Method for the manufacture of a superconductor with a superconductive intermetallic compound of at least two elements
Assignee: Siemens AG
•
Filing: 1975-04-30
•
Granted: 1977-08-30
•
Expires: 1995-04-30
Abstract
Abstract A method for the manufacture of a superconductor with a superconductive intermetallic compound consisting of at least two chemical elements in which a ductile structural part made of at least one element of the compound is brought into contact with a second structural part which contains a ductile carrier metal for the remaining elements of the compound after which the remaining elements of the compound are admitted to the second ductile structural part through a chemical transport reaction at elevated temperature, the compound being formed by a reaction of its remaining elements, diffusing through the second structural part, with the first structural part.
Inventors
- 👤 Gunther Ziegler
- 👤 Sigrun Frohmader
- 👤 Manfred Wilhelm
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 06:43
CPC Classifications
H; H10; H10N; H10N60/00; H10N60/01; H10N60/0184; Y; Y10; Y10S; Y10S505/00; Y10S505/825; Y10S505/917; Y10S505/918; Y10S505/919; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49014
Claims Analysis
Total Claims: 30
Claim 1
Independent Claim
173 words
A method for the manufacture of a superconductor with a superconductive intermetallic compound consisting of at least two chemical elements by steps comprising bringing a ductile structural part made of at least one element of the compound into contact with a second structural part which contains a ductile carrier metal for the remaining elements of the compound; subsequently supplying the remaining elements of the compound to the second structural part at elevated temperature; and diffusing the remaining elements through the second structural part and reacting said remaining elements with said first structural part to form the compound, wherein the improvement comprises performing said step of supplying so as to supply the remaining elements to the second structural part solely by a chemical transport reaction of the type in which said remaining elements are initially converted by a gaseous transport agent in a reversible reaction to form gaseous reaction products and the gaseous reaction products subsequently decomposed in a reversal of the reaction to thereby supply the remaining elements to the second structural part.
Claim 2
Independent Claim
173 words
A method for the manufacture of a superconductor with a superconductive intermetallic compound consisting of at least two chemical elements by steps comprising bringing a ductile structural part made of at least one element of the compound into contact with a second structural part which contains a ductile carrier metal for the remaining elements of the compound; subsequently supplying the remaining elements of the compound to the second structural part at elevated temperature; and diffusing the remaining elements through the second structural part and reacting said remaining elements with said first structural part to form the compound, wherein the improvement comprises performing said step of supplying so as to supply the remaining elements to the second structural part solely by a chemical transport reaction of the type in which said remaining elements are initially converted by a gaseous transport agent in a reversible reaction to form gaseous reaction products and the gaseous reaction products subsequently decomposed in a reversal of the reaction to thereby supply the remaining elements to the second structural part.
Claim 3
Dependent Claim
52 words
The method according to claim 1 wherein several cores of said first structural part are embedded in a matrix material of said second stuctural part and the resulting structure reduced in cross-section in a number of steps and wherein the chemical transport reaction is carried out after the last cross-section reducing step.
Claim 4
Dependent Claim
57 words
The method according to claim 1 wherein the superconductive compound to be produced is a compound of the type A 3 B with an A-15 crystal structure, consisting of two elements, and the first structural part consists of the higher melting point element of the compound, with the lower melting point element supplied through the transport reaction.
Claim 5
Dependent Claim
21 words
The method according to claim 1 wherein the second structural part consists only of the carrier metal for the remaining elements.
Claim 6
Dependent Claim
25 words
The method according to claim 1 wherein the second structural part also contains a share of the remaining elements of the compound to be produced.
Claim 7
Dependent Claim
12 words
The method according to claim 1 wherein said carrier metal is copper.
Claim 8
Dependent Claim
17 words
The method according to claim 1 wherein the transport reaction is carried out in a closed system.
Claim 9
Dependent Claim
17 words
The method according to claim 1 wherein the transport reaction is carried out in an open system.
Claim 10
Dependent Claim
38 words
The method according to claim 1 wherein the source for the element to be transported in the transport reaction and the conductor structure containing the second ductile component part are kept at least approximately at the same temperature.
Claim 11
Dependent Claim
14 words
The method according to claim 1 wherein the compound Nb 3 Sn is formed.
Claim 12
Dependent Claim
29 words
The method according to claim 10, wherein the first structural part consists of niobium and the second structural part of copper with 0 to 8.5 atom percent of tin.
Claim 13
Dependent Claim
16 words
The method according to claim 11 where 0 to 4 atom percent of tin is used.
Claim 14
Dependent Claim
17 words
The method according to claim 10 wherein chlorine is used as the transport agent for the tin.
Claim 15
Dependent Claim
21 words
The method according to claim 13 wherein said chlorine is introduced into the reaction chamber in the form of hydrogen chloride.
Claim 16
Dependent Claim
22 words
The method according to claim 10 wherein the transport reaction is carried out at a temperature of between 700° and 800° C.
Claim 17
Dependent Claim
14 words
The method according to claim 1 wherein the compound V 3 Ga is formed.
Claim 18
Dependent Claim
29 words
The method according to claim 16 wherein the first structural part consists of vanadium and the second structural part of copper with 0 to 23 atom percent of gallium.
Claim 19
Dependent Claim
19 words
The method according to claim 17 wherein said second component part contains 0 to 15 atom percent of gallium.
Claim 20
Dependent Claim
17 words
The method according to claim 16 wherein iodine is used as the transport agent for the gallium.
Claim 21
Dependent Claim
21 words
The method according to claim 19 wherein the iodine is introduced into the reaction chamber in the form of copper iodide.
Claim 22
Dependent Claim
21 words
The method according to claim 16 wherein the transport reaction is performed at a temperature of between 450° and 700° C.
Claim 23
Dependent Claim
51 words
The method according to claim 7 wherein the source for the element to be transported is distributed over the reaction chamber as uniformly as possible in such a manner that the transport paths to the different parts of the conductor structure containing the second structural part are of about equal length.
Claim 24
Dependent Claim
51 words
The method according to claim 9 wherein the source for the element to be transported is distributed over the reaction chamber as uniformly as possible in such a manner that the transport paths to the different parts of the conductor structure containing the second structural part are of about equal length.
Claim 25
Dependent Claim
25 words
The method according to claim 23 wherein the source for the element to be transported encloses the conductor structure in the form of a tube.
Claim 26
Dependent Claim
47 words
The method according to claim 1 wherein the transport reaction is controlled so that the second element is transported to the surface of the second structural part only in such an amount as can diffuse into the second structural part, forming or maintaining a homogeneous single-phase alloy.
Claim 27
Dependent Claim
32 words
The method according to claim 1 and further including an additional heat treatment in an inert atmosphere, to reinforce the layers of the intermetallic compound formed after the transport reaction is completed.
Claim 28
Dependent Claim
67 words
The method according to claim 1 wherein the second structural part is enriched with the second element of the compound at a temperature below the formation temperature of the compound in a first phase of the transport reaction and the compound is formed at a temperature above the formation temperature of the compound, while continuing to supply the second element of the compound in a second phase.
Claim 29
Independent Claim
245 words
A method for the manufacture of a superconducting with a superconductive intermetallic compound consisting of at least two chemical elements by steps comprising bringing a ductile structural part made of at least one element of the compound into contact with a second structural part which contains a ductile carrier metal for the remaining elements of the compound; subsequently supplying the remaining elements of the compound to the second structural part at elevated temperature; and diffusing the remaining elements through the second structural part and reacting said remaining elements with said first structural part to form the compound, wherein the improvement comprises: a. disposing said first and second structural parts, after being brought together, in a reaction chamber; b. also disposing within said reaction chamber the remaining elements; c. providing a supply of chemical transport agent for said remaining elements in said reaction chamber; d. heatimg said reaction chamber to cause said chemical transport agent to carry out a chemical transport reaction solely of the type in which said remaining elements react in a reversible reaction with the gaseous transport agent to form gaseous products which are subsequently decomposed in a reversal of the reaction at said second structural part, whereby said remaining elements are supplied to said second structural part by means of a chemical transport reaction; and e. maintaining said transport reaction for a predetermined period of time so as to supply a desired amount of said remaining elements to said second structural part.
Claim 30
Independent Claim
245 words
A method for the manufacture of a superconducting with a superconductive intermetallic compound consisting of at least two chemical elements by steps comprising bringing a ductile structural part made of at least one element of the compound into contact with a second structural part which contains a ductile carrier metal for the remaining elements of the compound; subsequently supplying the remaining elements of the compound to the second structural part at elevated temperature; and diffusing the remaining elements through the second structural part and reacting said remaining elements with said first structural part to form the compound, wherein the improvement comprises: a. disposing said first and second structural parts, after being brought together, in a reaction chamber; b. also disposing within said reaction chamber the remaining elements; c. providing a supply of chemical transport agent for said remaining elements in said reaction chamber; d. heatimg said reaction chamber to cause said chemical transport agent to carry out a chemical transport reaction solely of the type in which said remaining elements react in a reversible reaction with the gaseous transport agent to form gaseous products which are subsequently decomposed in a reversal of the reaction at said second structural part, whereby said remaining elements are supplied to said second structural part by means of a chemical transport reaction; and e. maintaining said transport reaction for a predetermined period of time so as to supply a desired amount of said remaining elements to said second structural part.
References Cited (Backward Citations)
US3268362A
Cited
US3342707A
Cited
US3425825A
Cited
US3281738A
Cited
US3397084A
Cited
US3449092A
Cited
US3525637A
Cited
US3578496A
Cited
US3595693A
Cited
US3728165A
Cited
US3829963A
Cited
US3838503A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-08-29 | 1981-02-28 | 1981-08-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-08-29 | 1985-02-28 | 1985-08-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-08-29 | 1989-02-28 | 1989-08-30 | $7700.00 | Window Closed / Lapsed |