Hardening process for crankshafts
Assignee: Rolls Royce Solutions GmbH
•
Filing: 1975-11-24
•
Granted: 1977-08-23
•
Expires: 1995-11-24
Abstract
Abstract A hardening process for a crankshaft which includes subjecting the crankshaft to a first induction hardening process to produce a hardened layer of a substantial thickness at all bearing locations and at all transitional points between the crank pins, journal pins and crank webs. Subsequently tempering the hardened zones of the crankshaft at the transitional points to a hardness value permitting a subsequent alignment of the crankshaft. Subjecting the crankshaft to a further induction hardening process to provide a second hardened layer only at the bearing locations which second layer has a depth which is less than the depth of the first hardened layer. The thus processed crankshaft is then subject to an expansion process to eliminate internal stresses therein.
Inventors
- 👤 Karl Just
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 18:03
CPC Classifications
C; C21; C21D; C21D1/00; C21D1/06; C21D1/09; C21D1/10; C21D9/00; C21D9/30; Y; Y02; Y02P; Y02P10/00; Y02P10/25; Y10; Y10S; Y10S148/00; Y10S148/902; Y10S148/904
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
130 words
A process for hardening a crankshaft which includes bearing locations defined by crank pins, journal pins and crank webs with the respective transitional areas between the crank pins, journal pins and crank webs being rounded areas, the process comprising: hardening all bearing locations and rounded areas of the crankshaft to provide a hardening layer of a predetermined depth at the bearing locations and rounded areas; tempering the hardening layer at the bearing locations and rounded zones to a predetermined hardness value which permits subsequent alignment of the crankshaft at the rounded areas; hardening only the bearing locations without affecting the rounded areas so as to provide a further hardening layer having a predetermined depth on the first mentioned hardening layer; and tempering the entire crankshaft to eliminate internal stresses therein.
Claim 2
Dependent Claim
130 words
A process for hardening a crankshaft which includes bearing locations defined by crank pins, journal pins and crank webs with the respective transitional areas between the crank pins, journal pins and crank webs being rounded areas, the process comprising: hardening all bearing locations and rounded areas of the crankshaft to provide a hardening layer of a predetermined depth at the bearing locations and rounded areas; tempering the hardening layer at the bearing locations and rounded zones to a predetermined hardness value which permits subsequent alignment of the crankshaft at the rounded areas; hardening only the bearing locations without affecting the rounded areas so as to provide a further hardening layer having a predetermined depth on the first mentioned hardening layer; and tempering the entire crankshaft to eliminate internal stresses therein.
Claim 3
Dependent Claim
32 words
A process according to claim 1, wherein the step of hardening all the bearing locations and rounded areas and the step of hardening only the bearing locations are effected by induction hardening.
Claim 4
Dependent Claim
36 words
A process according to claim 2, wherein the step of hardening only the bearing location includes providing a further hardened layer of a depth which is less than the depth of the first mentioned hardened layer.
Claim 5
Dependent Claim
49 words
A process according to claim 1, wherein the step of hardening all the bearing locations and rounded areas includes hardening said locations and said areas to a Rockwell hardness value of at least 60 with said predetermined depth of the hardening layer being in the range of 6-9 mm.
Claim 6
Dependent Claim
37 words
A process according to claim 4, wherein the step of tempering the hardening layer at the bearing locations and rounded areas includes tempering said locations and said areas to a Rockwell hardness value of at least 42.
Claim 7
Dependent Claim
29 words
A process according to claim 5, wherein the step of hardening only the bearing locations includes providing a further hardened layer having a depth of at least 3 mm.
Claim 8
Dependent Claim
29 words
A process according to claim 6, wherein the step of hardening only the bearing locations includes hardening only said locations to a Rockwell hardness value of at least 60.
Claim 9
Dependent Claim
30 words
A process according to claim 7, wherein the step of tempering the entire crankshaft includes tempering the further hardened layer to a Rockwell hardness value in the range of 50-53.
Claim 10
Dependent Claim
29 words
A process according to claim 1, wherein the step of hardening only the bearing locations includes providing a further hardened layer having a depth of at least 3 mm.
Claim 11
Dependent Claim
35 words
A process according to claim 9, wherein the step of hardening all the bearing locations and rounded areas of the crankshaft includes providing a hardening layer having a depth in the range of 6-9 mm.
References Cited (Backward Citations)
US2213241A
Cited
US3377214A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-08-22 | 1981-02-21 | 1981-08-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-08-22 | 1985-02-21 | 1985-08-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-08-22 | 1989-02-21 | 1989-08-23 | $7700.00 | Window Closed / Lapsed |