Copper-base alloys containing chromium, niobium and zirconium

Claim 2

A copper base alloy which exhibits a combination of high strength and high electrical conductivity, said alloy consisting essentially of 0.05 to 1.25% by weight chromium, 0.05 to 1.0% by weight zirconium, 0.05 to 1.5% by weight niobium, balance copper.

Claim 3

A process for improving both the strength and electrical conductivity properties of copper base alloys, which comprises: a. casting a copper base alloy consisting essentially of 0.05 to 1.25% by weight chromium, 0.05 to 1.0% by weight zirconium, 0.05 to 1.5% by weight niobium, balance copper; b. hot working the alloy at a starting temperature of 950°-1000° C to effect the maximum solid solution of all alloying elements; c. rapidly cooling the alloy to maintain said maximum solid solution of all alloying elements; d. cold working the alloy to a total reduction of at least 60%; and e. aging said alloy at 400°-500° C for one to 24 hours.

Claim 4

A process for improving both the strength and electrical conductivity properties of copper base alloys, which comprises: a. casting a copper base alloy consisting essentially of 0.05 to 1.25% by weight chromium, 0.05 to 1.0% by weight zirconium, 0.05 to 1.5% by weight niobium, balance copper; b. hot working the alloy at a starting temperature of 950°-1000° C to effect the maximum solid solution of all alloying elements; c. rapidly cooling the alloy to maintain said maximum solid solution of all alloying elements; d. cold working the alloy to a total reduction of at least 60%; and e. aging said alloy at 400°-500° C for one to 24 hours.

Claim 5

A process for improving both the strength and electrical conductivity properties of copper base alloys, which comprises: a. casting a copper base alloy consisting essentially 0.05 to 1.25% by weight chromium, 0.05 to 1.0% by weight zirconium, 0.05 to 1.5% by weight niobium, balance copper; b. hot working the alloy at a starting temperature of 850°-950° C; c. solution annealing the worked alloy at a solutionizing temperature of 950°-1000° C, for a period of time sufficient to insure the maximum solid solution of all alloying elements; d. rapidly cooling the alloy to maintain said maximum solid solution of all alloying elements; e. cold working the alloy to a total reduction of at least 60%; and f. aging said alloy at 400°-500° C for one to 24 hours.

Claim 6

A process for improving both the strength and electrical conductivity properties of copper base alloys, which comprises: a. casting a copper base alloy consisting essentially 0.05 to 1.25% by weight chromium, 0.05 to 1.0% by weight zirconium, 0.05 to 1.5% by weight niobium, balance copper; b. hot working the alloy at a starting temperature of 850°-950° C; c. solution annealing the worked alloy at a solutionizing temperature of 950°-1000° C, for a period of time sufficient to insure the maximum solid solution of all alloying elements; d. rapidly cooling the alloy to maintain said maximum solid solution of all alloying elements; e. cold working the alloy to a total reduction of at least 60%; and f. aging said alloy at 400°-500° C for one to 24 hours.

Claim 7

A process as in claim 2 wherein said aging step is accomplished in cycles with said cold working, where the cycles end with either an aging or a cold working step.

Claim 8

A process as in claim 2 wherein the alloy is cast at a temperature which ranges between 25° C above the melting point of the alloy up to 1300° C.

Claim 9

A process as in claim 2 wherein said rapid cooling is sufficient to cool the alloy to at least 350° C.

Claim 10

A process as in claim 3 wherein said aging step is accomplished in cycles with said cold working, where the cycles end with either an aging or a cold working step.

Claim 11

A process as in claim 2 wherein the hot working occurs at a temperature of 975°-1000° C.

Claim 12

A process as in claim 3 wherein the solutionizing temperature is 975°-1000° C.

Claim 13

A process as in claim 3 wherein the alloy is cast at a temperature which ranges between 25° C above the melting point of the alloy up to 1300° C.

Claim 14

A process as in claim 3 wherein said rapid cooling is sufficient to cool the alloy to at least 350° C.

Claim 15

A wrought copper base alloy in the worked and aged condition having high strength and high electrical conductivity properties, said wrought alloy consisting essentially of 0.05 to 1.25% by weight chromium, 0.05 to 1.0% by weight zirconium, 0.05 to 1.5% by weight niobium, balance copper.

Claim 16

A wrought copper base alloy in the worked and aged condition having high strength and high electrical conductivity properties, said wrought alloy consisting essentially of 0.05 to 1.25% by weight chromium, 0.05 to 1.0% by weight zirconium, 0.05 to 1.5% by weight niobium, balance copper.

Claim 17

An alloy as in claim 1 wherein said alloy consists essentially of 0.5 to 1.0% by weight chromium, 0.1 to 0.4% by weight zirconium, 0.1 to 0.4% by weight niobium, balance copper.

Claim 18

An alloy as in claim 1 wherein a small but effective amount of an element selected from the group consisting of arsenic, magnesium, cobalt, boron, calcium, cadmium and mischmetal is added to said alloy.

Claim 19

A process as in claim 2 wherein said alloy consists essentially of 0.5 to 1.0% by weight chromium, 0.1 to 0.4% by weight zirconium, 0.1 to 0.4% by weight niobium, balance copper.

Claim 20

A process as in claim 2 wherein a small but effective amount of an element selected from the group consisting of arsenic, magnesium, cobalt, boron, calcium, cadmium and mischmetal is added to said alloy of step (a).

Claim 21

A wrought alloy as in claim 12 wherein said alloy consists essentially of 0.5 to 1.0% by weight chromium, 0.1 to 0.4% by weight zirconium, 0.1 to 0.4% by weight niobium, balance copper.

Claim 22

A wrought alloy as in claim 12 wherein a small but effective amount of an element selected from the group consisting of arsenic, magnesium, cobalt, boron, calcium, cadmium and mischmetal is added to said alloy.

Claim 23

A process as in claim 3 wherein said alloy consists essentially of 0.5 to 1.0% by weight chromium, 0.1to 0.4% by weight zirconium, 0.1 to 0.4% by weight niobium, balance copper.

Claim 24

A process as in claim 3 wherein a small but effective amount of an element selected from the group consisting of arsenic, magnesium, cobalt, boron, calcium, cadmium and mischmetal is added to said alloy of step (a).