according to claim 1, wherein said solvent is ethylenedichloride, dioxane, methylethylketone, acetone, m-cresol, dimethyl formamide, N-methylpyrrolidone, dimethyl acetamide or dimethyl sulfoxide.
Claim 7
Dependent Claim
21 words
The process for preparing a water-dispersion varnish according to claim 1, wherein the volatile base is ammonia, trimethylamine, monoethanolamine or α-dimethylaminoethanolamine.
Claim 8
Dependent Claim
200 words
A water-dispersion varnish which is suitable for use in electrodeposition which is formed by reacting the reaction product of A. a polyesterimide having a carboxyl group in its chain or at the terminus of the chain and having an ester group and an imide group in its repeating unit or a polyesteramideimide having a carboxyl group in its chain or at the terminus of the chain and having an ester goup, an imide group and an amide group in its repeating unit, and B. an organic compound having at least two hydroxyl groups with C. a polybasic acid or its anhydride in the presence or absence of a solvent yielding a modified polyesterimide or polyesteramideimide having a molecular weight of from 5,000-100,000 and an acid value of 10-100; dissolving said modified polyesterimide or polyesteramideimide in an organic solvent; dispersing said modified polyesterimide or polyesteramideimide solution in an aqueous solution containing a surfactant and a volatile base; and forming a water dispersion of said modified polyesterimide or polyester amideimide by passing or bubbling an inert gas through the dispersion of said modified polyesterimide or polyesteramideimide solution and said aqueous solution to remove at least part of said solvent and volatile base.
Claim 9
Dependent Claim
200 words
A water-dispersion varnish which is suitable for use in electrodeposition which is formed by reacting the reaction product of A. a polyesterimide having a carboxyl group in its chain or at the terminus of the chain and having an ester group and an imide group in its repeating unit or a polyesteramideimide having a carboxyl group in its chain or at the terminus of the chain and having an ester goup, an imide group and an amide group in its repeating unit, and B. an organic compound having at least two hydroxyl groups with C. a polybasic acid or its anhydride in the presence or absence of a solvent yielding a modified polyesterimide or polyesteramideimide having a molecular weight of from 5,000-100,000 and an acid value of 10-100; dissolving said modified polyesterimide or polyesteramideimide in an organic solvent; dispersing said modified polyesterimide or polyesteramideimide solution in an aqueous solution containing a surfactant and a volatile base; and forming a water dispersion of said modified polyesterimide or polyester amideimide by passing or bubbling an inert gas through the dispersion of said modified polyesterimide or polyesteramideimide solution and said aqueous solution to remove at least part of said solvent and volatile base.
Claim 10
Dependent Claim
69 words
The varnish of claim 7, wherein said polyesterimide is produced by polymerizing 9-49 equivalent % of a dibasic acid, 5-40 equivalent % of a polycarboxylic anhydride having at least 3 carboxyl groups, 16-48 equivalent % of a monobasic lower aliphatic diester of an aromatic dicarboxylic acid, 0-40 equivalent % of a polyol having at least 2 hydroxyl groups and2.5-60 equivalent % of an amino compound having two amino groups.
Claim 11
Dependent Claim
62 words
The varnish of claim 7, wherein said polyesteramideimide is produced by polymerizing 20-60 equivalent % of polycarboxylic anhydride having at least 3 carboxyl groups, 10-30 equivalent % of diisocyanate, 15-50 equivalent % of a monobasic lower aliphatic diester of an aromatic dicarboxylic acid, 0-40 equivalent % of a polyvalent alcohol and 3-60 equivalent % of an amino compound having two amino groups.
Claim 12
Dependent Claim
60 words
The varnish of claim 7, wherein said organic compound having at least two hydroxyl groups is glycol, such as ethylene glycol, propylene glycol, diethylene glycol, glycerine, tris (β-hydroxyethyl)-isocyanurate, a polyalcohol or a polyester having free hydroxyl groups, and said polybasic acid or anhydride is tetrahydrophthalic acid, adipic acid, terephthalic acid, trimellitic acid, maleic acid, isophthalic acid or an anhydride thereof.
References Cited (Backward Citations)
DE1036426B
Cited
US3007852A
Cited
US3230162A
Cited
US3860546A
Cited
US3448017A
Cited
US3444066A
Cited
US3533998A
Cited
US3475282A
Cited
US3766117A
Cited
US3663402A
Cited
US3787338A
Cited
US3846269A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-09-26 | 1981-03-28 | 1981-09-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-09-26 | 1985-03-28 | 1985-09-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-09-26 | 1989-03-28 | 1989-09-27 | $7700.00 | Window Closed / Lapsed |