High strength ferritic alloy
Assignee: Energy Research and Development Administration ERDA
•
Filing: 1976-09-30
•
Granted: 1977-09-20
•
Expires: 1996-09-30
Abstract
Abstract A high-strength ferritic alloy useful for fast reactor duct and cladding applications where an iron base contains from about 9% to about 13% by weight chromium, from about 4% to about 8% by weight molybdenum, from about 0.2% to about 0.8% by weight niobium, from about 0.1% to about 0.3% by weight vanadium, from about 0.2% to about 0.8% by weight silicon, from about 0.2% to about 0.8% by weight manganese, a maximum of about 0.05% by weight nitrogen, a maximum of about 0.02% by weight sulfur, a maximum of about 0.02% by weight phosphorous, and from about 0.04% to about 0.12% by weight carbon.
Inventors
- 👤 William C. Hagel
- 👤 Frederick A. Smidt
- 👤 Michael K. Korenko
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 06:01
CPC Classifications
C; C22; C22C; C22C38/00; C22C38/18; C22C38/26; Y; Y10; Y10S; Y10S376/00; Y10S376/90
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
150 words
A high strength ferritic alloy having Laves phase precipitation as the primary ferritic alloy strengthener consisting essentially of from about 9% to about 13% by weight chromium, from about 4% to about 8% by weight molybdenum, from about 0.2% to about 0.8% by weight niobium, from about 0.1% to about 0.3% by weight vanadium, from about 0.2% to about 0.8% by weight silicon, from about 0.2% to about 0.8% by weight manganese, from 0.04% to about 0.12% by weight carbon, a maximum of about 0.05% by weight nitrogen, a maximum of about 0.02% by weight sulfur, a maximum of about 0.02% by weight phosphorus, and the balance iron, wherein said alloy will swell less than 5% at the fluence of 2.2 × 10 23 n/cm 2 (E > 0.1 MeV) and wherein said alloy exhibits 100 hour stress rupture strength in the range of about 30 ksi at 650° C.
Claim 2
Dependent Claim
150 words
A high strength ferritic alloy having Laves phase precipitation as the primary ferritic alloy strengthener consisting essentially of from about 9% to about 13% by weight chromium, from about 4% to about 8% by weight molybdenum, from about 0.2% to about 0.8% by weight niobium, from about 0.1% to about 0.3% by weight vanadium, from about 0.2% to about 0.8% by weight silicon, from about 0.2% to about 0.8% by weight manganese, from 0.04% to about 0.12% by weight carbon, a maximum of about 0.05% by weight nitrogen, a maximum of about 0.02% by weight sulfur, a maximum of about 0.02% by weight phosphorus, and the balance iron, wherein said alloy will swell less than 5% at the fluence of 2.2 × 10 23 n/cm 2 (E > 0.1 MeV) and wherein said alloy exhibits 100 hour stress rupture strength in the range of about 30 ksi at 650° C.
Claim 3
Dependent Claim
133 words
The alloy of claim 1 consisting essentially of from about 9.5% to about 11.5% by weight chromium, from about 5.5% to about 6.5% by weight molybdenum, from about 0.3% to about 0.6% by weight niobium, from about 0.1% to about 0.3% by weight vanadium, from about 0.2% to about 0.5% by weight silicon, from about 0.3% to about 0.6% by weight manganese, from about 0.04% to about 0.07% by weight carbon, and the balance iron, and the maximum swelling rate of said alloy at the peak ion irradiation swelling temperature of about 500° C. is 0.0062% per dpa (iron ion) as determined at 250 dpa using 2.8 MeV iron ion irradiation, and the maximum iron irradiation swelling rate of said alloy at peak swelling temperature of about 550° C. is 0.564% dpa (electron).
Claim 4
Dependent Claim
48 words
The alloy of claim 1 consisting essentially of about 10.5% by weight chromium, about 6.0% by weight molybdenum, about 0.5% by weight niobium, about 0.3% by weight vanadium, about 0.3% by weight silicon, about 0.4% by weight manganese, and about 0.05% by weight carbon, and the balance iron.
References Cited (Backward Citations)
US2848323A
Cited
US3663208A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-09-19 | 1981-03-21 | 1981-09-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-09-19 | 1985-03-21 | 1985-09-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-09-19 | 1989-03-21 | 1989-09-20 | $7700.00 | Window Closed / Lapsed |