Assignee: Sumitomo Chemical Co Ltd
•
Filing: 1974-07-23
•
Granted: 1977-09-06
•
Expires: 1994-07-23
Abstract
Abstract A thermosettable acrylic resin composition for powder coating comprising a mixture consisting essentially of (A) 100 parts by weight of an acrylic resin having a glass transition temperature of 10 DEG to 75 DEG C. and containing (a) 2 to 28 % by weight of a monomeric component containing epoxy group and (b) 0.1 to 8 % by weight of a monomeric component containing carboxyl or acid anhydride group, the gram equivalent ratio of said carboxyl groups to said epoxy groups contained in said acrylic resin being in the range from 1/2 to 1/20 (provided that the gram equivalent of an acid anhydride group is assumed to be equivalent to 2 gram equivalents of the carboxyl group) and (B) 0.5 to 25 parts by weight of a curing agent capable of crosslinking said acrylic resin (A). On being baked at 150 DEG to 220 DEG C. for 10 to 50 minutes, this composition gives a coating film excellent in strength, adherence, and surface leveling.
Inventors
- 👤 Iko Itoh
- 👤 Yasuhiko Inoue
- 👤 Shojiro Ito
- 👤 Kazumitsu Kawamura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 02:30
CPC Classifications
C; C08; C08G; C08G59/00; C08G59/18; C08G59/20; C08G59/32; C08G59/3209; C08K; C08K5/00; C08K5/04; C08K5/09; C08K5/16; C08K5/22; C08K5/24; C08K5/25
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
319 words
A powdered thermosettable acrylic resin composition for powder coating comprising a mixture consisting essentially of A. 100 parts by weight of an acrylic resin having a glass transition temperature of 10° to 75° C. and a weight average molecular weight of from 8,000 to 100,000, made by copolymerizing at least one nonfunctional monomer selected from the group consisting of methyl acrylate, ethyl acrylate, n-propyl acrylate, isopropyl acrylate, n-butyl acrylate, isobutyl acrylate, tert-butyl acrylate, hexyl acrylate, cyclohexyl acrylate, 2-ethylhexyl acrylate, octyl acrylate, 2-ethyloctyl acrylate, dodecyl acrylate, benzyl acrylate, phenyl acrylate, methyl methacrylate, ethyl methacrylate, n-propyl methacrylate, isopropyl methacrylate, n-butyl methacrylate, isobutyl methacrylate, tert-butyl methacrylate, hexyl methacrylate, cyclohexyl methacrylate, 2-ethylhexyl methacrylate, octyl methacrylate, 2-ethyloctyl methacrylate, dodecyl methacrylate, benzyl methacrylate, and phenyl methacrylate in an amount of about 20 to 97% by weight based on said acrylic resin with (a) at least one monomer containing an epoxy group selected from the group consisting of glycidyl acrylate, glycidyl methacrylate, β-methylglycidyl acrylate, β-methylglycidyl methacrylte, n-glycidylacrylamide, allyl glycidyl ether, and glycidyl vinylsulfonate in an amount of 2 to 28% by weight based on said acrylic resin and (b) at least one monomer containing a carboxyl group or an acid anhydride group selected from the group consisting of acrylic acid, methacrylic acid, crotonic acid, itaconic acid, fumaric acid, maleic acid, citraconic acid, monoalkyl itaconates, monoalkyl fumarates, monoalkyl maleates, monoalkyl citraconates, itaconic anhydride, maleic anhydride, and citraconic anhydride in an amount of 0.1 to 8% by weight based on said acrylic resin, wherein the gram equivalent ratio of said carboxyl groups to said epoxy groups in said acrylic resin is in the range from 1/2 to 1/20 (provided that the gram equivalent of an acid anhydride group is assumed to be equivalent to 2 gram equivalents of the carboxyl group) and B. 0.5 to 25 parts by weight of a curing agent selected from the group consisting of polycarboxylic acids, anhydrides or polycarboxylic acids, and polycarboxylic hydrazides.
Claim 2
Dependent Claim
319 words
A powdered thermosettable acrylic resin composition for powder coating comprising a mixture consisting essentially of A. 100 parts by weight of an acrylic resin having a glass transition temperature of 10° to 75° C. and a weight average molecular weight of from 8,000 to 100,000, made by copolymerizing at least one nonfunctional monomer selected from the group consisting of methyl acrylate, ethyl acrylate, n-propyl acrylate, isopropyl acrylate, n-butyl acrylate, isobutyl acrylate, tert-butyl acrylate, hexyl acrylate, cyclohexyl acrylate, 2-ethylhexyl acrylate, octyl acrylate, 2-ethyloctyl acrylate, dodecyl acrylate, benzyl acrylate, phenyl acrylate, methyl methacrylate, ethyl methacrylate, n-propyl methacrylate, isopropyl methacrylate, n-butyl methacrylate, isobutyl methacrylate, tert-butyl methacrylate, hexyl methacrylate, cyclohexyl methacrylate, 2-ethylhexyl methacrylate, octyl methacrylate, 2-ethyloctyl methacrylate, dodecyl methacrylate, benzyl methacrylate, and phenyl methacrylate in an amount of about 20 to 97% by weight based on said acrylic resin with (a) at least one monomer containing an epoxy group selected from the group consisting of glycidyl acrylate, glycidyl methacrylate, β-methylglycidyl acrylate, β-methylglycidyl methacrylte, n-glycidylacrylamide, allyl glycidyl ether, and glycidyl vinylsulfonate in an amount of 2 to 28% by weight based on said acrylic resin and (b) at least one monomer containing a carboxyl group or an acid anhydride group selected from the group consisting of acrylic acid, methacrylic acid, crotonic acid, itaconic acid, fumaric acid, maleic acid, citraconic acid, monoalkyl itaconates, monoalkyl fumarates, monoalkyl maleates, monoalkyl citraconates, itaconic anhydride, maleic anhydride, and citraconic anhydride in an amount of 0.1 to 8% by weight based on said acrylic resin, wherein the gram equivalent ratio of said carboxyl groups to said epoxy groups in said acrylic resin is in the range from 1/2 to 1/20 (provided that the gram equivalent of an acid anhydride group is assumed to be equivalent to 2 gram equivalents of the carboxyl group) and B. 0.5 to 25 parts by weight of a curing agent selected from the group consisting of polycarboxylic acids, anhydrides or polycarboxylic acids, and polycarboxylic hydrazides.
Claim 3
Dependent Claim
89 words
A composition according to claim 1, wherein nonfunctional monomer, which is copolymerized with (a) the functional monomer containing an epoxy group and (b) that containing a carboxyl or acid anhydride group to form the acrylic resin, comprises a mixture of said nonfunctional monomer and 0-65% by weight based on the acrylic resin of another ethelenically unsaturated monomer is (c) at least one member selected from the group consisting of esters of acrylic acid and esters of methacrylic acid or (d) a mixture of (c) and an ethylenically unsaturated monomer.
Claim 4
Dependent Claim
16 words
A composition according to claim 2, wherein said nonfunctional monomer is an ester of acrylic acid.
Claim 5
Dependent Claim
16 words
A composition according to claim 2, wherein said nonfunctional monomer is the ester of methacrylic acid.
Claim 6
Dependent Claim
39 words
A composition according to claim 2, wherein the other ethylenically unsaturated monomer is at least one member selected from the group consisting of styrene, vinyltoluene, acrylonitrile, methacrylonitrile, vinyl acetate, ethylene, propylene, vinyl fluoride, vinyl chloride, and lauryl vinyl ether.
Claim 7
Dependent Claim
17 words
A composition according to claim 1, wherein melt index of the acrylic resin is 1 to 100.
Claim 8
Dependent Claim
40 words
A composition according to claim 1, wherein in order to control melt index of the acrylic resin, said resin is prepared by polymerization in the presence of a chain transfer agent or an organic solvent having a sufficient chain-transfer effect.
Claim 9
Dependent Claim
23 words
A composition according to claim 7, wherein the chain transfer agent is dodecyl mercaptan, dibenzoyl disulfide, 2-ethylhexyl thioglycolate, carbon tetrabromide, or carbon tetrachloride.
Claim 10
Dependent Claim
16 words
A composition according to claim 7, wherein the organic solvent is isopropyl alcohol, isopropylbenzene, or toluene.
Claim 11
Dependent Claim
22 words
A composition according to claim 1, wherein the polycarboxylic acid or anhydride thereof has a melting point of 65° to 190° C.
Claim 12
Dependent Claim
64 words
A composition according to claim 10, wherein the polycarboxylic acid or anhydride thereof is succinic acid, glutaric acid, adipic acid, pimelic acid, suberic acid, azelaic acid, sebacic acid, citric acid, maleic acid, citraconic acid, itaconic acid, glutaconic acid, hexahydrophthalic acid, cyclohexene-1,2-dicarboxylic acid, 1,10-decanedicarboxylic acid, succinic anhydride, sebacic anhydride, itaconic anhydride, phthalic anhydride, trimellitic anhydride, or an acrylic resin containing carboxyl or acid anhydride groups.
Claim 13
Dependent Claim
42 words
A composition according to claim 1, which contains 0.1 to 10 parts by weight of an antiblocking agent based on the acrylic resin composition and/or 0.1 to 5 parts by weight of a surface leveling agent based on the acrylic resin composition.
Claim 14
Dependent Claim
13 words
A composition according to claim 1, which contains a plasticizer and/or a pigment.
Claim 15
Dependent Claim
25 words
A composition according to claim 13, wherein the plasticizer is an adipate, phosphate, phthalate, sebacate, or a polyester derived from adipic acid or azelaic acid.
Claim 16
Dependent Claim
37 words
A composition according to claim 12, wherein the surface leveling agent is homo- or co-oligmer of acrylic ester and styrene, metal salt of perfluorocarboxylic acid or perfluorosulfonic acid, and esters of perfluorocarboxylic acid with polyethyleneglycol or polypropyleneglycol.
Claim 17
Dependent Claim
29 words
A composition according to claim 1, wherein the mixture is melt blended in molten state at 80° to 130° C., cooled, and ground to pass through a 100-mesh screen.
Claim 18
Dependent Claim
27 words
A composition according to claim 1, wherein each ingredient of the mixture is previously ground to a powder of 100 to 150 mesh and then mixed together.
Claim 19
Dependent Claim
50 words
A composition according to claim 12, wherein the antiblocking agent is acetamide, propionamide, stearamide, arachamide, montanamide, cerotamide, diacetamide, bisoleamide, bislauramide, methylenebisstearamide, ethylenebisstearamide, myricyl cerotate, butylene glycol dimontanate, glyceryl tri-1,2-hydroxy stearate, polyethylene or atactic polypropylene having a molecular weight of 1,000 to 10,000, or a partial oxidation product of these polyolefins.
References Cited (Backward Citations)
CA499491A
Cited
US3242123A
Cited
US3563953A
Cited
US3843612A
Cited
US3845010A
Cited
US3847863A
Cited
US3803111A
Cited
US3784501A
Cited
US3857905A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-09-05 | 1981-03-07 | 1981-09-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-09-05 | 1985-03-07 | 1985-09-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-09-05 | 1989-03-07 | 1989-09-06 | $7700.00 | Window Closed / Lapsed |