Decorative sheet for solid color laminates
Assignee: Westinghouse Electric Corp
•
Filing: 1975-01-20
•
Granted: 1977-08-23
•
Expires: 1995-01-20
Abstract
Abstract A colored decorative plastic laminate is made from a core layer and a superimposed decorative layer comprising: a fibrous material, coloring particles having a Moh's hardness of up to about 6 and an average particle size range of between about 53 to 210 microns, and thermoset resin; where the weight ratio of fiber material:coloring particles is from about 1:0.04 to 1:0.4 and the colored decorative layer is characterized in that the pigments are dispersed only through the bottom two-thirds of the colored layer and concentrated in the colored layer near the core-decorative layer interface, the top one-third of the colored layer containing substantially no pigment particles.
Inventors
- 👤 Harold O. McCaskey, Jr.
- 👤 Salvatore E. Palazzolo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 20:59
CPC Classifications
B; B32; B32B; B32B5/00; B32B5/22; B32B5/24; B32B5/26; B32B29/00; B32B29/04; B32B5/30; B44; B44C; B44C3/00; B44C3/02; B44C5/00; B44C5/04; B44C5/0469; D; D21; D21H; D21H27/00; D21H27/18; D21H27/22; D21H27/26; D21H27/28; B32B2250/00; B32B2250/20; B32B2260/00; B32B2260/02; B32B2260/021; B32B2260/023; B32B2260/04; B32B2260/046; B32B2307/00; B32B2307/40; B32B2307/402; B32B2307/4026; B32B2451/00; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24355; Y10T428/24446; Y10T428/24455; Y10T428/25; Y10T428/252; Y10T428/256; Y10T428/258; Y10T428/31504; Y10T428/31942; Y10T428/31949; Y10T428/31964; Y10T428/31967
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
140 words
A machinable, colored, postformable decorative plastic laminate comprising a core layer of a plurality of resin impregnated fibrous sheets, and superimposed thereon a resin impregnated, colored decorative layer consisting of fibrous material selected from the group consisting of rayon, cellulose wood pulp and mixtures thereof, coloring particles having a Moh's hardness of up to about 6 and an average particle size range between about 53 to 210 microns and resin; wherein the weight ratio of fibrous material:coloring particles is from about 1:0.04 to 1:0.4; the colored decorative layer characterized in that the coloring particles are dispersed only through the bottom two-thirds of the colored layer and concentrated in the colored layer near the core-decorative layer interface, the top one-third of the colored layer containing substantially no coloring particles, the colored laminate characterized by having no separate clear protecting overlaying layer.
Claim 2
Dependent Claim
140 words
A machinable, colored, postformable decorative plastic laminate comprising a core layer of a plurality of resin impregnated fibrous sheets, and superimposed thereon a resin impregnated, colored decorative layer consisting of fibrous material selected from the group consisting of rayon, cellulose wood pulp and mixtures thereof, coloring particles having a Moh's hardness of up to about 6 and an average particle size range between about 53 to 210 microns and resin; wherein the weight ratio of fibrous material:coloring particles is from about 1:0.04 to 1:0.4; the colored decorative layer characterized in that the coloring particles are dispersed only through the bottom two-thirds of the colored layer and concentrated in the colored layer near the core-decorative layer interface, the top one-third of the colored layer containing substantially no coloring particles, the colored laminate characterized by having no separate clear protecting overlaying layer.
Claim 3
Dependent Claim
30 words
The laminate of claim 1, wherein the resin used in the core layer is a phenolic resin, and the resin used in the colored decorative layer is a melamine resin.
Claim 4
Dependent Claim
144 words
A machinable, colored, postformable decorative plastic laminate consisting of a core layer of a plurality of resin impregnated fibrous sheets, and superimposed thereon a thermoset resin impregnated, colored decorative layer consisting of fibrous material selected from the group consisting of rayon, cellulose wood pulp and mixtures thereof, coloring particles having a Moh's hardness of up to about 6 and an average particle size range between about 53 to 210 microns and thermoset resin; wherein the weight ratio of fibrous material: coloring particles is from about 1:0.04 to 1:0.4; the colored decorative layer characterized in that the coloring particles are dispersed only through the bottom two-thirds of the colored layer and cncentrated in the colored layer near the core-decorative layer interface, the top one-third of the colored layer containing substantially no coloring particles, the colored laminate characterized by having no separate clear protecting overlaying layer.
Claim 5
Dependent Claim
144 words
A machinable, colored, postformable decorative plastic laminate consisting of a core layer of a plurality of resin impregnated fibrous sheets, and superimposed thereon a thermoset resin impregnated, colored decorative layer consisting of fibrous material selected from the group consisting of rayon, cellulose wood pulp and mixtures thereof, coloring particles having a Moh's hardness of up to about 6 and an average particle size range between about 53 to 210 microns and thermoset resin; wherein the weight ratio of fibrous material: coloring particles is from about 1:0.04 to 1:0.4; the colored decorative layer characterized in that the coloring particles are dispersed only through the bottom two-thirds of the colored layer and cncentrated in the colored layer near the core-decorative layer interface, the top one-third of the colored layer containing substantially no coloring particles, the colored laminate characterized by having no separate clear protecting overlaying layer.
Claim 6
Dependent Claim
30 words
The laminate of claim 3, wherein the resin used in the core layer is a phenolic resin, and the resin used in the colored decorative layer is a melamine resin.
Claim 7
Dependent Claim
43 words
The laminate of claim 4 having a thickness of between about 3/64 to 1/16 inch, the core sheets consisting of two paper layers, the core layer next to the colored layer being uncreped paper and the other core layer being stretchable creped paper.
Claim 8
Dependent Claim
58 words
The laminate of claim 4 wherein both the phenolic resin and the melamine resin contain effective amounts of plasticizer, the resin ratio in the core sheets is between about 1.25 to 2.00, the resin ratio in the colored layer is between about 1.35 to 2.35 and the fibers in the colored layer are finely divided alpha cellulose fibers.
Claim 9
Dependent Claim
19 words
The laminate of claim 4 wherein the colored layer has a thickness of between about 5 to 25 mils.
Claim 10
Dependent Claim
95 words
A machinable, colored, post-formable sheet consisting of alpha cellulose fibrous material, coloring particles having a Moh's hardness of up to about 6 and an average particle size range of between about 53 to 210 microns, and thermoset melamine resin; wherein the weight ratio of fibrous material:coloring particles is from about 1:0.04 to 1:0.4; the colored sheet characterized in that the coloring particles are dispersed only through the bottom two-thirds of the sheet, the top one-third of the colored sheet containing substantially no coloring particles, the sheet characterized by having no separate, clear protecting overlaying layer.
Claim 11
Dependent Claim
95 words
A machinable, colored, post-formable sheet consisting of alpha cellulose fibrous material, coloring particles having a Moh's hardness of up to about 6 and an average particle size range of between about 53 to 210 microns, and thermoset melamine resin; wherein the weight ratio of fibrous material:coloring particles is from about 1:0.04 to 1:0.4; the colored sheet characterized in that the coloring particles are dispersed only through the bottom two-thirds of the sheet, the top one-third of the colored sheet containing substantially no coloring particles, the sheet characterized by having no separate, clear protecting overlaying layer.
Claim 12
Dependent Claim
25 words
The sheet of claim 8 having a thickness of between about 5 to 25 mils and a resin ratio of between about 1.35 to 2.35.
Claim 13
Dependent Claim
15 words
The sheet of claim 9, wherein the melamine resin contains an effective amount of plasticizer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-08-22 | 1981-02-21 | 1981-08-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-08-22 | 1985-02-21 | 1985-08-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-08-22 | 1989-02-21 | 1989-08-23 | $7700.00 | Window Closed / Lapsed |