Electrical resistance compositions
Assignee: ERA Patents Ltd
•
Filing: 1974-10-31
•
Granted: 1977-08-23
•
Expires: 1994-10-31
Abstract
Abstract Process for forming a vitreous enamel electrical resistor coating on a substrate, said vitreous enamel containing an electrically conductive species as a crystalline phase and having a temperature coefficient of resistance, as measured in the temperature range of 20° to 120° C, of from -500 to +500 ppm/° C, comprises applying to said substrate a paste comprising (1) an organic medium, (2) a powdered aluminoborate glass containing dissolved molybdenum trioxide, tungsten trioxide, cerium dioxide, manganese dioxide or ferric oxide in an amount of 2 to 30 mol percent of the total constituent oxides of the glass and (3) powdered boron, silicon, molybdenum disilicide or tungsten disilicide in an amount of 0.25 to 30 percent by weight based on the total weight of components (2) and (3) and firing the paste on the substrate at a temperature of about 600° to 900° C to form a vitreous enamel. The coated substrates are particularly useful in thick film printed and fired circuits.
Inventors
- 👤 Alexander S. Laurie
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 01:45
CPC Classifications
H; H01; H01B; H01B1/00; H01B1/14; H01C; H01C17/00; H01C17/06; H01C17/065; H01C17/06506; H01C17/06513; H01C17/06533
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
193 words
A process for forming a vitreous enamel electrical resistor coating on a substrate, said vitreous enamel containing an electrically conductive species as a crystalline phase and having a temperature coefficient of resistance, as measured in the temperature range of 20° to 120° C., of from -500 to +500 ppm/° C., comprising applying to a substrate a composition which comprises (1) a liquid organic medium, (2) a powdered aluminoborate glass, containing as a dissolved component, a metal oxide selected from the group consisting of molybdenum trioxide, tungsten troixide, cerium dioxide, manganese dioxide and ferric oxide in an amount of 2 to 30 mol percent based on the total amount of glass expressed as its component oxides and (3) a powdered reducing agent capable of withstanding glass firing temperature selected from the group consisting of boron, and silicon, in an amount of 0.25 to 30 percent by weight based on the total weight of glass and reducing agent, the relative proportions of (1), (2) and (3) being such that said compositions is a paste, and firing said paste on said substrate at a temperature of about 600° to 900° C. to form a vitreous enamel.
Claim 2
Dependent Claim
193 words
A process for forming a vitreous enamel electrical resistor coating on a substrate, said vitreous enamel containing an electrically conductive species as a crystalline phase and having a temperature coefficient of resistance, as measured in the temperature range of 20° to 120° C., of from -500 to +500 ppm/° C., comprising applying to a substrate a composition which comprises (1) a liquid organic medium, (2) a powdered aluminoborate glass, containing as a dissolved component, a metal oxide selected from the group consisting of molybdenum trioxide, tungsten troixide, cerium dioxide, manganese dioxide and ferric oxide in an amount of 2 to 30 mol percent based on the total amount of glass expressed as its component oxides and (3) a powdered reducing agent capable of withstanding glass firing temperature selected from the group consisting of boron, and silicon, in an amount of 0.25 to 30 percent by weight based on the total weight of glass and reducing agent, the relative proportions of (1), (2) and (3) being such that said compositions is a paste, and firing said paste on said substrate at a temperature of about 600° to 900° C. to form a vitreous enamel.
Claim 3
Dependent Claim
20 words
A process according to claim 1 in which the aluminoborate glass is a cadmium aluminoborate glass containing dissolved molybdenum trioxide.
Claim 4
Dependent Claim
13 words
A process according to claim 2 in which the reducing agent is boron.
Claim 5
Dependent Claim
13 words
A process according to claim 2 in which the reducing agent is silicon.
Claim 6
Dependent Claim
27 words
A process according to claim 1 in which the aluminoborate glass is a lead, cadmium aluminoborate glass containing dissolved molybdenum trioxide and the reducing agent is boron.
Claim 7
Dependent Claim
26 words
A process according to claim 1 in which the aluminoborate glass is a cadmium aluminoborate glass containing dissolved tungsten trioxide and the reducing agent is boron.
Claim 8
Dependent Claim
27 words
A process according to claim 1 in which the aluminoborate glass is a sodium, zinc aluminoborate glass containing dissolved tungsten trioxide and the reducing agent is boron.
Claim 9
Dependent Claim
21 words
A process according to claim 1 wherein the reducing agent is employed in an amount of less than 10% by weight.
References Cited (Backward Citations)
US2969582A
Cited
US2891914A
Cited
US3226342A
Cited
US3392312A
Cited
US3379942A
Cited
US3622523A
Cited
US3652302A
Cited
US3682840A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-08-22 | 1981-02-21 | 1981-08-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-08-22 | 1985-02-21 | 1985-08-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-08-22 | 1989-02-21 | 1989-08-23 | $7700.00 | Window Closed / Lapsed |