Method of producing polycrystalline diamonds
Assignee: Individual
•
Filing: 1973-01-02
•
Granted: 1977-09-20
•
Expires: 1993-01-02
Abstract
Abstract A method of producing polycrystalline diamonds which is characterized by providing a thermal contact of the reaction chamber with the cooled members of the device developing a high pressure and high temperatures for removing the heat generated within this chamber in the process of crystallization of a diamond, which method is also characterized in that the cross-sectional area of the metal-catalyst is not more than 0.04 that of the reaction chamber in a plane normal to the direction of the maximum withdrawal of the heat of crystallization. Said metal-catalyst is set in the carbon-containing material substantially in the center of the reaction chamber.
Inventors
- 👤 Leonid Fedorovich Vereschagin
- 👤 Evgeny Nikolaevich Yakovlev
- 👤 Tatyana Dmitrievna Varfolomeeva
- 👤 Alexandr Yakovlevich Preobrazhensky
- 👤 Vladislav Nikolaevich Slesarev
- 👤 Vasily Alexandrovich Stepanov
- 👤 Ljudmila Efimovna Shterenberg
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 16:35
CPC Classifications
B; B01; B01J; B01J3/00; B01J3/06; B01J3/062; B01J2203/00; B01J2203/06; B01J2203/0605; B01J2203/062; B01J2203/065; B01J2203/0655; B01J2203/0675; B01J2203/0685
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
173 words
A method for producing polycrystalline diamonds which comprises: filling a reaction chamber of a device for developing high pressure and high temperatures and having cooled portions with a carbon material; subjecting the carbon material in the presence of a metal catalyst to the simultaneous action of high pressures of at least 80 kbar and diamond synthesizing temperatures of at least about 1,200° C. and approaching the minimum temperature of diamond synthesis with the given metal catalyst for a period of time sufficient to obtain diamond crystallization; maintaining said reaction chamber in thermal contact with said cooled portions so as to effect removal of heat developed therein in the course of diamond crystallization at a rate of not less than 25 cal/min, said metal catalyst having a cross-sectional area of not more than 0.04 of the area of transverse section of said reaction chamber and being positioned in the carbon material substantially in the center of said reaction chamber, so as to ensure the growth of polycrystalline fine-grain diamond sample containing mutually intergrown crystallites.
Claim 2
Independent Claim
173 words
A method for producing polycrystalline diamonds which comprises: filling a reaction chamber of a device for developing high pressure and high temperatures and having cooled portions with a carbon material; subjecting the carbon material in the presence of a metal catalyst to the simultaneous action of high pressures of at least 80 kbar and diamond synthesizing temperatures of at least about 1,200° C. and approaching the minimum temperature of diamond synthesis with the given metal catalyst for a period of time sufficient to obtain diamond crystallization; maintaining said reaction chamber in thermal contact with said cooled portions so as to effect removal of heat developed therein in the course of diamond crystallization at a rate of not less than 25 cal/min, said metal catalyst having a cross-sectional area of not more than 0.04 of the area of transverse section of said reaction chamber and being positioned in the carbon material substantially in the center of said reaction chamber, so as to ensure the growth of polycrystalline fine-grain diamond sample containing mutually intergrown crystallites.
Claim 3
Dependent Claim
43 words
The method of claim 1, wherein said thermal contact of the reaction chamber with the cooled portions of said device is effected through a material whose heat conductivity is not lower than the heat conductivity of graphite at said high pressures and temperatures.
Claim 4
Dependent Claim
32 words
The method of claim 2, wherein the material, through which thermal contact is effected between the reaction chamber and the cooled portions of the high pressure and high temperature device, is graphite.
Claim 5
Dependent Claim
33 words
The method of claim 2, wherein the material through which thermal contact is effected between the reaction chamber and the cooled portions of the high pressure and high temperature device, is boron nitride.
Claim 6
Dependent Claim
33 words
The method of claim 2, wherein the material, through which thermal contact is effected between the reaction chamber and the cooled portions of the high pressure and high temperature device, is boron carbonitride.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-09-19 | 1981-03-21 | 1981-09-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-09-19 | 1985-03-21 | 1985-09-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-09-19 | 1989-03-21 | 1989-09-20 | $7700.00 | Window Closed / Lapsed |