US4049764A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of forming highly absorbent filaments and webs having improved softness, wicking, and solvent drying characteristics
Assignee: Kimberly Clark Corp
•
Filing: 1975-04-02
•
Granted: 1977-09-20
•
Expires: 1995-04-02
Abstract
Abstract In the formation of highly absorbent and rapidly wicking filaments and web structures by extrusion and solvent drying of extrudates composed of highly swollen hydrophilic chemically modified cellulose fibers, improved results are obtained in the form of a softer and better wicking product by treatment of the extrudate prior to extrusion. The extrudate is a mass containing the swollen chemically modified cellulose fibers and a water content of up to 98% at the time of extrusion. By adding to the extrudate, prior to extrusion, an amount of from about 2 to 50% of the solvent to be used in drying in the form of pure solvent or in the form of a mixture containing solvent but which may contain water or other non-solvent and the solvent to be used in drying, a much better performing extrudate is produced which results in better filament formation, improved bonding between filaments, lower water content in the extrudate, faster drying of the extruded product, and a softer, better wicking product.
Inventors
- 👤 Wayne C. Sigl
- 👤 Frederick O. Lassen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 14:43
CPC Classifications
A; A61; A61L; A61L15/00; A61L15/16; A61L15/22; A61L15/28
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
107 words
In a method of producing filaments and webs of cellulose fibers, which have been transformed by derivitization to increase their hydrophilic character, by extrusion of said fibers from a plasticized fibrous extrudable mass including a swelling medium and solvent drying to remove the swelling medium, the improvement wherein about 2 to 50% of a polar solvent in the form of pure solvent for the swelling medium being removed by drying or a mixture containing the solvent and up to 90% of a non-solvent by volume is added to said extrudable mass and mixed for a period of from about three to about ten minutes prior to extrusion.
Claim 2
Dependent Claim
107 words
In a method of producing filaments and webs of cellulose fibers, which have been transformed by derivitization to increase their hydrophilic character, by extrusion of said fibers from a plasticized fibrous extrudable mass including a swelling medium and solvent drying to remove the swelling medium, the improvement wherein about 2 to 50% of a polar solvent in the form of pure solvent for the swelling medium being removed by drying or a mixture containing the solvent and up to 90% of a non-solvent by volume is added to said extrudable mass and mixed for a period of from about three to about ten minutes prior to extrusion.
Claim 3
Dependent Claim
13 words
The method of claim 1 wherein said fibers are fibers of phosphorylated cellulose.
Claim 4
Dependent Claim
18 words
The method of claim 2 wherein said solvent is acetone and the same solvent is used for drying.
Claim 5
Dependent Claim
34 words
The method of claim 1 wherein said extrudable mass includes water and has a consistency 1 to 6% lower than the extrusion consistency and wherein said solvent is a polar solvent soluble in water.
Claim 6
Independent Claim
131 words
A method of producing highly absorbent, rapid wicking filaments and webs including the steps of, 1. chemically modifying cellulose fibers of paper-making size by a. chemical substitution, etherization, esterification; b. chemical substitution plus crosslinking; or c. polymeric grafting, 2. forming an extrudable mass of said chemically modified cellulose fibers by adding water until said fibers are plasticized and independently mobile, 3. adding to said extrudable mass a polar solvent or solvent mixture which is soluble in water, in an amount of from 2 to 50% of the weight of water to be removed in drying; 4. mechanically mixing said solvent and extrudable mass for a period of from about 3 to 10 minutes; and 5. extruding said extrudable mass as filaments into a drying bath containing the remainder of said solvent.
Claim 7
Independent Claim
131 words
A method of producing highly absorbent, rapid wicking filaments and webs including the steps of, 1. chemically modifying cellulose fibers of paper-making size by a. chemical substitution, etherization, esterification; b. chemical substitution plus crosslinking; or c. polymeric grafting, 2. forming an extrudable mass of said chemically modified cellulose fibers by adding water until said fibers are plasticized and independently mobile, 3. adding to said extrudable mass a polar solvent or solvent mixture which is soluble in water, in an amount of from 2 to 50% of the weight of water to be removed in drying; 4. mechanically mixing said solvent and extrudable mass for a period of from about 3 to 10 minutes; and 5. extruding said extrudable mass as filaments into a drying bath containing the remainder of said solvent.
Claim 8
Dependent Claim
19 words
The method of claim 5 including the additional step of collecting said extruded filaments to form a bonded web.
Claim 9
Dependent Claim
26 words
The method of claim 5 wherein said chemically treated fibers are phosphorylated cellulose and said solvent is acetone which is also used as the drying solvent.
References Cited (Backward Citations)
US1896725A
Cited
US3366582A
Cited
US3482011A
Cited
US3565886A
Cited
US3785918A
Cited
US3658790A
Cited
US3691154A
Cited
US3739782A
Cited
US3914354A
Cited
US3740940A
Cited
US3952081A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-09-19 | 1981-03-21 | 1981-09-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-09-19 | 1985-03-21 | 1985-09-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-09-19 | 1989-03-21 | 1989-09-20 | $7700.00 | Window Closed / Lapsed |