Corrosion-inhibiting rubber and methods of preparation
Assignee: Northern Instruments Corp
•
Filing: 1975-01-13
•
Granted: 1977-09-27
•
Expires: 1995-01-13
Abstract
Abstract The disclosed corrosion-inhibiting elastomers are typically made by milling the corrosion inhibitor into a solid rubber matrix. Preferred corrosion inhibitors include the aromatic carboxylates of primary, secondary or tertiary amines. Chromates and 2-ethylhexanoates can also be used. Organic ammonium nitrites are effective against some types of corrosion, but should be used with relatively inert elastomers. There appears to be synergistic cooperation between the elastomeric molecular structure and the corrosion inhibitor resulting in unusually effective protection of ferrous and/or nonferrous metals adjacent to rubber parts made from the corrosion-inhibiting elastomer.
Inventors
- 👤 Boris A. Miksic
- 👤 Donovan P. Stern
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 19:27
CPC Classifications
C; C08; C08K; C08K5/00; C08K5/16; C08K5/34; C08K5/3412; C08J; C08J9/00; C08J9/0014; C08J9/0028; C08K5/04; C08K5/09; C08K5/17; C08K5/19
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
29 words
A solid, corrosion-inhibiting elastomer containing a non-cellular or intercellular elastomeric matrix, said elastomeric matrix containing a corrosion-inhibiting amount of the corrosion-inhibiting compound cyclohexamethyleneimine dinitrobenzoate distributed through said elastomeric matrix.
Claim 2
Dependent Claim
29 words
A solid, corrosion-inhibiting elastomer containing a non-cellular or intercellular elastomeric matrix, said elastomeric matrix containing a corrosion-inhibiting amount of the corrosion-inhibiting compound cyclohexamethyleneimine dinitrobenzoate distributed through said elastomeric matrix.
Claim 3
Dependent Claim
48 words
A solid elastomer according to claim 1 in which at least a second corrosion-inhibiting compound other than cyclohexamethyleneimine dinitrobenzoate is distributed through said elastomeric matrix, said second compound having a vapor pressure at normal ambient temperatures which is less than about 3 × 10 -2 mm of mercury.
Claim 4
Dependent Claim
42 words
A solid elastomer according to claim 2 wherein said second corrosion-inhibiting compound is selected from the group consisting of: an aromatic carboxylate of a primary, secondary, or tertiary amine; a salt of chromic acid; a salt of nitrous acid; and combinations thereof.
Claim 5
Dependent Claim
153 words
A solid elastomer according to claim 3 wherein: said aromatic carboxylate has the following formula: ArCOOHNR.sup.1 R.sup.2 R.sup.3, wherein Ar represents an aromatic moiety, R 1 and R 2 represent hydrogen or an aliphatic, cycloaliphatic, or heterocylic radical, R 3 represents an aliphatic, cycloaliphatic, or heterocyclic radical, and R 3 taken together with R 1 or R 2 and the nitrogen atom represents a heterocyclo-aliphatic secondary or tertiary amino group; said salt of chromic acid is an organic ammonium chromate which is the salt of chromic acid and the compound NR 1 R 2 R 3 , wherein R 1 , R 2 , and R 3 are as defined previously; and said salt of nitrous acid is an organic ammonium nitrite which is the salt of nitrous acid and the compound NR 1 R 2 R 3 , wherein R 1 , R 2 , and R 3 are as defined previously.
Claim 6
Dependent Claim
26 words
A solid elastomer according to claim 4 wherein R 1 and R 2 represent hydrogen or a cycloaliphatic radical and R 3 represents a cycloaliphatic radical.
Claim 7
Dependent Claim
21 words
A solid elastomer according to claim 3 wherein the aromatic carboxylate is obtained from benzoic acid and monocyclohexyl or dicyclohexyl amine.
Claim 8
Dependent Claim
36 words
A solid elastomer according to claim 3 wherein said aromatic carboxylate is selected from the group consisting of a non-nitrated benzoate and a mono-nitrobenzoate of a heterocycloaliphatic amine, and mixtures of said non-nitrated benzoate and mono-nitrobenzoate.
Claim 9
Dependent Claim
13 words
A solid elastomer according to claim 7 wherein said heterocyclo-aliphatic amine is cyclohexamethyleneimine.
Claim 10
Dependent Claim
32 words
A solid elastomer according to claim 1 wherein said elastomer is non-cellular and said aromatic carboxylate is in the form of a finely divided anhydrous solid phase mechanically dispersed through said elastomer.
Claim 11
Dependent Claim
16 words
A solid elastomer according to claim 9 wherein said corrosion inhibiting amount is 0.1-30% by weight.
Claim 12
Dependent Claim
33 words
A solid elastomer according to claim 9 wherein said elastomer is a molded elastomeric part for an apparatus containing metal parts and wherein said corrosion inhibiting amount is less than 10% by weight.
Claim 13
Dependent Claim
23 words
A solid elastomer according to claim 11 wherein said elastomer is a masterbatch compound containing more than 5% by weight of said inhibitor.
Claim 14
Dependent Claim
89 words
A metal substrate coated with a layer of corrosion-inhibiting elastomer, said layer comprising at least two laminae: a. a first lamina, directly in adherent interfacial contact with said metal substrate, said lamina comprising a non-cellular elastomer having 0.1-30% by weight of cyclohexamethyleneimine dinitrobenzoate dispersed therethrough; b. a second lamina, in interfacial contact with said first lamina, said second lamina comprising a non-cellular elastomer having an amount exceeding 0.5% by weight of cyclohexamethyleneimine dinitrobenzoate dispersed therethrough, said amount being less than the amount of cyclohexamethyleneimine dinitrobenzoate in said lamina (a).
Claim 15
Dependent Claim
89 words
A metal substrate coated with a layer of corrosion-inhibiting elastomer, said layer comprising at least two laminae: a. a first lamina, directly in adherent interfacial contact with said metal substrate, said lamina comprising a non-cellular elastomer having 0.1-30% by weight of cyclohexamethyleneimine dinitrobenzoate dispersed therethrough; b. a second lamina, in interfacial contact with said first lamina, said second lamina comprising a non-cellular elastomer having an amount exceeding 0.5% by weight of cyclohexamethyleneimine dinitrobenzoate dispersed therethrough, said amount being less than the amount of cyclohexamethyleneimine dinitrobenzoate in said lamina (a).
Claim 16
Dependent Claim
88 words
A method for making the corrosion-inhibiting elastomer of claim 1 comprising the steps of: a. providing about 0.1 to 45 parts by weight of substantially anhydrous cyclohexamethylenimine dinitrobenzoate; b. dispersing said cyclohexamethyleneimine dinitrobenzoate in said substantially anhydrous form into a non-cellular substantially anhydrous mass of solid elastomer by milling of said substantially anhydrous mass in the presence of said cyclohexamethyleneimine dinitrobenzoate, the amount of said non-cellular substantially anhydrous mass of solid elastomer being no more than 100 parts by weight per amount by weight of said cyclohexamethyleneimine dinitrobenzoate.
Claim 17
Dependent Claim
34 words
A corrosion inhibiting composition comprising: 0.15-4 parts by weight of cyclohexamethyleneimine 3,5-dinitrobenzoate and 0.15-4 parts by weight of at least one of the following corrosion inhibiting compounds in combination therewith: cyclohexamethyleneimine mononitrobenzoate cyclohexamethyleneimine benzoate.
Claim 18
Dependent Claim
34 words
A corrosion inhibiting composition comprising: 0.15-4 parts by weight of cyclohexamethyleneimine 3,5-dinitrobenzoate and 0.15-4 parts by weight of at least one of the following corrosion inhibiting compounds in combination therewith: cyclohexamethyleneimine mononitrobenzoate cyclohexamethyleneimine benzoate.
Claim 19
Dependent Claim
43 words
A corrosion inhibiting composition comprising, in combination: a. cyclohexamethyleneimine 3,5-dinitrobenzoate; b. at least one additional compound selected from the group consisting of: an aromatic carboxylate of a primary, secondary, or tertiary amine; a salt of chromic acid; and a salt of nitrous acid.
Claim 20
Dependent Claim
43 words
A corrosion inhibiting composition comprising, in combination: a. cyclohexamethyleneimine 3,5-dinitrobenzoate; b. at least one additional compound selected from the group consisting of: an aromatic carboxylate of a primary, secondary, or tertiary amine; a salt of chromic acid; and a salt of nitrous acid.
Claim 21
Dependent Claim
154 words
A corrosion inhibiting composition according to claim 16 wherein: said aromatic carboxylate has the following formula: ArCOOHNR.sup.1 R.sup.2 R.sup.3, wherein Ar represents an aromatic moiety, R 1 and R 2 represent hydrogen or an aliphatic, cycloaliphatic, or heterocyclic radical, R 3 represents an aliphatic, cycloaliphatic, or heterocyclic radical, and R 3 taken together with R 1 or R 2 and the nitrogen atom represents a heterocyclo-aliphatic secondary or tertiary amino group; said salt of chromic acid is an organic ammonium chromate which is the salt of chromic acid and the compound NR 1 R 2 R 3 , wherein R 1 , R 2 , and R 3 are as defined previously; and said salt of nitrous acid is an organic ammonium nitrite which is the salt of nitrous acid and the compound NR 1 R 2 R 3 , wherein R 1 , R 2 , and R 3 are as defined previously.
Claim 22
Dependent Claim
20 words
A corrosion-inhibiting composition according to claim 16 wherein 0.1-30% by weight of said composition is distributed through a polymer matrix.
Claim 23
Dependent Claim
27 words
A corrosion-inhibiting composition according to claim 16 wherein the amounts of said components (a) and (b) are 0.75-4 parts by weight and 0.15-1.5 parts by weight, respectively.
Claim 24
Dependent Claim
12 words
A coated substrate wherein the coating comprises the composition of claim 16.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-09-26 | 1981-03-28 | 1981-09-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-09-26 | 1985-03-28 | 1985-09-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-09-26 | 1989-03-28 | 1989-09-27 | $7700.00 | Window Closed / Lapsed |